- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 1.8
- 拉伸强度 [MPa]: 32.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Water Absorption | 1.8 % | 1.8 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-1/-2 |
| Tensile Modulus | 0.500 GPa | 72.5 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 187 °C | 369 °F | ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | ISO75-1/-2 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 190 - 250 °C | 374 - 482 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | <= 0.10 % | <= 0.10 % | |