- 熔体流动速率 [g/10min]: 95.1
- 吸水率 [%]: 1.96
- 拉伸强度 [MPa]: 51.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 1.96 % | 1.96 % | |
| Moisture Absorption at Equilibrium | 0.64 % | 0.64 % | Humidity Absorption |
| Melt Flow | 95.1 g/10 min @Load 2.16 kg, Temperature 235 °C | 95.1 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min |
| Tensile Modulus | 2.07 GPa | 300 ksi | 1 mm/min |
| Charpy Impact Unnotched | 0.850 J/cm² @Temperature -30.0 °C | 4.05 ft-lb/in² @Temperature -22.0 °F | |
| Charpy Impact, Notched | 0.420 J/cm² | 2.00 ft-lb/in² | |
| 0.420 J/cm² @Temperature -30.0 °C | 2.00 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Strength | 28.5 kV/mm | 724 kV/in | |
| Dissipation Factor | 0.000315 @Frequency 1e+6 Hz | 0.000315 @Frequency 1e+6 Hz | |
| 0.000328 @Frequency 100 Hz | 0.000328 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 102 µm/m-°C @Temperature 20.0 °C | 56.7 µin/in-°F @Temperature 68.0 °F | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | ||
| Oxygen Index | 33 % | 33 % | |