- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 30.0
- 断裂伸长率 [%]: 30.0
- 弯曲强度 [MPa]: 44.0
- 弯曲模量 [MPa]: 0.800
- 硬度: 114.0
- 热变形温度 [℃]: 135.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 - 1.35 g/cc | 0.0368 - 0.0488 lb/in³ | Average value: 1.09 g/cc Grade Count:31 |
| Apparent Bulk Density | 0.265 - 0.450 g/cc | 0.00957 - 0.0163 lb/in³ | Average value: 0.363 g/cc Grade Count:3 |
| Water Absorption | 0.200 - 3.00 % | 0.200 - 3.00 % | Average value: 0.778 % Grade Count:12 |
| 14.75 - 14.75 % @Temperature 100 - 100 °C | 14.75 - 14.75 % @Temperature 212 - 212 °F | Average value: 14.8 % Grade Count:1 | |
| Moisture Absorption at Equilibrium | 0.500 - 3.00 % | 0.500 - 3.00 % | Average value: 1.38 % Grade Count:8 |
| Water Absorption at Saturation | 2.20 - 7.00 % | 2.20 - 7.00 % | Average value: 3.44 % Grade Count:14 |
| Particle Size | 7.00 - 23.0 µm | 7.00 - 23.0 µm | Average value: 16.7 µm Grade Count:3 |
| pH | 4.00 | 4.00 | Average value: 4.00 Grade Count:3 |
| Specific Surface Area | 1.50 - 20.0 m²/g | 1.50 - 20.0 m²/g | Average value: 9.17 m²/g Grade Count:3 |
| Linear Mold Shrinkage | 0.00900 - 0.0250 cm/cm | 0.00900 - 0.0250 in/in | Average value: 0.0134 cm/cm Grade Count:17 |
| Linear Mold Shrinkage, Transverse | 0.0100 - 0.0150 cm/cm | 0.0100 - 0.0150 in/in | Average value: 0.0122 cm/cm Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 114 - 115 | 114 - 115 | Average value: 114 Grade Count:6 |
| Hardness, Shore D | 75.0 - 82.0 | 75.0 - 82.0 | Average value: 78.3 Grade Count:4 |
| Tensile Strength, Ultimate | 44.0 - 130 MPa | 6380 - 18900 psi | Average value: 67.2 MPa Grade Count:14 |
| Tensile Strength, Yield | 30.0 - 79.3 MPa | 4350 - 11500 psi | Average value: 55.5 MPa Grade Count:17 |
| Elongation at Break | 2.10 - 370 % | 2.10 - 370 % | Average value: 63.8 % Grade Count:30 |
| Elongation at Yield | 2.10 - 20.0 % | 2.10 - 20.0 % | Average value: 11.0 % Grade Count:14 |
| Modulus of Elasticity | 1.05 - 9.98 GPa | 152 - 1450 ksi | Average value: 2.64 GPa Grade Count:24 |
| 0.300 - 0.800 GPa @Temperature 100 - 100 °C | 43.5 - 116 ksi @Temperature 212 - 212 °F | Average value: 0.500 GPa Grade Count:2 | |
| Flexural Yield Strength | 30.0 - 145 MPa | 4350 - 21000 psi | Average value: 85.5 MPa Grade Count:9 |
| Flexural Modulus | 0.800 - 9.26 GPa | 116 - 1340 ksi | Average value: 2.54 GPa Grade Count:16 |
| Izod Impact, Notched | 0.320 - 0.640 J/cm | 0.599 - 1.20 ft-lb/in | Average value: 0.458 J/cm Grade Count:12 |
| 0.500 - 0.500 J/cm @Temperature -40.0 - -40.0 °C | 0.937 - 0.937 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.500 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 2.14 - 5340 J/cm | 4.00 - 10000 ft-lb/in | Average value: 3.99 J/cm Grade Count:6 |
| Izod Impact, Notched (ISO) | 4.00 - 6.50 kJ/m² | 1.90 - 3.09 ft-lb/in² | Average value: 4.80 kJ/m² Grade Count:3 |
| 3.00 - 4.50 kJ/m² @Temperature -30.0 - -30.0 °C | 1.43 - 2.14 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 3.75 kJ/m² Grade Count:1 | |
| Charpy Impact Unnotched | 3.00 J/cm² - NB | 14.3 ft-lb/in² - NB | Average value: 5.50 J/cm² Grade Count:16 |
| 2.00 J/cm² - NB @Temperature -40.0 - -30.0 °C | 9.52 ft-lb/in² - NB @Temperature -40.0 - -22.0 °F | Average value: 2.83 J/cm² Grade Count:15 | |
| Charpy Impact, Notched | 0.350 - 12.0 J/cm² | 1.67 - 57.1 ft-lb/in² | Average value: 1.87 J/cm² Grade Count:17 |
| 0.300 - 1.90 J/cm² @Temperature -40.0 - -30.0 °C | 1.43 - 9.04 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 0.669 J/cm² Grade Count:15 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 3.00e+12 - 1.00e+15 ohm-cm | 3.00e+12 - 1.00e+15 ohm-cm | Average value: 4.80e+14 ohm-cm Grade Count:16 |
| Surface Resistance | 1.00e+10 - 1.00e+15 ohm | 1.00e+10 - 1.00e+15 ohm | Average value: 2.21e+14 ohm Grade Count:5 |
| Dielectric Constant | 2.90 - 12.0 | 2.90 - 12.0 | Average value: 4.11 Grade Count:16 |
| Dielectric Strength | 15.0 - 38.0 kV/mm | 381 - 965 kV/in | Average value: 26.6 kV/mm Grade Count:13 |
| Dissipation Factor | 0.0200 - 0.150 | 0.0200 - 0.150 | Average value: 0.0416 Grade Count:14 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:9 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 - 170 µm/m-°C | 27.8 - 94.4 µin/in-°F | Average value: 102 µm/m-°C Grade Count:14 |
| 160 - 180 µm/m-°C @Temperature 50.0 - 160 °C | 88.9 - 100 µin/in-°F @Temperature 122 - 320 °F | Average value: 170 µm/m-°C Grade Count:2 | |
| CTE, linear, Transverse to Flow | 180 - 180 µm/m-°C @Temperature 55.0 - 160 °C | 100 - 100 µin/in-°F @Temperature 131 - 320 °F | Average value: 180 µm/m-°C Grade Count:1 |
| Specific Heat Capacity | 1.67 - 1.88 J/g-°C | 0.399 - 0.450 BTU/lb-°F | Average value: 1.74 J/g-°C Grade Count:3 |
| Thermal Conductivity | 0.280 - 1.10 W/m-K | 1.94 - 7.63 BTU-in/hr-ft²-°F | Average value: 0.553 W/m-K Grade Count:3 |
| Melting Point | 142 - 224 °C | 288 - 435 °F | Average value: 207 °C Grade Count:24 |
| Maximum Service Temperature, Air | 100 - 160 °C | 212 - 320 °F | Average value: 133 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 - 210 °C | 275 - 410 °F | Average value: 162 °C Grade Count:21 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 - 190 °C | 122 - 374 °F | Average value: 75.6 °C Grade Count:25 |
| Vicat Softening Point | 110 - 210 °C | 230 - 410 °F | Average value: 176 °C Grade Count:14 |
| Minimum Service Temperature, Air | -100 - -40.0 °C | -148 - -40.0 °F | Average value: -55.0 °C Grade Count:3 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:23 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 190 - 279 °C | 374 - 535 °F | Average value: 229 °C Grade Count:4 |
| Melt Temperature | 230 - 290 °C | 446 - 554 °F | Average value: 264 °C Grade Count:5 |
| Mold Temperature | 50.0 - 93.3 °C | 122 - 200 °F | Average value: 75.3 °C Grade Count:7 |
| Drying Temperature | 79.4 - 82.2 °C | 175 - 180 °F | Average value: 80.1 °C Grade Count:5 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.75 hour Grade Count:4 |
| Moisture Content | 0.0200 - 2.00 % | 0.0200 - 2.00 % | Average value: 0.846 % Grade Count:8 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:3 |
| Injection Pressure | 68.9 - 124 MPa | 10000 - 18000 psi | Average value: 96.5 MPa Grade Count:5 |