- 熔体流动速率 [g/10min]: 29.8
- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 1.9
- 拉伸强度 [MPa]: 46.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | |
| Water Absorption | 1.9 % | 1.9 % | |
| Melt Flow | 29.8 g/10 min @Load 2.16 kg, Temperature 235 °C | 29.8 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min |
| Tensile Modulus | 1.45 GPa | 210 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Dissipation Factor | 0.000328 @Frequency 1e+6 Hz | 0.000328 @Frequency 1e+6 Hz | |
| 0.00033 @Frequency 100 Hz | 0.00033 @Frequency 100 Hz | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 183 °C | 361 °F | 10°C/min |
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||
| Oxygen Index | 25 % | 25 % | |