- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 0.14
- 缺口冲击强度: 1.34
- 拉伸强度 [MPa]: 183.0
- 弯曲模量 [MPa]: 10.0
- 硬度: 116.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Water Absorption | 0.14 % | 0.14 % | 24 hrs; ASTM D570 |
| Water Absorption at Saturation | 2.0 % | 2.0 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength, Yield | 183 MPa | 26500 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 |
| Izod Impact, Notched | 1.34 J/cm | 2.51 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 212 °C | 414 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | ASTM D648 |