  4. DuPont Performance Polymers Zytel® 77G33HS1L NC010 Nylon 612

DuPont Performance Polymers Zytel® 77G33HS1L NC010 Nylon 612

DuPont Performance Polymers Zytel® 77G33HS1L NC010 Nylon 612 物性表: DuPont Performance Polymers Zytel® 77G33HS1L NC010 Nylon 612物性表及特性介绍,DuPont Performance Polymers Zytel® 77G33HS1L NC010 Nylon 612注塑参数详情,如需DuPont Performance Polymers Zytel® 77G33HS1L NC010 Nylon 612下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.32
  • 吸水率 [%]: 0.16
  • 成型收缩率 [%]: 0.001
  • 缺口冲击强度: 1.28
  • 弯曲模量 [MPa]: 6.20
  • 硬度: 118.0
  • 热变形温度 [℃]: 216.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.32 g/cc1.32 g/ccDAM; ASTM D792
Density 1.32 g/cc0.0477 lb/in³DAM; ISO 1183
Filler Content 33 %33 %DAM
Water Absorption  0.16 %
@Temperature 23.0 °C		0.16 %
@Temperature 73.4 °F		Immersion 24h; DAM; ASTM D570
 2.0 %
@Temperature 23.0 °C		2.0 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 0.70 %
@Thickness 1.00 mm,
Temperature 23.0 °C		0.70 %
@Thickness 0.0394 in,
Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 1.8 %
@Thickness 1.00 mm,
Temperature 23.0 °C		1.8 %
@Thickness 0.0394 in,
Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage  0.0010 cm/cm
@Thickness 1.60 mm		0.0010 in/in
@Thickness 0.0630 in		Flow; DAM
 0.0020 cm/cm
@Thickness 3.20 mm		0.0020 in/in
@Thickness 0.126 in		Flow; DAM
 0.0040 cm/cm
@Thickness 6.40 mm		0.0040 in/in
@Thickness 0.252 in		Flow; DAM
 0.0090 cm/cm
@Thickness 1.60 mm		0.0090 in/in
@Thickness 0.0630 in		Transverse; DAM
 0.010 cm/cm
@Thickness 3.20 mm		0.010 in/in
@Thickness 0.126 in		Transverse; DAM
 0.011 cm/cm
@Thickness 6.40 mm		0.011 in/in
@Thickness 0.252 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.0030 cm/cm
@Thickness 2.00 mm		0.0030 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
@Thickness 2.00 mm		0.0090 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 118118DAM; ASTM D785
Tensile Strength at Break  140 MPa
@Temperature 23.0 °C		20300 psi
@Temperature 73.4 °F		50%RH; ISO 527
 168 MPa
@Temperature 23.0 °C		24400 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength  138 MPa
@Temperature 23.0 °C		20000 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 165 MPa
@Temperature 23.0 °C		23900 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  4.005 MPa
@Strain 0.100 %,
Temperature 150 °C		580.9 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.20 MPa
@Strain 0.100 %,
Temperature 150 °C		609 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.50 MPa
@Strain 0.100 %,
Temperature 120 °C		653 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.592 MPa
@Strain 0.100 %,
Temperature 100 °C		666.0 psi
@Strain 0.100 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 4.70 MPa
@Strain 0.100 %,
Temperature 120 °C		682 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.80 MPa
@Strain 0.100 %,
Temperature 100 °C		696 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 5.10 MPa
@Strain 0.100 %,
Temperature 80.0 °C		740 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 5.489 MPa
@Strain 0.100 %,
Temperature 80.0 °C		796.1 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 5.998 MPa
@Strain 0.100 %,
Temperature 60.0 °C		869.9 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 6.30 MPa
@Strain 0.100 %,
Temperature 60.0 °C		914 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 7.50 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1090 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 8.01 MPa
@Strain 0.200 %,
Temperature 150 °C		1160 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.10 MPa
@Strain 0.200 %,
Temperature 150 °C		1170 psi
@Strain 0.200 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.016 MPa
@Strain 0.200 %,
Temperature 120 °C		1308 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.30 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1350 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 9.40 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1360 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 9.50 MPa
@Strain 0.200 %,
Temperature 120 °C		1380 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.70 MPa
@Strain 0.200 %,
Temperature 100 °C		1410 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.75 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1410 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 9.765 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1416 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 9.879 MPa
@Strain 0.200 %,
Temperature 100 °C		1433 psi
@Strain 0.200 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.1 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1460 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 10.2 MPa
@Strain 0.200 %,
Temperature 80.0 °C		1480 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 10.746 MPa
@Strain 0.200 %,
Temperature 80.0 °C		1558.6 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.79 MPa
@Strain 0.300 %,
Temperature 150 °C		1710 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.8 MPa
@Strain 0.300 %,
Temperature 150 °C		1710 psi
@Strain 0.300 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.348 MPa
@Strain 0.200 %,
Temperature 60.0 °C		1790.9 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.6 MPa
@Strain 0.200 %,
Temperature 60.0 °C		1830 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 13.29 MPa
@Strain 0.300 %,
Temperature 120 °C		1928 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.0 MPa
@Strain 0.300 %,
Temperature 120 °C		2030 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.1 MPa
@Strain 0.300 %,
Temperature 100 °C		2050 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.569 MPa
@Strain 0.300 %,
Temperature 100 °C		2113.1 psi
@Strain 0.300 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.94 MPa
@Strain 0.400 %,
Temperature 150 °C		2167 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.0 MPa
@Strain 0.200 %,
Temperature 23.0 °C		2180 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 15.0 MPa
@Strain 0.300 %,
Temperature 80.0 °C		2180 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.7 MPa
@Strain 0.400 %,
Temperature 150 °C		2280 psi
@Strain 0.400 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.928 MPa
@Strain 0.300 %,
Temperature 80.0 °C		2310.2 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.51 MPa
@Strain 0.400 %,
Temperature 120 °C		2395 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.6 MPa
@Strain 0.400 %,
Temperature 100 °C		2550 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.032 MPa
@Strain 0.300 %,
Temperature 60.0 °C		2615.3 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.4 MPa
@Strain 0.400 %,
Temperature 120 °C		2670 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.561 MPa
@Strain 0.400 %,
Temperature 100 °C		2692.1 psi
@Strain 0.400 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.6 MPa
@Strain 0.200 %,
Temperature 23.0 °C		2700 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 18.8 MPa
@Strain 0.300 %,
Temperature 60.0 °C		2730 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 18.8 MPa
@Strain 0.400 %,
Temperature 80.0 °C		2730 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.8 MPa
@Strain 0.200 %,
Temperature 0.000 °C		2730 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 19.0 MPa
@Strain 0.500 %,
Temperature 150 °C		2760 psi
@Strain 0.500 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.17 MPa
@Strain 0.500 %,
Temperature 150 °C		2780 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.523 MPa
@Strain 0.200 %,
Temperature -40.0 °C		2831.6 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 20.0 MPa
@Strain 0.200 %,
Temperature 0.000 °C		2900 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 20.67 MPa
@Strain 0.200 %,
Temperature -40.0 °C		2998 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 21.16 MPa
@Strain 0.500 %,
Temperature 120 °C		3069 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.397 MPa
@Strain 0.400 %,
Temperature 80.0 °C		3103.4 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 22.0 MPa
@Strain 0.300 %,
Temperature 23.0 °C		3190 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 22.1 MPa
@Strain 0.600 %,
Temperature 150 °C		3210 psi
@Strain 0.600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.5 MPa
@Strain 0.500 %,
Temperature 120 °C		3260 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.736 MPa
@Strain 0.400 %,
Temperature 60.0 °C		3297.6 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.77 MPa
@Strain 0.600 %,
Temperature 150 °C		3303 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.9 MPa
@Strain 0.500 %,
Temperature 100 °C		3320 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.55 MPa
@Strain 0.500 %,
Temperature 100 °C		3416 psi
@Strain 0.500 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 24.7 MPa
@Strain 0.500 %,
Temperature 80.0 °C		3580 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 24.86 MPa
@Strain 0.600 %,
Temperature 120 °C		3606 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.9 MPa
@Strain 0.400 %,
Temperature 60.0 °C		3610 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 25.0 MPa
@Strain 0.700 %,
Temperature 150 °C		3630 psi
@Strain 0.700 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 26.098 MPa
@Strain 0.500 %,
Temperature 80.0 °C		3785.2 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 26.3 MPa
@Strain 0.600 %,
Temperature 120 °C		3810 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.37 MPa
@Strain 0.700 %,
Temperature 150 °C		3825 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.9 MPa
@Strain 0.600 %,
Temperature 100 °C		3900 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 27.5 MPa
@Strain 0.800 %,
Temperature 150 °C		3990 psi
@Strain 0.800 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 27.541 MPa
@Strain 0.600 %,
Temperature 100 °C		3994.5 psi
@Strain 0.600 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.7 MPa
@Strain 0.400 %,
Temperature 23.0 °C		4020 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.0 MPa
@Strain 0.300 %,
Temperature 0.000 °C		4060 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 28.1 MPa
@Strain 0.300 %,
Temperature 23.0 °C		4080 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.19 MPa
@Strain 0.700 %,
Temperature 120 °C		4089 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.413 MPa
@Strain 0.700 %,
Temperature 100 °C		4121.0 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.9 MPa
@Strain 0.600 %,
Temperature 80.0 °C		4190 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 29.008 MPa
@Strain 0.500 %,
Temperature 60.0 °C		4207.3 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.284 MPa
@Strain 0.300 %,
Temperature -40.0 °C		4247.3 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 29.42 MPa
@Strain 0.300 %,
Temperature 0.000 °C		4267 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 29.8 MPa
@Strain 0.700 %,
Temperature 120 °C		4320 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 29.88 MPa
@Strain 0.800 %,
Temperature 150 °C		4334 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.9 MPa
@Strain 0.900 %,
Temperature 150 °C		4340 psi
@Strain 0.900 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 30.0 MPa
@Strain 0.300 %,
Temperature -40.0 °C		4350 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 30.512 MPa
@Strain 0.600 %,
Temperature 80.0 °C		4425.4 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 30.9 MPa
@Strain 0.500 %,
Temperature 60.0 °C		4480 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 31.333 MPa
@Strain 0.700 %,
Temperature 100 °C		4544.5 psi
@Strain 0.700 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.41 MPa
@Strain 0.800 %,
Temperature 120 °C		4556 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.0 MPa
@Strain 1.00 %,
Temperature 150 °C		4640 psi
@Strain 1.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 32.21 MPa
@Strain 0.800 %,
Temperature 100 °C		4672 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.6 MPa
@Strain 0.700 %,
Temperature 80.0 °C		4730 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.8 MPa
@Strain 0.800 %,
Temperature 120 °C		4760 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.94 MPa
@Strain 0.900 %,
Temperature 150 °C		4778 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.1 MPa
@Strain 1.10 %,
Temperature 150 °C		4950 psi
@Strain 1.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.104 MPa
@Strain 0.600 %,
Temperature 60.0 °C		4946.4 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 34.35 MPa
@Strain 0.900 %,
Temperature 120 °C		4982 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.734 MPa
@Strain 0.700 %,
Temperature 80.0 °C		5037.8 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.026 MPa
@Strain 0.800 %,
Temperature 100 °C		5080.1 psi
@Strain 0.800 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 35.55 MPa
@Strain 1.00 %,
Temperature 150 °C		5156 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 35.868 MPa
@Strain 0.900 %,
Temperature 100 °C		5202.2 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.9 MPa
@Strain 0.900 %,
Temperature 120 °C		5210 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.9 MPa
@Strain 1.20 %,
Temperature 150 °C		5210 psi
@Strain 1.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.3 MPa
@Strain 0.800 %,
Temperature 80.0 °C		5260 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 36.5 MPa
@Strain 0.600 %,
Temperature 60.0 °C		5290 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.8 MPa
@Strain 0.500 %,
Temperature 23.0 °C		5340 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 37.0 MPa
@Strain 0.400 %,
Temperature 0.000 °C		5370 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 37.11 MPa
@Strain 1.00 %,
Temperature 120 °C		5382 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.7 MPa
@Strain 1.30 %,
Temperature 150 °C		5470 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 37.75 MPa
@Strain 0.400 %,
Temperature 23.0 °C		5475 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 37.8 MPa
@Strain 1.10 %,
Temperature 150 °C		5480 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 38.184 MPa
@Strain 0.400 %,
Temperature -40.0 °C		5538.1 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 38.219 MPa
@Strain 0.900 %,
Temperature 100 °C		5543.2 psi
@Strain 0.900 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.572 MPa
@Strain 0.800 %,
Temperature 80.0 °C		5594.4 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 38.6 MPa
@Strain 1.00 %,
Temperature 120 °C		5600 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.71 MPa
@Strain 0.700 %,
Temperature 60.0 °C		5614 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.2 MPa
@Strain 0.400 %,
Temperature 0.000 °C		5690 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 39.3 MPa
@Strain 1.40 %,
Temperature 150 °C		5700 psi
@Strain 1.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 39.39 MPa
@Strain 1.00 %,
Temperature 100 °C		5713 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 39.76 MPa
@Strain 1.10 %,
Temperature 120 °C		5767 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 39.8 MPa
@Strain 0.900 %,
Temperature 80.0 °C		5770 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.87 MPa
@Strain 1.20 %,
Temperature 150 °C		5783 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.1 MPa
@Strain 0.400 %,
Temperature -40.0 °C		5820 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 40.9 MPa
@Strain 1.50 %,
Temperature 150 °C		5930 psi
@Strain 1.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 41.113 MPa
@Strain 1.00 %,
Temperature 100 °C		5962.9 psi
@Strain 1.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 41.3 MPa
@Strain 1.10 %,
Temperature 120 °C		5990 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.6 MPa
@Strain 0.700 %,
Temperature 60.0 °C		6030 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.76 MPa
@Strain 1.30 %,
Temperature 150 °C		6057 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.122 MPa
@Strain 0.900 %,
Temperature 80.0 °C		6109.3 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.136 MPa
@Strain 1.20 %,
Temperature 120 °C		6111.3 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 42.4 MPa
@Strain 1.60 %,
Temperature 150 °C		6150 psi
@Strain 1.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.486 MPa
@Strain 1.10 %,
Temperature 100 °C		6162.1 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 43.0 MPa
@Strain 1.00 %,
Temperature 80.0 °C		6240 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.218 MPa
@Strain 0.800 %,
Temperature 60.0 °C		6268.3 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 43.56 MPa
@Strain 1.40 %,
Temperature 150 °C		6318 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.8 MPa
@Strain 1.70 %,
Temperature 150 °C		6350 psi
@Strain 1.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 43.8 MPa
@Strain 1.20 %,
Temperature 120 °C		6350 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.1 MPa
@Strain 0.600 %,
Temperature 23.0 °C		6400 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 44.206 MPa
@Strain 1.10 %,
Temperature 100 °C		6411.5 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.413 MPa
@Strain 1.30 %,
Temperature 120 °C		6441.6 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 45.1 MPa
@Strain 1.80 %,
Temperature 150 °C		6540 psi
@Strain 1.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 45.18 MPa
@Strain 1.50 %,
Temperature 150 °C		6553 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.259 MPa
@Strain 1.20 %,
Temperature 100 °C		6564.3 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.48 MPa
@Strain 1.00 %,
Temperature 80.0 °C		6596 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.1 MPa
@Strain 1.10 %,
Temperature 80.0 °C		6690 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 46.2 MPa
@Strain 1.30 %,
Temperature 120 °C		6700 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 46.2 MPa
@Strain 1.90 %,
Temperature 150 °C		6700 psi
@Strain 1.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 46.5 MPa
@Strain 0.800 %,
Temperature 60.0 °C		6740 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 46.6 MPa
@Strain 0.500 %,
Temperature 0.000 °C		6760 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 46.691 MPa
@Strain 1.40 %,
Temperature 120 °C		6772.0 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.71 MPa
@Strain 1.60 %,
Temperature 150 °C		6775 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 46.85 MPa
@Strain 0.500 %,
Temperature 23.0 °C		6795 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 47.1 MPa
@Strain 1.20 %,
Temperature 100 °C		6830 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 47.4 MPa
@Strain 2.00 %,
Temperature 150 °C		6870 psi
@Strain 2.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 47.628 MPa
@Strain 0.900 %,
Temperature 60.0 °C		6907.9 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 48.0 MPa
@Strain 1.30 %,
Temperature 100 °C		6960 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.15 MPa
@Strain 1.70 %,
Temperature 150 °C		6984 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.4 MPa
@Strain 1.40 %,
Temperature 120 °C		7020 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 48.41 MPa
@Strain 0.500 %,
Temperature 0.000 °C		7021 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 48.5 MPa
@Strain 2.10 %,
Temperature 150 °C		7030 psi
@Strain 2.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 48.839 MPa
@Strain 1.10 %,
Temperature 80.0 °C		7083.5 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.968 MPa
@Strain 1.50 %,
Temperature 120 °C		7102.2 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.998 MPa
@Strain 0.500 %,
Temperature -40.0 °C		7106.6 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 49.4 MPa
@Strain 1.20 %,
Temperature 80.0 °C		7160 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 49.5 MPa
@Strain 1.80 %,
Temperature 150 °C		7180 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 49.6 MPa
@Strain 2.20 %,
Temperature 150 °C		7190 psi
@Strain 2.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 49.794 MPa
@Strain 1.30 %,
Temperature 100 °C		7222.0 psi
@Strain 1.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 50.3 MPa
@Strain 1.50 %,
Temperature 120 °C		7300 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 50.5 MPa
@Strain 2.30 %,
Temperature 150 °C		7320 psi
@Strain 2.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 50.6 MPa
@Strain 0.900 %,
Temperature 60.0 °C		7340 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.8 MPa
@Strain 0.500 %,
Temperature -40.0 °C		7370 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 50.85 MPa
@Strain 1.90 %,
Temperature 150 °C		7375 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 50.866 MPa
@Strain 1.60 %,
Temperature 120 °C		7377.5 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.1 MPa
@Strain 0.700 %,
Temperature 23.0 °C		7410 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.4 MPa
@Strain 2.40 %,
Temperature 150 °C		7450 psi
@Strain 2.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 51.646 MPa
@Strain 1.00 %,
Temperature 60.0 °C		7490.6 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.909 MPa
@Strain 1.20 %,
Temperature 80.0 °C		7528.8 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.11 MPa
@Strain 2.00 %,
Temperature 150 °C		7558 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 52.289 MPa
@Strain 1.40 %,
Temperature 100 °C		7583.9 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 52.3 MPa
@Strain 1.60 %,
Temperature 120 °C		7590 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 52.3 MPa
@Strain 2.50 %,
Temperature 150 °C		7590 psi
@Strain 2.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 52.5 MPa
@Strain 1.30 %,
Temperature 80.0 °C		7610 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 52.501 MPa
@Strain 1.40 %,
Temperature 100 °C		7614.6 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.764 MPa
@Strain 1.70 %,
Temperature 120 °C		7652.8 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.0 MPa
@Strain 2.60 %,
Temperature 150 °C		7690 psi
@Strain 2.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 53.19 MPa
@Strain 2.10 %,
Temperature 150 °C		7715 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 53.671 MPa
@Strain 1.50 %,
Temperature 100 °C		7784.3 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 53.7 MPa
@Strain 2.70 %,
Temperature 150 °C		7790 psi
@Strain 2.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 54.1 MPa
@Strain 1.70 %,
Temperature 120 °C		7850 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 54.36 MPa
@Strain 2.20 %,
Temperature 150 °C		7884 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 54.4 MPa
@Strain 2.80 %,
Temperature 150 °C		7890 psi
@Strain 2.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 54.473 MPa
@Strain 1.80 %,
Temperature 120 °C		7900.7 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.584 MPa
@Strain 1.50 %,
Temperature 100 °C		7916.8 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 54.6 MPa
@Strain 1.00 %,
Temperature 60.0 °C		7920 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.787 MPa
@Strain 1.30 %,
Temperature 80.0 °C		7946.2 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 55.1 MPa
@Strain 2.90 %,
Temperature 150 °C		7990 psi
@Strain 2.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 55.44 MPa
@Strain 2.30 %,
Temperature 150 °C		8041 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 55.5 MPa
@Strain 1.40 %,
Temperature 80.0 °C		8050 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.566 MPa
@Strain 1.10 %,
Temperature 60.0 °C		8059.2 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.6 MPa
@Strain 3.00 %,
Temperature 150 °C		8060 psi
@Strain 3.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 55.8 MPa
@Strain 1.80 %,
Temperature 120 °C		8090 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 55.9 MPa
@Strain 0.600 %,
Temperature 23.0 °C		8110 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 55.9 MPa
@Strain 0.600 %,
Temperature 0.000 °C		8110 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 55.955 MPa
@Strain 1.60 %,
Temperature 100 °C		8115.6 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 56.086 MPa
@Strain 1.90 %,
Temperature 120 °C		8134.6 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 56.1 MPa
@Strain 3.10 %,
Temperature 150 °C		8140 psi
@Strain 3.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 56.34 MPa
@Strain 2.40 %,
Temperature 150 °C		8171 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 56.5 MPa
@Strain 3.20 %,
Temperature 150 °C		8190 psi
@Strain 3.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 56.84 MPa
@Strain 0.600 %,
Temperature 0.000 °C		8244 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 57.0 MPa
@Strain 3.30 %,
Temperature 150 °C		8270 psi
@Strain 3.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 57.079 MPa
@Strain 1.60 %,
Temperature 100 °C		8278.6 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 57.33 MPa
@Strain 2.50 %,
Temperature 150 °C		8315 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 57.4 MPa
@Strain 1.90 %,
Temperature 120 °C		8330 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 57.4 MPa
@Strain 3.40 %,
Temperature 150 °C		8330 psi
@Strain 3.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 57.474 MPa
@Strain 1.40 %,
Temperature 80.0 °C		8335.9 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 57.6 MPa
@Strain 0.800 %,
Temperature 23.0 °C		8350 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 57.604 MPa
@Strain 2.00 %,
Temperature 120 °C		8354.8 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 57.7 MPa
@Strain 3.50 %,
Temperature 150 °C		8370 psi
@Strain 3.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 58.0 MPa
@Strain 0.600 %,
Temperature -40.0 °C		8410 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 58.14 MPa
@Strain 2.60 %,
Temperature 150 °C		8433 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 58.2 MPa
@Strain 1.50 %,
Temperature 80.0 °C		8440 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 58.307 MPa
@Strain 1.70 %,
Temperature 100 °C		8456.7 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 58.6 MPa
@Strain 1.10 %,
Temperature 60.0 °C		8500 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 58.9 MPa
@Strain 2.00 %,
Temperature 120 °C		8540 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 59.04 MPa
@Strain 2.70 %,
Temperature 150 °C		8563 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 59.047 MPa
@Strain 0.600 %,
Temperature -40.0 °C		8564.1 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 59.174 MPa
@Strain 1.70 %,
Temperature 100 °C		8582.5 psi
@Strain 1.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 59.29 MPa
@Strain 1.20 %,
Temperature 60.0 °C		8599 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.313 MPa
@Strain 2.10 %,
Temperature 120 °C		8602.6 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 59.67 MPa
@Strain 2.80 %,
Temperature 150 °C		8654 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 60.161 MPa
@Strain 1.50 %,
Temperature 80.0 °C		8725.6 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 60.3 MPa
@Strain 2.10 %,
Temperature 120 °C		8750 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 60.348 MPa
@Strain 1.80 %,
Temperature 100 °C		8752.8 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.48 MPa
@Strain 2.90 %,
Temperature 150 °C		8772 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 60.641 MPa
@Strain 2.20 %,
Temperature 120 °C		8795.2 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 61.1 MPa
@Strain 1.60 %,
Temperature 80.0 °C		8860 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.11 MPa
@Strain 3.00 %,
Temperature 150 °C		8863 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 61.17 MPa
@Strain 1.80 %,
Temperature 100 °C		8872 psi
@Strain 1.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 61.7 MPa
@Strain 2.20 %,
Temperature 120 °C		8950 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 61.74 MPa
@Strain 3.10 %,
Temperature 150 °C		8955 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 62.065 MPa
@Strain 2.30 %,
Temperature 120 °C		9001.8 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 62.3 MPa
@Strain 1.20 %,
Temperature 60.0 °C		9040 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 62.365 MPa
@Strain 1.90 %,
Temperature 100 °C		9045.3 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 62.37 MPa
@Strain 3.20 %,
Temperature 150 °C		9046 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 62.655 MPa
@Strain 1.60 %,
Temperature 80.0 °C		9087.4 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 62.72 MPa
@Strain 1.30 %,
Temperature 60.0 °C		9097 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 62.866 MPa
@Strain 1.90 %,
Temperature 100 °C		9118.0 psi
@Strain 1.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 62.91 MPa
@Strain 3.30 %,
Temperature 150 °C		9124 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 63.0 MPa
@Strain 2.30 %,
Temperature 120 °C		9140 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 63.298 MPa
@Strain 2.40 %,
Temperature 120 °C		9180.6 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 63.4 MPa
@Strain 0.900 %,
Temperature 23.0 °C		9200 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.45 MPa
@Strain 3.40 %,
Temperature 150 °C		9203 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 63.5 MPa
@Strain 1.70 %,
Temperature 80.0 °C		9210 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.9 MPa
@Strain 3.50 %,
Temperature 150 °C		9270 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 64.077 MPa
@Strain 2.00 %,
Temperature 100 °C		9293.6 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 64.2 MPa
@Strain 2.40 %,
Temperature 120 °C		9310 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 64.26 MPa
@Strain 3.60 %,
Temperature 150 °C		9320 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 64.532 MPa
@Strain 2.50 %,
Temperature 120 °C		9359.6 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 64.65 MPa
@Strain 0.700 %,
Temperature 23.0 °C		9377 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 64.663 MPa
@Strain 2.00 %,
Temperature 100 °C		9378.6 psi
@Strain 2.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 64.71 MPa
@Strain 3.70 %,
Temperature 150 °C		9385 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 64.8 MPa
@Strain 0.700 %,
Temperature 0.000 °C		9400 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.958 MPa
@Strain 1.70 %,
Temperature 80.0 °C		9421.4 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 65.07 MPa
@Strain 3.80 %,
Temperature 150 °C		9438 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.2 MPa
@Strain 2.50 %,
Temperature 120 °C		9460 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 65.34 MPa
@Strain 3.90 %,
Temperature 150 °C		9477 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.671 MPa
@Strain 2.60 %,
Temperature 120 °C		9524.8 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 65.7 MPa
@Strain 4.00 %,
Temperature 150 °C		9530 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.768 MPa
@Strain 2.10 %,
Temperature 100 °C		9538.9 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 65.856 MPa
@Strain 1.40 %,
Temperature 60.0 °C		9551.6 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 65.9 MPa
@Strain 1.30 %,
Temperature 60.0 °C		9560 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 65.97 MPa
@Strain 4.10 %,
Temperature 150 °C		9568 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 66.0 MPa
@Strain 1.80 %,
Temperature 80.0 °C		9570 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.2 MPa
@Strain 2.60 %,
Temperature 120 °C		9600 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 66.24 MPa
@Strain 4.20 %,
Temperature 150 °C		9607 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 66.359 MPa
@Strain 2.10 %,
Temperature 100 °C		9624.6 psi
@Strain 2.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 66.42 MPa
@Strain 4.30 %,
Temperature 150 °C		9633 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 66.51 MPa
@Strain 4.40 %,
Temperature 150 °C		9646 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 66.52 MPa
@Strain 0.700 %,
Temperature 0.000 °C		9648 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 66.715 MPa
@Strain 2.70 %,
Temperature 120 °C		9676.2 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 66.973 MPa
@Strain 1.80 %,
Temperature 80.0 °C		9713.6 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 67.1 MPa
@Strain 2.70 %,
Temperature 120 °C		9730 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 67.344 MPa
@Strain 2.20 %,
Temperature 100 °C		9767.4 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 67.664 MPa
@Strain 2.80 %,
Temperature 120 °C		9813.9 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 67.756 MPa
@Strain 2.20 %,
Temperature 100 °C		9827.2 psi
@Strain 2.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 67.9 MPa
@Strain 2.80 %,
Temperature 120 °C		9850 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 68.234 MPa
@Strain 0.700 %,
Temperature -40.0 °C		9896.5 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 68.3 MPa
@Strain 0.700 %,
Temperature -40.0 °C		9910 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 68.3 MPa
@Strain 1.90 %,
Temperature 80.0 °C		9910 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 68.613 MPa
@Strain 2.90 %,
Temperature 120 °C		9951.5 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 68.7 MPa
@Strain 2.90 %,
Temperature 120 °C		9960 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 68.717 MPa
@Strain 2.30 %,
Temperature 100 °C		9966.6 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 68.992 MPa
@Strain 1.50 %,
Temperature 60.0 °C		10006 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 69.084 MPa
@Strain 1.90 %,
Temperature 80.0 °C		10020 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 69.2 MPa
@Strain 1.40 %,
Temperature 60.0 °C		10000 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 69.2 MPa
@Strain 1.00 %,
Temperature 23.0 °C		10000 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 69.3 MPa
@Strain 3.00 %,
Temperature 120 °C		10100 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 69.353 MPa
@Strain 2.30 %,
Temperature 100 °C		10059 psi
@Strain 2.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 69.562 MPa
@Strain 3.00 %,
Temperature 120 °C		10089 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 69.979 MPa
@Strain 2.40 %,
Temperature 100 °C		10150 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 70.0 MPa
@Strain 3.10 %,
Temperature 120 °C		10200 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 70.321 MPa
@Strain 3.10 %,
Temperature 120 °C		10199 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 70.4 MPa
@Strain 3.20 %,
Temperature 120 °C		10200 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 70.65 MPa
@Strain 2.40 %,
Temperature 100 °C		10250 psi
@Strain 2.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 70.7 MPa
@Strain 2.00 %,
Temperature 80.0 °C		10300 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.9 MPa
@Strain 3.30 %,
Temperature 120 °C		10300 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 71.003 MPa
@Strain 2.00 %,
Temperature 80.0 °C		10298 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 71.08 MPa
@Strain 3.20 %,
Temperature 120 °C		10310 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 71.133 MPa
@Strain 2.50 %,
Temperature 100 °C		10317 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 71.3 MPa
@Strain 3.40 %,
Temperature 120 °C		10300 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 71.6 MPa
@Strain 3.50 %,
Temperature 120 °C		10400 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 71.839 MPa
@Strain 3.30 %,
Temperature 120 °C		10419 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 71.932 MPa
@Strain 1.60 %,
Temperature 60.0 °C		10433 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 71.947 MPa
@Strain 2.50 %,
Temperature 100 °C		10435 psi
@Strain 2.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 72.18 MPa
@Strain 2.60 %,
Temperature 100 °C		10470 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 72.314 MPa
@Strain 3.40 %,
Temperature 120 °C		10488 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 72.5 MPa
@Strain 1.50 %,
Temperature 60.0 °C		10500 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 72.7 MPa
@Strain 0.800 %,
Temperature 23.0 °C		10500 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 72.826 MPa
@Strain 2.10 %,
Temperature 80.0 °C		10563 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 72.9 MPa
@Strain 2.10 %,
Temperature 80.0 °C		10600 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 72.978 MPa
@Strain 3.50 %,
Temperature 120 °C		10585 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 73.0 MPa
@Strain 0.800 %,
Temperature 0.000 °C		10600 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.04 MPa
@Strain 0.800 %,
Temperature 0.000 °C		10590 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 73.045 MPa
@Strain 2.60 %,
Temperature 100 °C		10594 psi
@Strain 2.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 73.53 MPa
@Strain 2.70 %,
Temperature 100 °C		10660 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 73.548 MPa
@Strain 3.60 %,
Temperature 120 °C		10667 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 73.832 MPa
@Strain 3.70 %,
Temperature 120 °C		10708 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 74.043 MPa
@Strain 2.70 %,
Temperature 100 °C		10739 psi
@Strain 2.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 74.307 MPa
@Strain 3.80 %,
Temperature 120 °C		10777 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 74.457 MPa
@Strain 2.20 %,
Temperature 80.0 °C		10799 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 74.591 MPa
@Strain 3.90 %,
Temperature 120 °C		10819 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 74.676 MPa
@Strain 1.70 %,
Temperature 60.0 °C		10831 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 74.7 MPa
@Strain 1.10 %,
Temperature 23.0 °C		10800 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.841 MPa
@Strain 2.80 %,
Temperature 100 °C		10855 psi
@Strain 2.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 74.97 MPa
@Strain 2.80 %,
Temperature 100 °C		10870 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 75.0 MPa
@Strain 4.00 %,
Temperature 120 °C		10900 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 75.0 MPa
@Strain 2.20 %,
Temperature 80.0 °C		10900 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 75.6 MPa
@Strain 1.60 %,
Temperature 60.0 °C		11000 psi
@Strain 1.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 75.639 MPa
@Strain 2.90 %,
Temperature 100 °C		10971 psi
@Strain 2.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 75.7 MPa
@Strain 0.800 %,
Temperature -40.0 °C		11000 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 76.088 MPa
@Strain 2.30 %,
Temperature 80.0 °C		11036 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 76.23 MPa
@Strain 2.90 %,
Temperature 100 °C		11060 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 76.338 MPa
@Strain 3.00 %,
Temperature 100 °C		11072 psi
@Strain 3.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 76.937 MPa
@Strain 3.10 %,
Temperature 100 °C		11159 psi
@Strain 3.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 77.0 MPa
@Strain 2.30 %,
Temperature 80.0 °C		11200 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 77.038 MPa
@Strain 0.800 %,
Temperature -40.0 °C		11173 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 77.322 MPa
@Strain 1.80 %,
Temperature 60.0 °C		11215 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 77.4 MPa
@Strain 3.00 %,
Temperature 100 °C		11200 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 77.528 MPa
@Strain 2.40 %,
Temperature 80.0 °C		11245 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 77.535 MPa
@Strain 3.20 %,
Temperature 100 °C		11246 psi
@Strain 3.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 77.835 MPa
@Strain 3.30 %,
Temperature 100 °C		11289 psi
@Strain 3.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 78.234 MPa
@Strain 3.40 %,
Temperature 100 °C		11347 psi
@Strain 3.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 78.533 MPa
@Strain 3.50 %,
Temperature 100 °C		11390 psi
@Strain 3.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 78.57 MPa
@Strain 3.10 %,
Temperature 100 °C		11400 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 78.7 MPa
@Strain 1.70 %,
Temperature 60.0 °C		11400 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.775 MPa
@Strain 2.50 %,
Temperature 80.0 °C		11425 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 78.9 MPa
@Strain 2.40 %,
Temperature 80.0 °C		11400 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 79.74 MPa
@Strain 3.20 %,
Temperature 100 °C		11570 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 79.87 MPa
@Strain 1.90 %,
Temperature 60.0 °C		11580 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 80.0 MPa
@Strain 1.20 %,
Temperature 23.0 °C		11600 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 80.022 MPa
@Strain 2.60 %,
Temperature 80.0 °C		11606 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 80.6 MPa
@Strain 0.900 %,
Temperature 23.0 °C		11700 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.64 MPa
@Strain 3.30 %,
Temperature 100 °C		11700 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 80.8 MPa
@Strain 2.50 %,
Temperature 80.0 °C		11700 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 81.078 MPa
@Strain 2.70 %,
Temperature 80.0 °C		11759 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 81.1 MPa
@Strain 0.900 %,
Temperature 0.000 °C		11800 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 81.45 MPa
@Strain 3.40 %,
Temperature 100 °C		11810 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 81.6 MPa
@Strain 1.80 %,
Temperature 60.0 °C		11800 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.02 MPa
@Strain 0.900 %,
Temperature 0.000 °C		11900 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 82.037 MPa
@Strain 2.80 %,
Temperature 80.0 °C		11898 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 82.222 MPa
@Strain 2.00 %,
Temperature 60.0 °C		11925 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 82.35 MPa
@Strain 3.50 %,
Temperature 100 °C		11940 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 82.5 MPa
@Strain 2.60 %,
Temperature 80.0 °C		12000 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 82.98 MPa
@Strain 3.60 %,
Temperature 100 °C		12040 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 82.997 MPa
@Strain 2.90 %,
Temperature 80.0 °C		12038 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 83.61 MPa
@Strain 3.70 %,
Temperature 100 °C		12130 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 83.668 MPa
@Strain 3.00 %,
Temperature 80.0 °C		12135 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 84.2 MPa
@Strain 2.70 %,
Temperature 80.0 °C		12200 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 84.2 MPa
@Strain 1.90 %,
Temperature 60.0 °C		12200 psi
@Strain 1.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 84.24 MPa
@Strain 3.80 %,
Temperature 100 °C		12220 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 84.244 MPa
@Strain 3.10 %,
Temperature 80.0 °C		12219 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 84.476 MPa
@Strain 2.10 %,
Temperature 60.0 °C		12252 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 84.724 MPa
@Strain 3.20 %,
Temperature 80.0 °C		12288 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 84.87 MPa
@Strain 3.90 %,
Temperature 100 °C		12310 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 84.9 MPa
@Strain 1.30 %,
Temperature 23.0 °C		12300 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 84.9 MPa
@Strain 0.900 %,
Temperature -40.0 °C		12300 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 85.012 MPa
@Strain 3.30 %,
Temperature 80.0 °C		12330 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 85.3 MPa
@Strain 3.40 %,
Temperature 80.0 °C		12400 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 85.32 MPa
@Strain 4.00 %,
Temperature 100 °C		12370 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 85.46 MPa
@Strain 0.900 %,
Temperature -40.0 °C		12390 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 85.491 MPa
@Strain 3.50 %,
Temperature 80.0 °C		12399 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 85.68 MPa
@Strain 4.10 %,
Temperature 100 °C		12430 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 85.8 MPa
@Strain 2.80 %,
Temperature 80.0 °C		12400 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 86.13 MPa
@Strain 4.20 %,
Temperature 100 °C		12490 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 86.4 MPa
@Strain 4.30 %,
Temperature 100 °C		12500 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 86.632 MPa
@Strain 2.20 %,
Temperature 60.0 °C		12565 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 86.67 MPa
@Strain 4.40 %,
Temperature 100 °C		12570 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 86.9 MPa
@Strain 2.00 %,
Temperature 60.0 °C		12600 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 87.03 MPa
@Strain 4.50 %,
Temperature 100 °C		12620 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 87.21 MPa
@Strain 4.60 %,
Temperature 100 °C		12650 psi
@Strain 4.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 87.39 MPa
@Strain 4.70 %,
Temperature 100 °C		12670 psi
@Strain 4.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 87.4 MPa
@Strain 2.90 %,
Temperature 80.0 °C		12700 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 87.66 MPa
@Strain 4.80 %,
Temperature 100 °C		12710 psi
@Strain 4.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 87.75 MPa
@Strain 4.90 %,
Temperature 100 °C		12730 psi
@Strain 4.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 87.84 MPa
@Strain 5.00 %,
Temperature 100 °C		12740 psi
@Strain 5.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 88.05 MPa
@Strain 1.00 %,
Temperature 23.0 °C		12770 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 88.494 MPa
@Strain 2.30 %,
Temperature 60.0 °C		12835 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 88.7 MPa
@Strain 1.00 %,
Temperature 0.000 °C		12900 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 88.7 MPa
@Strain 3.00 %,
Temperature 80.0 °C		12900 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 89.2 MPa
@Strain 2.10 %,
Temperature 60.0 °C		12900 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 89.5 MPa
@Strain 1.40 %,
Temperature 23.0 °C		13000 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 90.1 MPa
@Strain 3.10 %,
Temperature 80.0 °C		13100 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 90.258 MPa
@Strain 2.40 %,
Temperature 60.0 °C		13091 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 90.9 MPa
@Strain 1.00 %,
Temperature 0.000 °C		13200 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.3 MPa
@Strain 3.20 %,
Temperature 80.0 °C		13200 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 91.7 MPa
@Strain 2.20 %,
Temperature 60.0 °C		13300 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 91.826 MPa
@Strain 2.50 %,
Temperature 60.0 °C		13318 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 92.4 MPa
@Strain 3.30 %,
Temperature 80.0 °C		13400 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 93.0 MPa
@Strain 1.00 %,
Temperature -40.0 °C		13500 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.394 MPa
@Strain 2.60 %,
Temperature 60.0 °C		13546 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 93.4 MPa
@Strain 3.40 %,
Temperature 80.0 °C		13500 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 94.0 MPa
@Strain 2.30 %,
Temperature 60.0 °C		13600 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 94.0 MPa
@Strain 1.50 %,
Temperature 23.0 °C		13600 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 94.265 MPa
@Strain 1.00 %,
Temperature -40.0 °C		13672 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 94.3 MPa
@Strain 3.50 %,
Temperature 80.0 °C		13700 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 94.766 MPa
@Strain 2.70 %,
Temperature 60.0 °C		13745 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 95.1 MPa
@Strain 3.60 %,
Temperature 80.0 °C		13800 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 95.2 MPa
@Strain 1.10 %,
Temperature 23.0 °C		13800 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 95.5 MPa
@Strain 1.10 %,
Temperature 0.000 °C		13900 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 95.9 MPa
@Strain 3.70 %,
Temperature 80.0 °C		13900 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 96.04 MPa
@Strain 2.80 %,
Temperature 60.0 °C		13930 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 96.2 MPa
@Strain 2.40 %,
Temperature 60.0 °C		14000 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 96.5 MPa
@Strain 3.80 %,
Temperature 80.0 °C		14000 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 96.922 MPa
@Strain 2.90 %,
Temperature 60.0 °C		14057 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 97.0 MPa
@Strain 4.00 %,
Temperature 80.0 °C		14100 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 97.1 MPa
@Strain 3.90 %,
Temperature 80.0 °C		14100 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 97.706 MPa
@Strain 3.00 %,
Temperature 60.0 °C		14171 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 98.1 MPa
@Strain 1.60 %,
Temperature 23.0 °C		14200 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 98.2 MPa
@Strain 2.50 %,
Temperature 60.0 °C		14200 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 98.588 MPa
@Strain 3.10 %,
Temperature 60.0 °C		14299 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 98.79 MPa
@Strain 1.10 %,
Temperature 0.000 °C		14330 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 99.078 MPa
@Strain 3.20 %,
Temperature 60.0 °C		14370 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 99.568 MPa
@Strain 3.30 %,
Temperature 60.0 °C		14441 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 99.764 MPa
@Strain 3.40 %,
Temperature 60.0 °C		14470 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 100 MPa
@Strain 3.50 %,
Temperature 60.0 °C		14500 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 100.1 MPa
@Strain 2.60 %,
Temperature 60.0 °C		14520 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 100.7 MPa
@Strain 1.10 %,
Temperature -40.0 °C		14610 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 101.25 MPa
@Strain 1.10 %,
Temperature -40.0 °C		14685 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 101.7 MPa
@Strain 2.70 %,
Temperature 60.0 °C		14750 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 102.1 MPa
@Strain 1.70 %,
Temperature 23.0 °C		14810 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 102.2 MPa
@Strain 1.20 %,
Temperature 23.0 °C		14820 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 102.7 MPa
@Strain 1.20 %,
Temperature 0.000 °C		14900 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 103.3 MPa
@Strain 2.80 %,
Temperature 60.0 °C		14980 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 104.6 MPa
@Strain 2.90 %,
Temperature 60.0 °C		15170 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 105.4 MPa
@Strain 1.80 %,
Temperature 23.0 °C		15290 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 106.1 MPa
@Strain 3.00 %,
Temperature 60.0 °C		15390 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 106.76 MPa
@Strain 1.20 %,
Temperature 0.000 °C		15484 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 107.4 MPa
@Strain 3.10 %,
Temperature 60.0 °C		15580 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 108.1 MPa
@Strain 1.30 %,
Temperature 0.000 °C		15680 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 108.35 MPa
@Strain 1.30 %,
Temperature 23.0 °C		15715 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 108.4 MPa
@Strain 1.20 %,
Temperature -40.0 °C		15720 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 108.6 MPa
@Strain 1.90 %,
Temperature 23.0 °C		15750 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 108.7 MPa
@Strain 3.20 %,
Temperature 60.0 °C		15770 psi
@Strain 3.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 109.8 MPa
@Strain 3.30 %,
Temperature 60.0 °C		15930 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 109.86 MPa
@Strain 1.20 %,
Temperature -40.0 °C		15934 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.8 MPa
@Strain 3.40 %,
Temperature 60.0 °C		16070 psi
@Strain 3.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 111.6 MPa
@Strain 3.50 %,
Temperature 60.0 °C		16190 psi
@Strain 3.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 112.1 MPa
@Strain 3.60 %,
Temperature 60.0 °C		16260 psi
@Strain 3.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 112.5 MPa
@Strain 3.70 %,
Temperature 60.0 °C		16320 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 112.6 MPa
@Strain 2.00 %,
Temperature 23.0 °C		16330 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 112.9 MPa
@Strain 3.80 %,
Temperature 60.0 °C		16370 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 113 MPa
@Strain 3.90 %,
Temperature 60.0 °C		16400 psi
@Strain 3.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 113 MPa
@Strain 4.00 %,
Temperature 60.0 °C		16400 psi
@Strain 4.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 114.35 MPa
@Strain 1.40 %,
Temperature 23.0 °C		16585 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 114.65 MPa
@Strain 1.30 %,
Temperature 0.000 °C		16629 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 114.9 MPa
@Strain 1.40 %,
Temperature 0.000 °C		16660 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 115.7 MPa
@Strain 2.10 %,
Temperature 23.0 °C		16780 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 116.66 MPa
@Strain 1.30 %,
Temperature -40.0 °C		16920 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 117.1 MPa
@Strain 1.30 %,
Temperature -40.0 °C		16980 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 118.3 MPa
@Strain 2.20 %,
Temperature 23.0 °C		17160 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 119.85 MPa
@Strain 1.50 %,
Temperature 23.0 °C		17383 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 120.51 MPa
@Strain 1.40 %,
Temperature 0.000 °C		17479 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 120.7 MPa
@Strain 1.50 %,
Temperature 0.000 °C		17510 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 121.8 MPa
@Strain 2.30 %,
Temperature 23.0 °C		17670 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 122.4 MPa
@Strain 1.40 %,
Temperature -40.0 °C		17750 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 124.03 MPa
@Strain 1.40 %,
Temperature -40.0 °C		17989 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 124.8 MPa
@Strain 2.40 %,
Temperature 23.0 °C		18100 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 125.2 MPa
@Strain 1.60 %,
Temperature 23.0 °C		18160 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 126.5 MPa
@Strain 1.60 %,
Temperature 0.000 °C		18350 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 127.3 MPa
@Strain 2.50 %,
Temperature 23.0 °C		18460 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 127.49 MPa
@Strain 1.50 %,
Temperature 0.000 °C		18491 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 129.7 MPa
@Strain 1.50 %,
Temperature -40.0 °C		18810 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 129.8 MPa
@Strain 2.60 %,
Temperature 23.0 °C		18830 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 130.25 MPa
@Strain 1.70 %,
Temperature 23.0 °C		18891 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 131.2 MPa
@Strain 1.50 %,
Temperature -40.0 °C		19030 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 131.9 MPa
@Strain 2.70 %,
Temperature 23.0 °C		19130 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 132 MPa
@Strain 1.70 %,
Temperature 0.000 °C		19100 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 133.56 MPa
@Strain 1.60 %,
Temperature 0.000 °C		19371 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 133.8 MPa
@Strain 2.80 %,
Temperature 23.0 °C		19410 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 134.75 MPa
@Strain 1.80 %,
Temperature 23.0 °C		19544 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 135.7 MPa
@Strain 2.90 %,
Temperature 23.0 °C		19680 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 135.7 MPa
@Strain 1.60 %,
Temperature -40.0 °C		19680 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 137 MPa
@Strain 1.80 %,
Temperature 0.000 °C		19900 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 137.3 MPa
@Strain 3.00 %,
Temperature 23.0 °C		19910 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 137.81 MPa
@Strain 1.60 %,
Temperature -40.0 °C		19988 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 138.5 MPa
@Strain 3.10 %,
Temperature 23.0 °C		20090 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 138.8 MPa
@Strain 1.90 %,
Temperature 23.0 °C		20130 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 139.43 MPa
@Strain 1.70 %,
Temperature 0.000 °C		20223 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 139.6 MPa
@Strain 3.20 %,
Temperature 23.0 °C		20250 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 141.9 MPa
@Strain 1.90 %,
Temperature 0.000 °C		20580 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 142 MPa
@Strain 1.70 %,
Temperature -40.0 °C		20600 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 142.45 MPa
@Strain 2.00 %,
Temperature 23.0 °C		20661 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 143.74 MPa
@Strain 1.70 %,
Temperature -40.0 °C		20848 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 145.19 MPa
@Strain 1.80 %,
Temperature 0.000 °C		21058 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 145.95 MPa
@Strain 2.10 %,
Temperature 23.0 °C		21168 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 146.5 MPa
@Strain 2.00 %,
Temperature 0.000 °C		21250 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 147.6 MPa
@Strain 1.80 %,
Temperature -40.0 °C		21410 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 149.3 MPa
@Strain 2.20 %,
Temperature 23.0 °C		21650 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 149.87 MPa
@Strain 1.80 %,
Temperature -40.0 °C		21737 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 150.7 MPa
@Strain 2.10 %,
Temperature 0.000 °C		21860 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 151.1 MPa
@Strain 1.90 %,
Temperature 0.000 °C		21920 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 152.25 MPa
@Strain 2.30 %,
Temperature 23.0 °C		22082 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 153.8 MPa
@Strain 1.90 %,
Temperature -40.0 °C		22310 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 154.8 MPa
@Strain 2.20 %,
Temperature 0.000 °C		22450 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 154.85 MPa
@Strain 2.40 %,
Temperature 23.0 °C		22459 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 155.99 MPa
@Strain 1.90 %,
Temperature -40.0 °C		22624 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 156.51 MPa
@Strain 2.00 %,
Temperature 0.000 °C		22700 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 157.55 MPa
@Strain 2.50 %,
Temperature 23.0 °C		22851 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 158.6 MPa
@Strain 2.30 %,
Temperature 0.000 °C		23000 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 159.5 MPa
@Strain 2.00 %,
Temperature -40.0 °C		23130 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 160.15 MPa
@Strain 2.60 %,
Temperature 23.0 °C		23228 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 161.25 MPa
@Strain 2.10 %,
Temperature 0.000 °C		23387 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 162.02 MPa
@Strain 2.00 %,
Temperature -40.0 °C		23499 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 162.2 MPa
@Strain 2.40 %,
Temperature 0.000 °C		23530 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 162.75 MPa
@Strain 2.70 %,
Temperature 23.0 °C		23605 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 165.4 MPa
@Strain 2.50 %,
Temperature 0.000 °C		23990 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 165.4 MPa
@Strain 2.80 %,
Temperature 23.0 °C		23990 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 165.8 MPa
@Strain 2.10 %,
Temperature -40.0 °C		24050 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 166.11 MPa
@Strain 2.20 %,
Temperature 0.000 °C		24092 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 167.6 MPa
@Strain 2.90 %,
Temperature 23.0 °C		24310 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 167.76 MPa
@Strain 2.10 %,
Temperature -40.0 °C		24332 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 168.7 MPa
@Strain 2.60 %,
Temperature 0.000 °C		24470 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 169.5 MPa
@Strain 3.00 %,
Temperature 23.0 °C		24580 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 170.46 MPa
@Strain 2.30 %,
Temperature 0.000 °C		24723 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 171.7 MPa
@Strain 2.70 %,
Temperature 0.000 °C		24900 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 172 MPa
@Strain 2.20 %,
Temperature -40.0 °C		24900 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 173.12 MPa
@Strain 2.20 %,
Temperature -40.0 °C		25109 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 174.3 MPa
@Strain 2.80 %,
Temperature 0.000 °C		25280 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 174.51 MPa
@Strain 2.40 %,
Temperature 0.000 °C		25311 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 177.8 MPa
@Strain 2.30 %,
Temperature -40.0 °C		25790 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 178 MPa
@Strain 2.30 %,
Temperature -40.0 °C		25800 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 178.45 MPa
@Strain 2.50 %,
Temperature 0.000 °C		25882 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 181.89 MPa
@Strain 2.60 %,
Temperature 0.000 °C		26381 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 182.79 MPa
@Strain 2.40 %,
Temperature -40.0 °C		26511 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 183.1 MPa
@Strain 2.40 %,
Temperature -40.0 °C		26560 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 184.52 MPa
@Strain 2.70 %,
Temperature 0.000 °C		26762 psi
@Strain 2.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 187.16 MPa
@Strain 2.80 %,
Temperature 0.000 °C		27145 psi
@Strain 2.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 187.67 MPa
@Strain 2.50 %,
Temperature -40.0 °C		27219 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 188.1 MPa
@Strain 2.50 %,
Temperature -40.0 °C		27280 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 191.4 MPa
@Strain 2.60 %,
Temperature -40.0 °C		27760 psi
@Strain 2.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 193.4 MPa
@Strain 2.60 %,
Temperature -40.0 °C		28050 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 194.94 MPa
@Strain 2.70 %,
Temperature -40.0 °C		28274 psi
@Strain 2.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 198.3 MPa
@Strain 2.70 %,
Temperature -40.0 °C		28760 psi
@Strain 2.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 202.9 MPa
@Strain 2.80 %,
Temperature -40.0 °C		29430 psi
@Strain 2.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 207.5 MPa
@Strain 2.90 %,
Temperature -40.0 °C		30100 psi
@Strain 2.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 211.6 MPa
@Strain 3.00 %,
Temperature -40.0 °C		30690 psi
@Strain 3.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 215.9 MPa
@Strain 3.10 %,
Temperature -40.0 °C		31310 psi
@Strain 3.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 219.7 MPa
@Strain 3.20 %,
Temperature -40.0 °C		31860 psi
@Strain 3.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 223.1 MPa
@Strain 3.30 %,
Temperature -40.0 °C		32360 psi
@Strain 3.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 225.8 MPa
@Strain 3.40 %,
Temperature -40.0 °C		32750 psi
@Strain 3.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		DAM; ISO 527
 3.2 %
@Temperature 23.0 °C		3.2 %
@Temperature 73.4 °F		50%RH; ISO 527
 4.0 %
@Temperature 23.0 °C		4.0 %
@Temperature 73.4 °F		50%RH; ASTM D638
Tensile Modulus  7.90 GPa
@Temperature 23.0 °C		1150 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 9.50 GPa
@Temperature 23.0 °C		1380 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Strength 255 MPa
@Temperature 23.0 °C		37000 psi
@Temperature 73.4 °F		DAM; ASTM D790
Flexural Modulus  6.20 GPa
@Temperature 23.0 °C		899 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 7.00 GPa
@Temperature 23.0 °C		1020 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 8.20 GPa
@Temperature 23.0 °C		1190 ksi
@Temperature 73.4 °F		DAM; ISO 178
 8.27 GPa
@Temperature 23.0 °C		1200 ksi
@Temperature 73.4 °F		DAM; ASTM D790
Shear Strength 76.0 MPa
@Temperature 23.0 °C		11000 psi
@Temperature 73.4 °F		DAM; ASTM D732
Izod Impact, Notched  1.28 J/cm
@Temperature 23.0 °C		2.40 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 1.33 J/cm
@Temperature 23.0 °C		2.49 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Notched (ISO)  10.0 kJ/m²
@Temperature -40.0 °C		4.76 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 180/1A
 10.0 kJ/m²
@Temperature -30.0 °C		4.76 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 11.0 kJ/m²
@Temperature -40.0 °C		5.23 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 11.0 kJ/m²
@Temperature -30.0 °C		5.23 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 12.0 kJ/m²
@Temperature 23.0 °C		5.71 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
 13.0 kJ/m²
@Temperature 23.0 °C		6.19 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)  45.0 kJ/m²
@Temperature -30.0 °C		21.4 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1U
 60.0 kJ/m²
@Temperature -30.0 °C		28.6 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 60.0 kJ/m²
@Temperature 23.0 °C		28.6 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1U
 70.0 kJ/m²
@Temperature 23.0 °C		33.3 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
Charpy Impact Unnotched  6.00 J/cm²
@Temperature -30.0 °C		28.6 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 6.50 J/cm²
@Temperature -30.0 °C		30.9 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 8.00 J/cm²
@Temperature 23.0 °C		38.1 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 9.00 J/cm²
@Temperature 23.0 °C		42.8 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  1.00 J/cm²
@Temperature -30.0 °C		4.76 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 1.00 J/cm²
@Temperature -40.0 °C		4.76 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 179/1eA
 1.10 J/cm²
@Temperature -30.0 °C		5.23 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 1.20 J/cm²
@Temperature 23.0 °C		5.71 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 1.20 J/cm²
@Temperature -40.0 °C		5.71 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 1.30 J/cm²
@Temperature 23.0 °C		6.19 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+12 ohm-cm
@Temperature 23.0 °C		1.00e+12 ohm-cm
@Temperature 73.4 °F		50%RH; ASTM D257
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; ASTM D257
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Surface Resistance 1.00e+15 ohm
@Temperature 23.0 °C		1.00e+15 ohm
@Temperature 73.4 °F		DAM; ASTM D257
Dielectric Constant  3.4
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.4
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 3.7
@Frequency 1000 Hz,
Temperature 23.0 °C		3.7
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
Dielectric Strength 20.5 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		521 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		DAM; Short Time; ASTM D149
Dissipation Factor  0.020
@Frequency 1000 Hz,
Temperature 23.0 °C		0.020
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
Comparative Tracking Index  >= 550 V
@Temperature 23.0 °C		>= 550 V
@Temperature 73.4 °F		DAM; UL 746A
 600 V
@Temperature 23.0 °C		600 V
@Temperature 73.4 °F		DAM; IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  83.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		46.1 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 83.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		46.1 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 113 µm/m-°C
@Temperature 23.0 - 55.0 °C		62.8 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 113 µm/m-°C
@Temperature 23.0 - 55.0 °C		62.8 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 158 µm/m-°C
@Temperature 55.0 - 160 °C		87.8 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
 158 µm/m-°C
@Temperature 55.0 - 160 °C		87.8 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
Melting Point 217 °C423 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 216 °C421 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C392 °FDAM; ISO 75-1/-2
 210 °C410 °FDAM; ASTM D648
Glass Transition Temp, Tg 70.0 °C158 °F10°C/min; DAM; ISO 11357-1/-2
UL RTI, Electrical  65.0 °C
@Thickness 0.750 mm		149 °F
@Thickness 0.0295 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 0.750 mm		149 °F
@Thickness 0.0295 in		DAM; UL 746B
 65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical without Impact  65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 0.750 mm		149 °F
@Thickness 0.0295 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		DAM; UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
 
Processing PropertiesMetricEnglishComments
Melt Temperature 218 °C424 °F10°C/min; DAM; ISO 11357-1/-3
 290 °C554 °FDAM; Optimum
 280 - 300 °C536 - 572 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.15 %<= 0.15 %DAM
 
Descriptive Properties
AdditiveHeat StabilizerDAM
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesDimensional Stability, GoodDAM
 Heat StabilizedDAM
 Moisture Absorption, LowDAM
FillerGlass fiber reinforcementDAM
FormsPelletsDAM
GenericNylon 612DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA612-GF33<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA612DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass Reinforced ResinsDAM
Resin IdentificationPA612-GF33ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 Electrical/Electronic ApplicationsDAM
 Industrial ApplicationsDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47490.html

免责声明: 本文 DuPont Performance Polymers Zytel® 77G33HS1L NC010 Nylon 612 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4