- 吸水率 [%]: 0.4
- 缺口冲击强度: 1.17
- 拉伸强度 [MPa]: 128.0
- 弯曲模量 [MPa]: 5.86
- 热变形温度 [℃]: 213.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.315 g/cc | 1.315 g/cc | ASTM D792 |
| Water Absorption | 0.40 % @Thickness 3.17 mm | 0.40 % @Thickness 0.125 in | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 128 MPa | 18500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 5.86 GPa | 850 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 172 MPa | 25000 psi | ASTM D790 |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 2.20 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1000 ohm-cm | 1000 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1000 ohm | 1000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Unannealed, 0.125 in bars; ASTM D648 |