  4. DuPont Performance Polymers Zytel® RS LC3090 NC010 Nylon 610

DuPont Performance Polymers Zytel® RS LC3090 NC010 Nylon 610

DuPont Performance Polymers Zytel® RS LC3090 NC010 Nylon 610 物性表: DuPont Performance Polymers Zytel® RS LC3090 NC010 Nylon 610物性表及特性介绍,DuPont Performance Polymers Zytel® RS LC3090 NC010 Nylon 610注塑参数详情,如需DuPont Performance Polymers Zytel® RS LC3090 NC010 Nylon 610下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.08
  • 吸水率 [%]: 0.58
  • 拉伸强度 [MPa]: 47.0
  • 弯曲模量 [MPa]: 1.90
  • 热变形温度 [℃]: 151.0
 
Physical PropertiesMetricEnglishComments
Density 1.08 g/cc0.0390 lb/in³DAM; ISO 1183
Water Absorption 0.58 %
@Temperature 23.0 °C		0.58 %
@Temperature 73.4 °F		Immersion 24h; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.012 cm/cm
@Thickness 2.00 mm		0.012 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.012 cm/cm
@Thickness 2.00 mm		0.012 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Stress  0.0300 MPa
@Strain 0.000 %,
Temperature 60.0 °C		4.35 psi
@Strain 0.000 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 0.0600 MPa
@Strain 0.000 %,
Temperature 40.0 °C		8.70 psi
@Strain 0.000 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 0.0700 MPa
@Strain 0.000 %,
Temperature 60.0 °C		10.2 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 0.0700 MPa
@Strain 0.000 %,
Temperature 90.0 °C		10.2 psi
@Strain 0.000 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 0.0900 MPa
@Strain 0.000 %,
Temperature 150 °C		13.1 psi
@Strain 0.000 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 0.0900 MPa
@Strain 0.000 %,
Temperature 120 °C		13.1 psi
@Strain 0.000 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 0.0900 MPa
@Strain 0.000 %,
Temperature 120 °C		13.1 psi
@Strain 0.000 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 0.100 MPa
@Strain 0.000 %,
Temperature 150 °C		14.5 psi
@Strain 0.000 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.100 MPa
@Strain 0.000 %,
Temperature 90.0 °C		14.5 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 0.200 MPa
@Strain 0.000 %,
Temperature 40.0 °C		29.0 psi
@Strain 0.000 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 0.220 MPa
@Strain 0.000 %,
Temperature 23.0 °C		31.9 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 0.330 MPa
@Strain 0.000 %,
Temperature 0.000 °C		47.9 psi
@Strain 0.000 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 0.340 MPa
@Strain 0.000 %,
Temperature -40.0 °C		49.3 psi
@Strain 0.000 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 0.360 MPa
@Strain 0.000 %,
Temperature -20.0 °C		52.2 psi
@Strain 0.000 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 0.410 MPa
@Strain 0.000 %,
Temperature -20.0 °C		59.5 psi
@Strain 0.000 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 0.410 MPa
@Strain 0.000 %,
Temperature -40.0 °C		59.5 psi
@Strain 0.000 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 0.450 MPa
@Strain 0.000 %,
Temperature 0.000 °C		65.3 psi
@Strain 0.000 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 0.460 MPa
@Strain 0.000 %,
Temperature 23.0 °C		66.7 psi
@Strain 0.000 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 0.500 MPa
@Strain 0.0300 %,
Temperature -40.0 °C		72.5 psi
@Strain 0.0300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 0.520 MPa
@Strain 0.0900 %,
Temperature 60.0 °C		75.4 psi
@Strain 0.0900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 0.620 MPa
@Strain 0.0200 %,
Temperature -40.0 °C		89.9 psi
@Strain 0.0200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 0.790 MPa
@Strain 0.110 %,
Temperature 40.0 °C		115 psi
@Strain 0.110 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 0.980 MPa
@Strain 0.180 %,
Temperature 60.0 °C		142 psi
@Strain 0.180 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 1.02 MPa
@Strain 0.0600 %,
Temperature -40.0 °C		148 psi
@Strain 0.0600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 1.15 MPa
@Strain 0.0500 %,
Temperature -40.0 °C		167 psi
@Strain 0.0500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 1.16 MPa
@Strain 0.0400 %,
Temperature -20.0 °C		168 psi
@Strain 0.0400 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 1.21 MPa
@Strain 0.0100 %,
Temperature -40.0 °C		175 psi
@Strain 0.0100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 1.32 MPa
@Strain 0.0800 %,
Temperature 23.0 °C		191 psi
@Strain 0.0800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 1.37 MPa
@Strain 0.100 %,
Temperature 40.0 °C		199 psi
@Strain 0.100 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 1.46 MPa
@Strain 0.200 %,
Temperature 40.0 °C		212 psi
@Strain 0.200 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 1.51 MPa
@Strain 0.0500 %,
Temperature -20.0 °C		219 psi
@Strain 0.0500 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 1.55 MPa
@Strain 0.0900 %,
Temperature -40.0 °C		225 psi
@Strain 0.0900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 1.81 MPa
@Strain 0.0600 %,
Temperature 0.000 °C		263 psi
@Strain 0.0600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 1.96 MPa
@Strain 0.0800 %,
Temperature -40.0 °C		284 psi
@Strain 0.0800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 1.98 MPa
@Strain 0.0700 %,
Temperature 23.0 °C		287 psi
@Strain 0.0700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 2.04 MPa
@Strain 0.0700 %,
Temperature -20.0 °C		296 psi
@Strain 0.0700 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 2.05 MPa
@Strain 0.110 %,
Temperature -40.0 °C		297 psi
@Strain 0.110 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 2.06 MPa
@Strain 0.0700 %,
Temperature 0.000 °C		299 psi
@Strain 0.0700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 2.38 MPa
@Strain 0.160 %,
Temperature 23.0 °C		345 psi
@Strain 0.160 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 2.52 MPa
@Strain 0.180 %,
Temperature 40.0 °C		365 psi
@Strain 0.180 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 2.56 MPa
@Strain 0.130 %,
Temperature -40.0 °C		371 psi
@Strain 0.130 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 2.68 MPa
@Strain 0.100 %,
Temperature -20.0 °C		389 psi
@Strain 0.100 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 2.78 MPa
@Strain 0.130 %,
Temperature -40.0 °C		403 psi
@Strain 0.130 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 2.84 MPa
@Strain 0.110 %,
Temperature -20.0 °C		412 psi
@Strain 0.110 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 2.87 MPa
@Strain 0.720 %,
Temperature 90.0 °C		416 psi
@Strain 0.720 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 2.91 MPa
@Strain 1.12 %,
Temperature 150 °C		422 psi
@Strain 1.12 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 3.09 MPa
@Strain 0.150 %,
Temperature -40.0 °C		448 psi
@Strain 0.150 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 3.15 MPa
@Strain 0.120 %,
Temperature 0.000 °C		457 psi
@Strain 0.120 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 3.42 MPa
@Strain 0.240 %,
Temperature 23.0 °C		496 psi
@Strain 0.240 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 3.52 MPa
@Strain 0.150 %,
Temperature 23.0 °C		511 psi
@Strain 0.150 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 3.62 MPa
@Strain 0.170 %,
Temperature -40.0 °C		525 psi
@Strain 0.170 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 3.62 MPa
@Strain 0.160 %,
Temperature -40.0 °C		525 psi
@Strain 0.160 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 3.66 MPa
@Strain 0.140 %,
Temperature 0.000 °C		531 psi
@Strain 0.140 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 3.73 MPa
@Strain 0.140 %,
Temperature -20.0 °C		541 psi
@Strain 0.140 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 3.86 MPa
@Strain 0.140 %,
Temperature -20.0 °C		560 psi
@Strain 0.140 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 4.10 MPa
@Strain 0.190 %,
Temperature -40.0 °C		595 psi
@Strain 0.190 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 4.38 MPa
@Strain 0.180 %,
Temperature -40.0 °C		635 psi
@Strain 0.180 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 4.48 MPa
@Strain 0.170 %,
Temperature -20.0 °C		650 psi
@Strain 0.170 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 4.49 MPa
@Strain 0.180 %,
Temperature 0.000 °C		651 psi
@Strain 0.180 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 4.63 MPa
@Strain 0.220 %,
Temperature -40.0 °C		672 psi
@Strain 0.220 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 4.83 MPa
@Strain 0.850 %,
Temperature 60.0 °C		701 psi
@Strain 0.850 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 4.88 MPa
@Strain 0.180 %,
Temperature -20.0 °C		708 psi
@Strain 0.180 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 5.02 MPa
@Strain 0.220 %,
Temperature 23.0 °C		728 psi
@Strain 0.220 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 5.11 MPa
@Strain 0.230 %,
Temperature -40.0 °C		741 psi
@Strain 0.230 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 5.15 MPa
@Strain 0.200 %,
Temperature -40.0 °C		747 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 5.20 MPa
@Strain 0.200 %,
Temperature -20.0 °C		754 psi
@Strain 0.200 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 5.21 MPa
@Strain 0.200 %,
Temperature 0.000 °C		756 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 5.82 MPa
@Strain 0.230 %,
Temperature -20.0 °C		844 psi
@Strain 0.230 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 5.85 MPa
@Strain 0.240 %,
Temperature 0.000 °C		848 psi
@Strain 0.240 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 5.87 MPa
@Strain 0.230 %,
Temperature -40.0 °C		851 psi
@Strain 0.230 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 6.00 MPa
@Strain 0.230 %,
Temperature -20.0 °C		870 psi
@Strain 0.230 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 6.79 MPa
@Strain 0.420 %,
Temperature 40.0 °C		985 psi
@Strain 0.420 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 6.82 MPa
@Strain 0.250 %,
Temperature 0.000 °C		989 psi
@Strain 0.250 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 7.32 MPa
@Strain 2.81 %,
Temperature 120 °C		1060 psi
@Strain 2.81 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.64 MPa
@Strain 4.83 %,
Temperature 150 °C		1110 psi
@Strain 4.83 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.66 MPa
@Strain 0.340 %,
Temperature -40.0 °C		1110 psi
@Strain 0.340 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 8.73 MPa
@Strain 2.34 %,
Temperature 90.0 °C		1270 psi
@Strain 2.34 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 11.24 MPa
@Strain 1.36 %,
Temperature 40.0 °C		1630 psi
@Strain 1.36 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 11.29 MPa
@Strain 4.42 %,
Temperature 120 °C		1637 psi
@Strain 4.42 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.67 MPa
@Strain 19.61 %,
Temperature 150 °C		1838 psi
@Strain 19.61 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.66 MPa
@Strain 15.4 %,
Temperature 150 °C		1981 psi
@Strain 15.4 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.9 MPa
@Strain 35.77 %,
Temperature 150 °C		2020 psi
@Strain 35.77 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.22 MPa
@Strain 74.79 %,
Temperature 150 °C		2062 psi
@Strain 74.79 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.32 MPa
@Strain 53.66 %,
Temperature 150 °C		2077 psi
@Strain 53.66 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.5 MPa
@Strain 97.79 %,
Temperature 150 °C		2100 psi
@Strain 97.79 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.71 MPa
@Strain 120.22 %,
Temperature 150 °C		2134 psi
@Strain 120.22 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.82 MPa
@Strain 0.560 %,
Temperature -20.0 °C		2149 psi
@Strain 0.560 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 14.91 MPa
@Strain 140.41 %,
Temperature 150 °C		2163 psi
@Strain 140.41 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.03 MPa
@Strain 151.24 %,
Temperature 150 °C		2180 psi
@Strain 151.24 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.09 MPa
@Strain 155.64 %,
Temperature 150 °C		2189 psi
@Strain 155.64 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.41 MPa
@Strain 31.09 %,
Temperature 150 °C		2235 psi
@Strain 31.09 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.56 MPa
@Strain 159.24 %,
Temperature 150 °C		2257 psi
@Strain 159.24 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.03 MPa
@Strain 48.0 %,
Temperature 150 °C		2325 psi
@Strain 48.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.07 MPa
@Strain 4.08 %,
Temperature 60.0 °C		2331 psi
@Strain 4.08 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.16 MPa
@Strain 162.13 %,
Temperature 150 °C		2344 psi
@Strain 162.13 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.21 MPa
@Strain 66.5 %,
Temperature 150 °C		2351 psi
@Strain 66.5 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.28 MPa
@Strain 86.91 %,
Temperature 150 °C		2361 psi
@Strain 86.91 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.48 MPa
@Strain 108.08 %,
Temperature 150 °C		2390 psi
@Strain 108.08 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.56 MPa
@Strain 16.72 %,
Temperature 120 °C		2402 psi
@Strain 16.72 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.75 MPa
@Strain 127.64 %,
Temperature 150 °C		2429 psi
@Strain 127.64 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.01 MPa
@Strain 143.1 %,
Temperature 150 °C		2467 psi
@Strain 143.1 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.35 MPa
@Strain 153.75 %,
Temperature 150 °C		2516 psi
@Strain 153.75 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.51 MPa
@Strain 167.77 %,
Temperature 150 °C		2540 psi
@Strain 167.77 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.63 MPa
@Strain 160.48 %,
Temperature 150 °C		2557 psi
@Strain 160.48 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.03 MPa
@Strain 165.47 %,
Temperature 150 °C		2615 psi
@Strain 165.47 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.36 MPa
@Strain 32.34 %,
Temperature 120 °C		2663 psi
@Strain 32.34 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.67 MPa
@Strain 179.08 %,
Temperature 150 °C		2708 psi
@Strain 179.08 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.75 MPa
@Strain 18.38 %,
Temperature 120 °C		2719 psi
@Strain 18.38 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.92 MPa
@Strain 49.29 %,
Temperature 120 °C		2744 psi
@Strain 49.29 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.0 MPa
@Strain 68.28 %,
Temperature 120 °C		2760 psi
@Strain 68.28 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.03 MPa
@Strain 89.58 %,
Temperature 120 °C		2760 psi
@Strain 89.58 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.15 MPa
@Strain 0.760 %,
Temperature -40.0 °C		2777 psi
@Strain 0.760 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 19.28 MPa
@Strain 171.78 %,
Temperature 150 °C		2796 psi
@Strain 171.78 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.38 MPa
@Strain 111.08 %,
Temperature 120 °C		2811 psi
@Strain 111.08 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.53 MPa
@Strain 193.77 %,
Temperature 150 °C		2833 psi
@Strain 193.77 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.65 MPa
@Strain 130.59 %,
Temperature 120 °C		2850 psi
@Strain 130.59 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.81 MPa
@Strain 13.57 %,
Temperature 90.0 °C		2873 psi
@Strain 13.57 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 19.92 MPa
@Strain 146.76 %,
Temperature 120 °C		2889 psi
@Strain 146.76 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.16 MPa
@Strain 158.86 %,
Temperature 120 °C		2924 psi
@Strain 158.86 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.26 MPa
@Strain 34.15 %,
Temperature 120 °C		2938 psi
@Strain 34.15 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.31 MPa
@Strain 181.42 %,
Temperature 150 °C		2946 psi
@Strain 181.42 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.44 MPa
@Strain 209.25 %,
Temperature 150 °C		2965 psi
@Strain 209.25 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.45 MPa
@Strain 165.43 %,
Temperature 120 °C		2966 psi
@Strain 165.43 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.74 MPa
@Strain 51.1 %,
Temperature 120 °C		3008 psi
@Strain 51.1 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.78 MPa
@Strain 168.96 %,
Temperature 120 °C		3014 psi
@Strain 168.96 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.86 MPa
@Strain 69.53 %,
Temperature 120 °C		3025 psi
@Strain 69.53 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.93 MPa
@Strain 89.3 %,
Temperature 120 °C		3036 psi
@Strain 89.3 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.08 MPa
@Strain 195.61 %,
Temperature 150 °C		3057 psi
@Strain 195.61 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.18 MPa
@Strain 109.3 %,
Temperature 120 °C		3072 psi
@Strain 109.3 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.35 MPa
@Strain 222.8 %,
Temperature 150 °C		3097 psi
@Strain 222.8 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.49 MPa
@Strain 7.55 %,
Temperature 60.0 °C		3117 psi
@Strain 7.55 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.58 MPa
@Strain 127.93 %,
Temperature 120 °C		3130 psi
@Strain 127.93 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.89 MPa
@Strain 143.39 %,
Temperature 120 °C		3175 psi
@Strain 143.39 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.96 MPa
@Strain 211.7 %,
Temperature 150 °C		3185 psi
@Strain 211.7 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.22 MPa
@Strain 173.45 %,
Temperature 120 °C		3223 psi
@Strain 173.45 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.22 MPa
@Strain 155.42 %,
Temperature 120 °C		3223 psi
@Strain 155.42 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.37 MPa
@Strain 233.96 %,
Temperature 150 °C		3245 psi
@Strain 233.96 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.46 MPa
@Strain 28.79 %,
Temperature 90.0 °C		3258 psi
@Strain 28.79 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 22.57 MPa
@Strain 163.93 %,
Temperature 120 °C		3274 psi
@Strain 163.93 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.62 MPa
@Strain 15.36 %,
Temperature 90.0 °C		3281 psi
@Strain 15.36 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 22.95 MPa
@Strain 0.930 %,
Temperature -20.0 °C		3329 psi
@Strain 0.930 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 22.96 MPa
@Strain 226.76 %,
Temperature 150 °C		3330 psi
@Strain 226.76 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.03 MPa
@Strain 170.05 %,
Temperature 120 °C		3340 psi
@Strain 170.05 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.07 MPa
@Strain 45.7 %,
Temperature 90.0 °C		3346 psi
@Strain 45.7 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.18 MPa
@Strain 64.6 %,
Temperature 90.0 °C		3362 psi
@Strain 64.6 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.26 MPa
@Strain 85.33 %,
Temperature 90.0 °C		3374 psi
@Strain 85.33 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.35 MPa
@Strain 4.27 %,
Temperature 40.0 °C		3387 psi
@Strain 4.27 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 23.42 MPa
@Strain 244.24 %,
Temperature 150 °C		3397 psi
@Strain 244.24 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.59 MPa
@Strain 106.23 %,
Temperature 90.0 °C		3421 psi
@Strain 106.23 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.62 MPa
@Strain 181.4 %,
Temperature 120 °C		3426 psi
@Strain 181.4 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.93 MPa
@Strain 238.87 %,
Temperature 150 °C		3471 psi
@Strain 238.87 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.96 MPa
@Strain 125.44 %,
Temperature 90.0 °C		3475 psi
@Strain 125.44 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 24.13 MPa
@Strain 175.88 %,
Temperature 120 °C		3500 psi
@Strain 175.88 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.31 MPa
@Strain 141.59 %,
Temperature 90.0 °C		3526 psi
@Strain 141.59 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 24.42 MPa
@Strain 194.77 %,
Temperature 120 °C		3542 psi
@Strain 194.77 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.46 MPa
@Strain 254.22 %,
Temperature 150 °C		3548 psi
@Strain 254.22 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 24.53 MPa
@Strain 11.23 %,
Temperature 60.0 °C		3558 psi
@Strain 11.23 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 24.65 MPa
@Strain 153.4 %,
Temperature 90.0 °C		3575 psi
@Strain 153.4 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 24.99 MPa
@Strain 249.42 %,
Temperature 150 °C		3624 psi
@Strain 249.42 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.03 MPa
@Strain 160.71 %,
Temperature 90.0 °C		3630 psi
@Strain 160.71 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 25.11 MPa
@Strain 30.67 %,
Temperature 90.0 °C		3642 psi
@Strain 30.67 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 25.11 MPa
@Strain 1.17 %,
Temperature 23.0 °C		3642 psi
@Strain 1.17 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 25.32 MPa
@Strain 211.15 %,
Temperature 120 °C		3672 psi
@Strain 211.15 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.43 MPa
@Strain 184.18 %,
Temperature 120 °C		3688 psi
@Strain 184.18 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.46 MPa
@Strain 263.78 %,
Temperature 150 °C		3693 psi
@Strain 263.78 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 25.48 MPa
@Strain 165.5 %,
Temperature 90.0 °C		3696 psi
@Strain 165.5 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 25.82 MPa
@Strain 47.28 %,
Temperature 90.0 °C		3745 psi
@Strain 47.28 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 26.09 MPa
@Strain 64.98 %,
Temperature 90.0 °C		3784 psi
@Strain 64.98 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 26.1 MPa
@Strain 259.54 %,
Temperature 150 °C		3790 psi
@Strain 259.54 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.25 MPa
@Strain 289.42 %,
Temperature 150 °C		3807 psi
@Strain 289.42 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 26.31 MPa
@Strain 15.11 %,
Temperature 60.0 °C		3816 psi
@Strain 15.11 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 26.33 MPa
@Strain 83.5 %,
Temperature 90.0 °C		3819 psi
@Strain 83.5 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 26.38 MPa
@Strain 196.7 %,
Temperature 120 °C		3826 psi
@Strain 196.7 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.44 MPa
@Strain 227.21 %,
Temperature 120 °C		3835 psi
@Strain 227.21 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.49 MPa
@Strain 273.35 %,
Temperature 150 °C		3842 psi
@Strain 273.35 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 26.66 MPa
@Strain 102.17 %,
Temperature 90.0 °C		3867 psi
@Strain 102.17 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 26.86 MPa
@Strain 1.18 %,
Temperature -40.0 °C		3896 psi
@Strain 1.18 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 26.87 MPa
@Strain 170.68 %,
Temperature 90.0 °C		3897 psi
@Strain 170.68 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 27.07 MPa
@Strain 120 %,
Temperature 90.0 °C		3926 psi
@Strain 120 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 27.22 MPa
@Strain 269.68 %,
Temperature 150 °C		3948 psi
@Strain 269.68 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.28 MPa
@Strain 212.26 %,
Temperature 120 °C		3957 psi
@Strain 212.26 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.31 MPa
@Strain 2.04 %,
Temperature 23.0 °C		3961 psi
@Strain 2.04 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.39 MPa
@Strain 19.15 %,
Temperature 60.0 °C		3973 psi
@Strain 19.15 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.49 MPa
@Strain 282.43 %,
Temperature 150 °C		3987 psi
@Strain 282.43 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 27.56 MPa
@Strain 136.01 %,
Temperature 90.0 °C		3997 psi
@Strain 136.01 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 28.02 MPa
@Strain 9.91 %,
Temperature 60.0 °C		4064 psi
@Strain 9.91 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 28.05 MPa
@Strain 23.33 %,
Temperature 60.0 °C		4068 psi
@Strain 23.33 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.07 MPa
@Strain 149.23 %,
Temperature 90.0 °C		4071 psi
@Strain 149.23 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 28.35 MPa
@Strain 179 %,
Temperature 90.0 °C		4112 psi
@Strain 179 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 28.36 MPa
@Strain 279.55 %,
Temperature 150 °C		4113 psi
@Strain 279.55 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.44 MPa
@Strain 228.07 %,
Temperature 120 °C		4125 psi
@Strain 228.07 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.45 MPa
@Strain 27.7 %,
Temperature 60.0 °C		4126 psi
@Strain 27.7 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.56 MPa
@Strain 159.66 %,
Temperature 90.0 °C		4142 psi
@Strain 159.66 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 28.57 MPa
@Strain 250.88 %,
Temperature 120 °C		4144 psi
@Strain 250.88 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.68 MPa
@Strain 32.19 %,
Temperature 60.0 °C		4160 psi
@Strain 32.19 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.8 MPa
@Strain 36.82 %,
Temperature 60.0 °C		4180 psi
@Strain 36.82 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.86 MPa
@Strain 67.07 %,
Temperature 60.0 °C		4186 psi
@Strain 67.07 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.87 MPa
@Strain 41.54 %,
Temperature 60.0 °C		4187 psi
@Strain 41.54 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.87 MPa
@Strain 61.74 %,
Temperature 60.0 °C		4187 psi
@Strain 61.74 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.87 MPa
@Strain 72.48 %,
Temperature 60.0 °C		4187 psi
@Strain 72.48 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.88 MPa
@Strain 56.51 %,
Temperature 60.0 °C		4189 psi
@Strain 56.51 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.89 MPa
@Strain 46.41 %,
Temperature 60.0 °C		4190 psi
@Strain 46.41 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.89 MPa
@Strain 51.42 %,
Temperature 60.0 °C		4190 psi
@Strain 51.42 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.9 MPa
@Strain 77.94 %,
Temperature 60.0 °C		4190 psi
@Strain 77.94 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.93 MPa
@Strain 83.46 %,
Temperature 60.0 °C		4196 psi
@Strain 83.46 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.98 MPa
@Strain 89.0 %,
Temperature 60.0 °C		4203 psi
@Strain 89.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.01 MPa
@Strain 7.58 %,
Temperature 40.0 °C		4208 psi
@Strain 7.58 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 29.09 MPa
@Strain 94.56 %,
Temperature 60.0 °C		4219 psi
@Strain 94.56 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.19 MPa
@Strain 100.03 %,
Temperature 60.0 °C		4234 psi
@Strain 100.03 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.22 MPa
@Strain 167.94 %,
Temperature 90.0 °C		4238 psi
@Strain 167.94 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 29.22 MPa
@Strain 297.02 %,
Temperature 150 °C		4238 psi
@Strain 297.02 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.25 MPa
@Strain 192.14 %,
Temperature 90.0 °C		4242 psi
@Strain 192.14 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 29.54 MPa
@Strain 288.97 %,
Temperature 150 °C		4284 psi
@Strain 288.97 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.57 MPa
@Strain 241.83 %,
Temperature 120 °C		4289 psi
@Strain 241.83 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.85 MPa
@Strain 260.89 %,
Temperature 120 °C		4329 psi
@Strain 260.89 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 30.08 MPa
@Strain 175.17 %,
Temperature 90.0 °C		4363 psi
@Strain 175.17 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 30.25 MPa
@Strain 208.44 %,
Temperature 90.0 °C		4387 psi
@Strain 208.44 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 30.74 MPa
@Strain 253.08 %,
Temperature 120 °C		4458 psi
@Strain 253.08 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.06 MPa
@Strain 270.86 %,
Temperature 120 °C		4505 psi
@Strain 270.86 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 31.43 MPa
@Strain 183.29 %,
Temperature 90.0 °C		4559 psi
@Strain 183.29 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 31.53 MPa
@Strain 224.82 %,
Temperature 90.0 °C		4573 psi
@Strain 224.82 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 32.08 MPa
@Strain 263.03 %,
Temperature 120 °C		4653 psi
@Strain 263.03 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.25 MPa
@Strain 298.44 %,
Temperature 120 °C		4677 psi
@Strain 298.44 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.29 MPa
@Strain 280.79 %,
Temperature 120 °C		4683 psi
@Strain 280.79 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.38 MPa
@Strain 11.02 %,
Temperature 40.0 °C		4696 psi
@Strain 11.02 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 32.71 MPa
@Strain 194.32 %,
Temperature 90.0 °C		4744 psi
@Strain 194.32 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 32.73 MPa
@Strain 238.67 %,
Temperature 90.0 °C		4747 psi
@Strain 238.67 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 33.45 MPa
@Strain 272.65 %,
Temperature 120 °C		4852 psi
@Strain 272.65 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 33.58 MPa
@Strain 290.42 %,
Temperature 120 °C		4870 psi
@Strain 290.42 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 33.67 MPa
@Strain 208.77 %,
Temperature 90.0 °C		4883 psi
@Strain 208.77 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 34.01 MPa
@Strain 249.49 %,
Temperature 90.0 °C		4933 psi
@Strain 249.49 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 34.31 MPa
@Strain 32.7 %,
Temperature 60.0 °C		4976 psi
@Strain 32.7 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.4 MPa
@Strain 14.65 %,
Temperature 40.0 °C		4990 psi
@Strain 14.65 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 34.79 MPa
@Strain 299.81 %,
Temperature 120 °C		5046 psi
@Strain 299.81 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.8 MPa
@Strain 282.18 %,
Temperature 120 °C		5050 psi
@Strain 282.18 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.89 MPa
@Strain 224.91 %,
Temperature 90.0 °C		5060 psi
@Strain 224.91 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 35.04 MPa
@Strain 88.17 %,
Temperature 40.0 °C		5082 psi
@Strain 88.17 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.05 MPa
@Strain 94.08 %,
Temperature 40.0 °C		5084 psi
@Strain 94.08 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.11 MPa
@Strain 58.35 %,
Temperature 60.0 °C		5092 psi
@Strain 58.35 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.12 MPa
@Strain 82.32 %,
Temperature 40.0 °C		5094 psi
@Strain 82.32 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.16 MPa
@Strain 100.03 %,
Temperature 40.0 °C		5100 psi
@Strain 100.03 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.18 MPa
@Strain 76.56 %,
Temperature 40.0 °C		5102 psi
@Strain 76.56 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.25 MPa
@Strain 86.62 %,
Temperature 60.0 °C		5113 psi
@Strain 86.62 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.27 MPa
@Strain 2.72 %,
Temperature 40.0 °C		5115 psi
@Strain 2.72 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 35.28 MPa
@Strain 70.92 %,
Temperature 40.0 °C		5117 psi
@Strain 70.92 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.43 MPa
@Strain 65.38 %,
Temperature 40.0 °C		5139 psi
@Strain 65.38 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.48 MPa
@Strain 259.18 %,
Temperature 90.0 °C		5146 psi
@Strain 259.18 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 35.51 MPa
@Strain 18.44 %,
Temperature 40.0 °C		5150 psi
@Strain 18.44 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.59 MPa
@Strain 60.0 %,
Temperature 40.0 °C		5162 psi
@Strain 60.0 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.59 MPa
@Strain 117.56 %,
Temperature 60.0 °C		5162 psi
@Strain 117.56 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.72 MPa
@Strain 54.73 %,
Temperature 40.0 °C		5181 psi
@Strain 54.73 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.87 MPa
@Strain 1.60 %,
Temperature 0.000 °C		5203 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 35.89 MPa
@Strain 49.63 %,
Temperature 40.0 °C		5205 psi
@Strain 49.63 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.06 MPa
@Strain 44.72 %,
Temperature 40.0 °C		5230 psi
@Strain 44.72 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.08 MPa
@Strain 22.41 %,
Temperature 40.0 °C		5233 psi
@Strain 22.41 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.2 MPa
@Strain 39.95 %,
Temperature 40.0 °C		5250 psi
@Strain 39.95 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.22 MPa
@Strain 291.52 %,
Temperature 120 °C		5253 psi
@Strain 291.52 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.31 MPa
@Strain 35.32 %,
Temperature 40.0 °C		5266 psi
@Strain 35.32 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.31 MPa
@Strain 240.37 %,
Temperature 90.0 °C		5266 psi
@Strain 240.37 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 36.32 MPa
@Strain 26.58 %,
Temperature 40.0 °C		5268 psi
@Strain 26.58 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.37 MPa
@Strain 30.88 %,
Temperature 40.0 °C		5275 psi
@Strain 30.88 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.53 MPa
@Strain 147.51 %,
Temperature 60.0 °C		5298 psi
@Strain 147.51 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.93 MPa
@Strain 268.65 %,
Temperature 90.0 °C		5356 psi
@Strain 268.65 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 37.08 MPa
@Strain 171.45 %,
Temperature 60.0 °C		5378 psi
@Strain 171.45 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.64 MPa
@Strain 188.45 %,
Temperature 60.0 °C		5459 psi
@Strain 188.45 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.65 MPa
@Strain 253.42 %,
Temperature 90.0 °C		5461 psi
@Strain 253.42 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 38.18 MPa
@Strain 197.17 %,
Temperature 60.0 °C		5538 psi
@Strain 197.17 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.38 MPa
@Strain 278.23 %,
Temperature 90.0 °C		5567 psi
@Strain 278.23 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 38.52 MPa
@Strain 58.29 %,
Temperature 23.0 °C		5587 psi
@Strain 58.29 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.87 MPa
@Strain 64.25 %,
Temperature 23.0 °C		5638 psi
@Strain 64.25 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.98 MPa
@Strain 263.82 %,
Temperature 90.0 °C		5654 psi
@Strain 263.82 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 39.09 MPa
@Strain 70.2 %,
Temperature 23.0 °C		5670 psi
@Strain 70.2 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.17 MPa
@Strain 76.19 %,
Temperature 23.0 °C		5681 psi
@Strain 76.19 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.2 MPa
@Strain 82.16 %,
Temperature 23.0 °C		5690 psi
@Strain 82.16 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.2 MPa
@Strain 88.11 %,
Temperature 23.0 °C		5690 psi
@Strain 88.11 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.32 MPa
@Strain 94.1 %,
Temperature 23.0 °C		5703 psi
@Strain 94.1 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.48 MPa
@Strain 100.04 %,
Temperature 23.0 °C		5726 psi
@Strain 100.04 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.81 MPa
@Strain 297.04 %,
Temperature 90.0 °C		5774 psi
@Strain 297.04 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 39.85 MPa
@Strain 4.94 %,
Temperature 23.0 °C		5780 psi
@Strain 4.94 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.94 MPa
@Strain 287.93 %,
Temperature 90.0 °C		5793 psi
@Strain 287.93 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 40.12 MPa
@Strain 201.44 %,
Temperature 60.0 °C		5819 psi
@Strain 201.44 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.24 MPa
@Strain 308.97 %,
Temperature 60.0 °C		5836 psi
@Strain 308.97 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.31 MPa
@Strain 69.11 %,
Temperature 40.0 °C		5846 psi
@Strain 69.11 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 40.47 MPa
@Strain 308.95 %,
Temperature 60.0 °C		5870 psi
@Strain 308.95 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.51 MPa
@Strain 272.69 %,
Temperature 90.0 °C		5875 psi
@Strain 272.69 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 40.74 MPa
@Strain 308.93 %,
Temperature 60.0 °C		5909 psi
@Strain 308.93 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.87 MPa
@Strain 75.22 %,
Temperature 40.0 °C		5928 psi
@Strain 75.22 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 41.01 MPa
@Strain 6.16 %,
Temperature 40.0 °C		5948 psi
@Strain 6.16 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 41.05 MPa
@Strain 308.91 %,
Temperature 60.0 °C		5954 psi
@Strain 308.91 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.17 MPa
@Strain 81.35 %,
Temperature 40.0 °C		5971 psi
@Strain 81.35 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 41.24 MPa
@Strain 87.53 %,
Temperature 40.0 °C		5981 psi
@Strain 87.53 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 41.29 MPa
@Strain 93.78 %,
Temperature 40.0 °C		5989 psi
@Strain 93.78 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 41.34 MPa
@Strain 100.05 %,
Temperature 40.0 °C		5996 psi
@Strain 100.05 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 41.42 MPa
@Strain 308.89 %,
Temperature 60.0 °C		6007 psi
@Strain 308.89 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.89 MPa
@Strain 308.86 %,
Temperature 60.0 °C		6076 psi
@Strain 308.86 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 42.08 MPa
@Strain 281.37 %,
Temperature 90.0 °C		6103 psi
@Strain 281.37 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 42.09 MPa
@Strain 51.8 %,
Temperature 23.0 °C		6105 psi
@Strain 51.8 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 42.28 MPa
@Strain 9.84 %,
Temperature 40.0 °C		6132 psi
@Strain 9.84 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 42.45 MPa
@Strain 62.72 %,
Temperature 40.0 °C		6157 psi
@Strain 62.72 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 42.53 MPa
@Strain 308.82 %,
Temperature 60.0 °C		6168 psi
@Strain 308.82 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 43.0 MPa
@Strain 1.82 %,
Temperature -20.0 °C		6240 psi
@Strain 1.82 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 43.06 MPa
@Strain 8.32 %,
Temperature 23.0 °C		6245 psi
@Strain 8.32 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.24 MPa
@Strain 299.33 %,
Temperature 90.0 °C		6271 psi
@Strain 299.33 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 43.56 MPa
@Strain 13.49 %,
Temperature 40.0 °C		6318 psi
@Strain 13.49 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 43.58 MPa
@Strain 308.78 %,
Temperature 60.0 °C		6321 psi
@Strain 308.78 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 43.66 MPa
@Strain 56.94 %,
Temperature 40.0 °C		6332 psi
@Strain 56.94 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 43.74 MPa
@Strain 290.29 %,
Temperature 90.0 °C		6344 psi
@Strain 290.29 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 43.96 MPa
@Strain 25.78 %,
Temperature 23.0 °C		6376 psi
@Strain 25.78 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.18 MPa
@Strain 2.02 %,
Temperature -40.0 °C		6408 psi
@Strain 2.02 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 44.19 MPa
@Strain 210.69 %,
Temperature 60.0 °C		6409 psi
@Strain 210.69 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 44.23 MPa
@Strain 51.62 %,
Temperature 40.0 °C		6415 psi
@Strain 51.62 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 44.36 MPa
@Strain 31.7 %,
Temperature 23.0 °C		6434 psi
@Strain 31.7 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.43 MPa
@Strain 37.71 %,
Temperature 23.0 °C		6444 psi
@Strain 37.71 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.43 MPa
@Strain 43.69 %,
Temperature 23.0 °C		6444 psi
@Strain 43.69 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.44 MPa
@Strain 17.18 %,
Temperature 40.0 °C		6445 psi
@Strain 17.18 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 44.48 MPa
@Strain 49.65 %,
Temperature 23.0 °C		6451 psi
@Strain 49.65 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.52 MPa
@Strain 239.49 %,
Temperature 60.0 °C		6457 psi
@Strain 239.49 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 44.57 MPa
@Strain 55.64 %,
Temperature 23.0 °C		6464 psi
@Strain 55.64 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.62 MPa
@Strain 46.61 %,
Temperature 40.0 °C		6472 psi
@Strain 46.61 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 44.66 MPa
@Strain 45.8 %,
Temperature 23.0 °C		6477 psi
@Strain 45.8 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 44.78 MPa
@Strain 61.63 %,
Temperature 23.0 °C		6495 psi
@Strain 61.63 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.89 MPa
@Strain 41.86 %,
Temperature 40.0 °C		6511 psi
@Strain 41.86 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 44.91 MPa
@Strain 67.58 %,
Temperature 23.0 °C		6514 psi
@Strain 67.58 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.96 MPa
@Strain 20.95 %,
Temperature 40.0 °C		6521 psi
@Strain 20.95 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 44.97 MPa
@Strain 79.02 %,
Temperature 23.0 °C		6522 psi
@Strain 79.02 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 45.01 MPa
@Strain 73.54 %,
Temperature 23.0 °C		6528 psi
@Strain 73.54 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 45.08 MPa
@Strain 79.39 %,
Temperature 23.0 °C		6538 psi
@Strain 79.39 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 45.08 MPa
@Strain 74.75 %,
Temperature 23.0 °C		6538 psi
@Strain 74.75 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 45.1 MPa
@Strain 83.88 %,
Temperature 23.0 °C		6540 psi
@Strain 83.88 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 45.12 MPa
@Strain 37.36 %,
Temperature 40.0 °C		6544 psi
@Strain 37.36 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 45.23 MPa
@Strain 24.82 %,
Temperature 40.0 °C		6560 psi
@Strain 24.82 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 45.24 MPa
@Strain 89.11 %,
Temperature 23.0 °C		6562 psi
@Strain 89.11 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 45.26 MPa
@Strain 33.02 %,
Temperature 40.0 °C		6564 psi
@Strain 33.02 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 45.29 MPa
@Strain 11.68 %,
Temperature 23.0 °C		6569 psi
@Strain 11.68 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 45.33 MPa
@Strain 28.87 %,
Temperature 40.0 °C		6575 psi
@Strain 28.87 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 45.4 MPa
@Strain 94.51 %,
Temperature 23.0 °C		6580 psi
@Strain 94.51 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 45.45 MPa
@Strain 100.06 %,
Temperature 23.0 °C		6592 psi
@Strain 100.06 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 45.99 MPa
@Strain 1.98 %,
Temperature -40.0 °C		6670 psi
@Strain 1.98 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 46.04 MPa
@Strain 40.35 %,
Temperature 23.0 °C		6678 psi
@Strain 40.35 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.78 MPa
@Strain 15.1 %,
Temperature 23.0 °C		6785 psi
@Strain 15.1 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.93 MPa
@Strain 35.33 %,
Temperature 23.0 °C		6807 psi
@Strain 35.33 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.93 MPa
@Strain 308.81 %,
Temperature 60.0 °C		6807 psi
@Strain 308.81 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 47.47 MPa
@Strain 269.11 %,
Temperature 60.0 °C		6885 psi
@Strain 269.11 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 47.47 MPa
@Strain 46.7 %,
Temperature 0.000 °C		6885 psi
@Strain 46.7 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 47.53 MPa
@Strain 30.69 %,
Temperature 23.0 °C		6894 psi
@Strain 30.69 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.6 MPa
@Strain 18.65 %,
Temperature 23.0 °C		6900 psi
@Strain 18.65 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.86 MPa
@Strain 26.41 %,
Temperature 23.0 °C		6942 psi
@Strain 26.41 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.92 MPa
@Strain 22.41 %,
Temperature 23.0 °C		6950 psi
@Strain 22.41 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.94 MPa
@Strain 52.62 %,
Temperature 0.000 °C		6953 psi
@Strain 52.62 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.28 MPa
@Strain 64.49 %,
Temperature 0.000 °C		7002 psi
@Strain 64.49 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.31 MPa
@Strain 58.53 %,
Temperature 0.000 °C		7007 psi
@Strain 58.53 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.4 MPa
@Strain 70.4 %,
Temperature 0.000 °C		7020 psi
@Strain 70.4 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.63 MPa
@Strain 82.27 %,
Temperature 0.000 °C		7053 psi
@Strain 82.27 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.72 MPa
@Strain 76.32 %,
Temperature 0.000 °C		7066 psi
@Strain 76.32 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.88 MPa
@Strain 100.05 %,
Temperature 0.000 °C		7089 psi
@Strain 100.05 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.93 MPa
@Strain 88.16 %,
Temperature 0.000 °C		7097 psi
@Strain 88.16 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.93 MPa
@Strain 94.1 %,
Temperature 0.000 °C		7097 psi
@Strain 94.1 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.99 MPa
@Strain 2.27 %,
Temperature 0.000 °C		7105 psi
@Strain 2.27 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 50.5 MPa
@Strain 289.24 %,
Temperature 60.0 °C		7320 psi
@Strain 289.24 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.62 MPa
@Strain 40.3 %,
Temperature -20.0 °C		7342 psi
@Strain 40.3 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 50.98 MPa
@Strain 74.43 %,
Temperature -20.0 °C		7394 psi
@Strain 74.43 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 51.17 MPa
@Strain 30.94 %,
Temperature 0.000 °C		7422 psi
@Strain 30.94 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 51.41 MPa
@Strain 50.0 %,
Temperature -20.0 °C		7456 psi
@Strain 50.0 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 51.47 MPa
@Strain 45.14 %,
Temperature -20.0 °C		7465 psi
@Strain 45.14 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 51.57 MPa
@Strain 54.8 %,
Temperature -20.0 °C		7480 psi
@Strain 54.8 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 51.71 MPa
@Strain 59.63 %,
Temperature -20.0 °C		7500 psi
@Strain 59.63 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 51.72 MPa
@Strain 303.18 %,
Temperature 60.0 °C		7501 psi
@Strain 303.18 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.76 MPa
@Strain 46.01 %,
Temperature 0.000 °C		7507 psi
@Strain 46.01 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 51.83 MPa
@Strain 92.14 %,
Temperature 0.000 °C		7517 psi
@Strain 92.14 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 51.83 MPa
@Strain 64.46 %,
Temperature -20.0 °C		7517 psi
@Strain 64.46 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 51.85 MPa
@Strain 86.28 %,
Temperature 0.000 °C		7520 psi
@Strain 86.28 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 51.85 MPa
@Strain 40.96 %,
Temperature 0.000 °C		7520 psi
@Strain 40.96 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 51.86 MPa
@Strain 35.92 %,
Temperature 0.000 °C		7522 psi
@Strain 35.92 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 51.92 MPa
@Strain 51.03 %,
Temperature 0.000 °C		7530 psi
@Strain 51.03 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 51.99 MPa
@Strain 56.07 %,
Temperature 0.000 °C		7541 psi
@Strain 56.07 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 51.99 MPa
@Strain 69.26 %,
Temperature -20.0 °C		7541 psi
@Strain 69.26 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 52.02 MPa
@Strain 61.09 %,
Temperature 0.000 °C		7545 psi
@Strain 61.09 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 52.18 MPa
@Strain 66.1 %,
Temperature 0.000 °C		7568 psi
@Strain 66.1 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 52.24 MPa
@Strain 76.16 %,
Temperature 0.000 °C		7577 psi
@Strain 76.16 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 52.27 MPa
@Strain 71.14 %,
Temperature 0.000 °C		7581 psi
@Strain 71.14 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 52.38 MPa
@Strain 81.18 %,
Temperature 0.000 °C		7597 psi
@Strain 81.18 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 54.13 MPa
@Strain 29.47 %,
Temperature -20.0 °C		7851 psi
@Strain 29.47 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 54.14 MPa
@Strain 25.55 %,
Temperature -20.0 °C		7852 psi
@Strain 25.55 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 54.47 MPa
@Strain 18.92 %,
Temperature 23.0 °C		7900 psi
@Strain 18.92 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 54.5 MPa
@Strain 33.22 %,
Temperature -20.0 °C		7900 psi
@Strain 33.22 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 54.58 MPa
@Strain 36.96 %,
Temperature -20.0 °C		7916 psi
@Strain 36.96 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 54.65 MPa
@Strain 52.29 %,
Temperature -20.0 °C		7926 psi
@Strain 52.29 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 54.67 MPa
@Strain 48.19 %,
Temperature -20.0 °C		7929 psi
@Strain 48.19 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 54.69 MPa
@Strain 44.43 %,
Temperature -20.0 °C		7932 psi
@Strain 44.43 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 54.72 MPa
@Strain 40.67 %,
Temperature -20.0 °C		7936 psi
@Strain 40.67 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 56.19 MPa
@Strain 2.76 %,
Temperature -20.0 °C		8150 psi
@Strain 2.76 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 56.77 MPa
@Strain 13.26 %,
Temperature 23.0 °C		8234 psi
@Strain 13.26 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 57.77 MPa
@Strain 39.63 %,
Temperature 0.000 °C		8379 psi
@Strain 39.63 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 58.71 MPa
@Strain 2.81 %,
Temperature -40.0 °C		8515 psi
@Strain 2.81 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 58.92 MPa
@Strain 7.92 %,
Temperature 23.0 °C		8546 psi
@Strain 7.92 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 59.36 MPa
@Strain 3.41 %,
Temperature 23.0 °C		8609 psi
@Strain 3.41 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 60.81 MPa
@Strain 24.98 %,
Temperature 0.000 °C		8820 psi
@Strain 24.98 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 62.99 MPa
@Strain 33.81 %,
Temperature 0.000 °C		9136 psi
@Strain 33.81 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.12 MPa
@Strain 5.20 %,
Temperature 0.000 °C		9300 psi
@Strain 5.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.55 MPa
@Strain 28.89 %,
Temperature 0.000 °C		9362 psi
@Strain 28.89 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.29 MPa
@Strain 8.78 %,
Temperature 0.000 °C		9470 psi
@Strain 8.78 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.3 MPa
@Strain 3.17 %,
Temperature -40.0 °C		9470 psi
@Strain 3.17 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 65.33 MPa
@Strain 24.42 %,
Temperature 0.000 °C		9475 psi
@Strain 24.42 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.64 MPa
@Strain 20.29 %,
Temperature 0.000 °C		9520 psi
@Strain 20.29 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.74 MPa
@Strain 12.52 %,
Temperature 0.000 °C		9535 psi
@Strain 12.52 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.95 MPa
@Strain 16.35 %,
Temperature 0.000 °C		9565 psi
@Strain 16.35 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.32 MPa
@Strain 3.20 %,
Temperature -20.0 °C		9619 psi
@Strain 3.20 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 66.8 MPa
@Strain 3.56 %,
Temperature 0.000 °C		9690 psi
@Strain 3.56 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 68.21 MPa
@Strain 19.51 %,
Temperature 0.000 °C		9893 psi
@Strain 19.51 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 69.37 MPa
@Strain 33.66 %,
Temperature -20.0 °C		10060 psi
@Strain 33.66 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 70.2 MPa
@Strain 14.8 %,
Temperature 0.000 °C		10200 psi
@Strain 14.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 70.39 MPa
@Strain 3.61 %,
Temperature -40.0 °C		10210 psi
@Strain 3.61 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 72.53 MPa
@Strain 10.37 %,
Temperature 0.000 °C		10520 psi
@Strain 10.37 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 73.17 MPa
@Strain 4.99 %,
Temperature -20.0 °C		10610 psi
@Strain 4.99 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 73.84 MPa
@Strain 28.93 %,
Temperature -20.0 °C		10710 psi
@Strain 28.93 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 74.44 MPa
@Strain 20.08 %,
Temperature -20.0 °C		10800 psi
@Strain 20.08 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 75.47 MPa
@Strain 24.79 %,
Temperature -20.0 °C		10950 psi
@Strain 24.79 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 75.93 MPa
@Strain 6.37 %,
Temperature 0.000 °C		11010 psi
@Strain 6.37 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.42 MPa
@Strain 21.0 %,
Temperature -20.0 °C		11080 psi
@Strain 21.0 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 77.02 MPa
@Strain 17.44 %,
Temperature -20.0 °C		11170 psi
@Strain 17.44 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 77.21 MPa
@Strain 7.78 %,
Temperature -20.0 °C		11200 psi
@Strain 7.78 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 77.55 MPa
@Strain 14.06 %,
Temperature -20.0 °C		11250 psi
@Strain 14.06 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 77.79 MPa
@Strain 10.82 %,
Temperature -20.0 °C		11280 psi
@Strain 10.82 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 77.95 MPa
@Strain 16.33 %,
Temperature -20.0 °C		11310 psi
@Strain 16.33 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 78.05 MPa
@Strain 4.41 %,
Temperature -40.0 °C		11320 psi
@Strain 4.41 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 79.79 MPa
@Strain 4.47 %,
Temperature -40.0 °C		11570 psi
@Strain 4.47 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 80.26 MPa
@Strain 12.91 %,
Temperature -20.0 °C		11640 psi
@Strain 12.91 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 80.89 MPa
@Strain 4.84 %,
Temperature -20.0 °C		11730 psi
@Strain 4.84 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 82.38 MPa
@Strain 9.81 %,
Temperature -20.0 °C		11950 psi
@Strain 9.81 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 84.04 MPa
@Strain 7.06 %,
Temperature -20.0 °C		12190 psi
@Strain 7.06 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 85.15 MPa
@Strain 29.24 %,
Temperature -40.0 °C		12350 psi
@Strain 29.24 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 85.91 MPa
@Strain 5.80 %,
Temperature -40.0 °C		12460 psi
@Strain 5.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 86.55 MPa
@Strain 5.41 %,
Temperature -40.0 °C		12550 psi
@Strain 5.41 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 86.65 MPa
@Strain 26.47 %,
Temperature -40.0 °C		12570 psi
@Strain 26.47 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 88.13 MPa
@Strain 11.01 %,
Temperature -40.0 °C		12780 psi
@Strain 11.01 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 88.63 MPa
@Strain 24.06 %,
Temperature -40.0 °C		12850 psi
@Strain 24.06 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 89.05 MPa
@Strain 10.68 %,
Temperature -40.0 °C		12920 psi
@Strain 10.68 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 89.79 MPa
@Strain 7.45 %,
Temperature -40.0 °C		13020 psi
@Strain 7.45 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 89.95 MPa
@Strain 21.7 %,
Temperature -40.0 °C		13050 psi
@Strain 21.7 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 90.45 MPa
@Strain 6.44 %,
Temperature -40.0 °C		13120 psi
@Strain 6.44 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 90.98 MPa
@Strain 19.44 %,
Temperature -40.0 °C		13200 psi
@Strain 19.44 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 91.13 MPa
@Strain 9.89 %,
Temperature -40.0 °C		13220 psi
@Strain 9.89 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.28 MPa
@Strain 9.24 %,
Temperature -40.0 °C		13240 psi
@Strain 9.24 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 91.59 MPa
@Strain 17.29 %,
Temperature -40.0 °C		13280 psi
@Strain 17.29 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 91.62 MPa
@Strain 15.17 %,
Temperature -40.0 °C		13290 psi
@Strain 15.17 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 91.63 MPa
@Strain 13.1 %,
Temperature -40.0 °C		13290 psi
@Strain 13.1 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 91.7 MPa
@Strain 11.15 %,
Temperature -40.0 °C		13300 psi
@Strain 11.15 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 91.95 MPa
@Strain 7.63 %,
Temperature -40.0 °C		13340 psi
@Strain 7.63 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.99 MPa
@Strain 8.79 %,
Temperature -40.0 °C		13340 psi
@Strain 8.79 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Tensile Strength, Yield 47.0 MPa
@Temperature 23.0 °C		6820 psi
@Temperature 73.4 °F		DAM; ISO 527
Elongation at Break 258 %
@Temperature 23.0 °C		258 %
@Temperature 73.4 °F		DAM; ISO 527
Tensile Modulus  0.213 GPa
@Temperature 150 °C		30.9 ksi
@Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.227 GPa
@Temperature 150 °C		32.9 ksi
@Temperature 302 °F		DAM; ISO 11403-1/-2
 0.272 GPa
@Temperature 120 °C		39.5 ksi
@Temperature 248 °F		50%RH; ISO 11403-1/-2
 0.309 GPa
@Temperature 120 °C		44.8 ksi
@Temperature 248 °F		DAM; ISO 11403-1/-2
 0.357 GPa
@Temperature 90.0 °C		51.8 ksi
@Temperature 194 °F		50%RH; ISO 11403-1/-2
 0.375 GPa
@Temperature 90.0 °C		54.4 ksi
@Temperature 194 °F		DAM; ISO 11403-1/-2
 0.500 GPa
@Temperature 60.0 °C		72.5 ksi
@Temperature 140 °F		50%RH; ISO 11403-1/-2
 0.602 GPa
@Temperature 60.0 °C		87.3 ksi
@Temperature 140 °F		DAM; ISO 11403-1/-2
 0.717 GPa
@Temperature 40.0 °C		104 ksi
@Temperature 104 °F		50%RH; ISO 11403-1/-2
 1.254 GPa
@Temperature 23.0 °C		181.9 ksi
@Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 1.349 GPa
@Temperature 40.0 °C		195.7 ksi
@Temperature 104 °F		DAM; ISO 11403-1/-2
 2.055 GPa
@Temperature 23.0 °C		298.1 ksi
@Temperature 73.4 °F		DAM; ISO 11403-1/-2
 2.313 GPa
@Temperature 0.000 °C		335.5 ksi
@Temperature 32.0 °F		DAM; ISO 11403-1/-2
 2.315 GPa
@Temperature 23.0 °C		335.8 ksi
@Temperature 73.4 °F		DAM; ISO 527
 2.316 GPa
@Temperature -40.0 °C		335.9 ksi
@Temperature -40.0 °F		DAM; ISO 11403-1/-2
 2.32 GPa
@Temperature -20.0 °C		336 ksi
@Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 2.374 GPa
@Temperature -20.0 °C		344.3 ksi
@Temperature -4.00 °F		DAM; ISO 11403-1/-2
 2.458 GPa
@Temperature 0.000 °C		356.5 ksi
@Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 2.459 GPa
@Temperature -40.0 °C		356.6 ksi
@Temperature -40.0 °F		50%RH; ISO 11403-1/-2
Flexural Strength 86.0 MPa
@Temperature 23.0 °C		12500 psi
@Temperature 73.4 °F		DAM; ISO 178
Flexural Modulus 1.90 GPa
@Temperature 23.0 °C		276 ksi
@Temperature 73.4 °F		DAM; ISO 178
Charpy Impact Unnotched NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		DAM; ISO 179/1eU
Charpy Impact, Notched 0.560 J/cm²
@Temperature 23.0 °C		2.66 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 151 °C304 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 54.0 °C129 °FDAM; ISO 75-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; DAM; ISO 11357-1/-3
 240 °C464 °FDAM; Optimum; Extrusion
 235 - 245 °C455 - 473 °FDAM; Extrusion
Drying Temperature 80.0 °C176 °FDAM; Extrusion
Dry Time 3.00 - 4.00 hour3.00 - 4.00 hourDAM; Extrusion
Moisture Content <= 0.050 %<= 0.050 %DAM; Extrusion
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesChemical Resistance, GoodDAM
 Dimensional Stability, GoodDAM
 Flexibility, GoodDAM
 Moisture Absorption, LowDAM
 Renewable Resource ContentDAM
 Viscosity, HighDAM
FormsPelletsDAM
GenericPA610DAM
Material StatusPreliminary DataDAM
Part Marking Code>PA610<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA610DAM
Processing MethodExtrusionDAM
Product CategoryExtrusion ResinsDAM
 Renewably Sourced ResinsDAM
 Unreinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA610ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
UsesAutomotive ApplicationsDAM
 Cable JacketingDAM
 Consumer ApplicationsDAM
 FilamentsDAM
 HoseDAM
 Industrial ApplicationsDAM
 TubingDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47878.html

免责声明: 本文 DuPont Performance Polymers Zytel® RS LC3090 NC010 Nylon 610 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4