- 密度 [g/cm3]: 4.28
- 缺口冲击强度: 0.33
- 拉伸强度 [MPa]: 40.0
- 断裂伸长率 [%]: 61.0
- 弯曲模量 [MPa]: 4.77
- 热变形温度 [℃]: 167.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 4.30 g/cc | 4.30 g/cc | ASTM D792 |
| Density | 4.28 g/cc | 0.155 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec | 0.0070 - 0.0090 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec | 0.0070 - 0.0090 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D638 |
| 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D638 |
| 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.3 % | 1.3 % | Type I, 5 mm/min; ASTM D638 |
| 1.4 % | 1.4 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 1.3 % | 1.3 % | Type I, 5 mm/min; ASTM D638 |
| 1.4 % | 1.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.84 GPa | 702 ksi | 1 mm/min; ISO 527 |
| 5.77 GPa | 837 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 61.0 MPa | 8850 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| 62.0 MPa | 8990 psi | ISO 178 | |
| Flexural Yield Strength | 61.0 MPa | 8850 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.77 GPa | 692 ksi | 2 mm/min; ISO 178 |
| 4.88 GPa | 708 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.330 J/cm | 0.618 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.02 J/cm | 3.78 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C | 6.64 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.44 | 0.44 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.38 | 0.38 | ASTM D3702 Modified |
| K (wear) Factor | 96.7 x 10-8 mm³/N-M | 48.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 66.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 36.7 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 65.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 36.1 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 167 °C | 333 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 162 °C @Thickness 3.20 mm | 324 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 84.0 °C @Thickness 3.20 mm | 183 °F @Thickness 0.126 in | unannealed; ASTM D648 | |