- 密度 [g/cm3]: 1.42
- 缺口冲击强度: 12.0
- 拉伸强度 [MPa]: 148.0
- 断裂伸长率 [%]: 200
- 弯曲模量 [MPa]: 7.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 147 MPa | 21300 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 148 MPa | 21500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.4 % | 3.4 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.3 % | 3.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 198 MPa | 28700 psi | break, 2 mm/min; ISO 178 |
| Flexural Yield Strength | 200 MPa | 29000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.30 GPa | 1060 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.55 | 0.55 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.50 | 0.50 | ASTM D3702 Modified |
| K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 28.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 15.6 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 101 µm/m-°C @Temperature 23.0 - 60.0 °C | 56.1 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |