DuPont Performance Polymers Zytel® RS LC3060 NC010 Nylon 610 物性表: DuPont Performance Polymers Zytel® RS LC3060 NC010 Nylon 610物性表及特性介绍,DuPont Performance Polymers Zytel® RS LC3060 NC010 Nylon 610注塑参数详情,如需DuPont Performance Polymers Zytel® RS LC3060 NC010 Nylon 610下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.07
  • 拉伸强度 [MPa]: 58.0
 
Physical PropertiesMetricEnglishComments
Density 1.07 g/cc0.0387 lb/in³DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.014 cm/cm0.014 in/inParallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.015 cm/cm0.015 in/inNormal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 62.0 MPa
@Temperature 23.0 °C		8990 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Stress  0.0400 MPa
@Strain 0.000 %,
Temperature 60.0 °C		5.80 psi
@Strain 0.000 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 0.0800 MPa
@Strain 0.000 %,
Temperature 60.0 °C		11.6 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 0.0900 MPa
@Strain 0.000 %,
Temperature 90.0 °C		13.1 psi
@Strain 0.000 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 0.0900 MPa
@Strain 0.000 %,
Temperature 150 °C		13.1 psi
@Strain 0.000 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.0900 MPa
@Strain 0.000 %,
Temperature 120 °C		13.1 psi
@Strain 0.000 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 0.0900 MPa
@Strain 0.000 %,
Temperature 120 °C		13.1 psi
@Strain 0.000 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 0.100 MPa
@Strain 0.000 %,
Temperature 90.0 °C		14.5 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 0.100 MPa
@Strain 0.000 %,
Temperature 150 °C		14.5 psi
@Strain 0.000 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 0.100 MPa
@Strain 0.000 %,
Temperature 40.0 °C		14.5 psi
@Strain 0.000 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 0.230 MPa
@Strain 0.000 %,
Temperature 23.0 °C		33.4 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 0.270 MPa
@Strain 0.000 %,
Temperature 40.0 °C		39.2 psi
@Strain 0.000 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 0.280 MPa
@Strain 0.000 %,
Temperature -40.0 °C		40.6 psi
@Strain 0.000 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 0.300 MPa
@Strain 0.100 %,
Temperature 150 °C		43.5 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.310 MPa
@Strain 0.0200 %,
Temperature -40.0 °C		45.0 psi
@Strain 0.0200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 0.330 MPa
@Strain 0.0700 %,
Temperature 120 °C		47.9 psi
@Strain 0.0700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 0.370 MPa
@Strain 0.000 %,
Temperature -40.0 °C		53.7 psi
@Strain 0.000 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 0.380 MPa
@Strain 0.0800 %,
Temperature 90.0 °C		55.1 psi
@Strain 0.0800 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 0.420 MPa
@Strain 0.000 %,
Temperature -20.0 °C		60.9 psi
@Strain 0.000 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 0.440 MPa
@Strain 0.000 %,
Temperature 0.000 °C		63.8 psi
@Strain 0.000 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 0.440 MPa
@Strain 0.000 %,
Temperature 0.000 °C		63.8 psi
@Strain 0.000 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 0.510 MPa
@Strain 0.190 %,
Temperature 150 °C		74.0 psi
@Strain 0.190 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.520 MPa
@Strain 0.0300 %,
Temperature -40.0 °C		75.4 psi
@Strain 0.0300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 0.530 MPa
@Strain 0.000 %,
Temperature -20.0 °C		76.9 psi
@Strain 0.000 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 0.540 MPa
@Strain 0.000 %,
Temperature 23.0 °C		78.3 psi
@Strain 0.000 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 0.540 MPa
@Strain 0.100 %,
Temperature 60.0 °C		78.3 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 0.580 MPa
@Strain 0.160 %,
Temperature 120 °C		84.1 psi
@Strain 0.160 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 0.650 MPa
@Strain 0.100 %,
Temperature 60.0 °C		94.3 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 0.660 MPa
@Strain 0.160 %,
Temperature 90.0 °C		95.7 psi
@Strain 0.160 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 0.700 MPa
@Strain 0.0600 %,
Temperature -40.0 °C		102 psi
@Strain 0.0600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 0.830 MPa
@Strain 0.240 %,
Temperature 120 °C		120 psi
@Strain 0.240 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 0.840 MPa
@Strain 0.100 %,
Temperature 40.0 °C		122 psi
@Strain 0.100 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 0.940 MPa
@Strain 0.230 %,
Temperature 90.0 °C		136 psi
@Strain 0.230 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 0.990 MPa
@Strain 0.190 %,
Temperature 60.0 °C		144 psi
@Strain 0.190 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 1.07 MPa
@Strain 0.0500 %,
Temperature -40.0 °C		155 psi
@Strain 0.0500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 1.21 MPa
@Strain 0.0400 %,
Temperature -20.0 °C		175 psi
@Strain 0.0400 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 1.23 MPa
@Strain 0.190 %,
Temperature 60.0 °C		178 psi
@Strain 0.190 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 1.34 MPa
@Strain 0.0800 %,
Temperature 23.0 °C		194 psi
@Strain 0.0800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 1.36 MPa
@Strain 0.0800 %,
Temperature -40.0 °C		197 psi
@Strain 0.0800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 1.39 MPa
@Strain 0.0400 %,
Temperature 0.000 °C		202 psi
@Strain 0.0400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 1.43 MPa
@Strain 0.0400 %,
Temperature -20.0 °C		207 psi
@Strain 0.0400 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 1.58 MPa
@Strain 0.200 %,
Temperature 40.0 °C		229 psi
@Strain 0.200 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 1.63 MPa
@Strain 0.100 %,
Temperature 40.0 °C		236 psi
@Strain 0.100 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 1.67 MPa
@Strain 0.0600 %,
Temperature 0.000 °C		242 psi
@Strain 0.0600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 1.80 MPa
@Strain 0.0900 %,
Temperature -40.0 °C		261 psi
@Strain 0.0900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 1.91 MPa
@Strain 0.0600 %,
Temperature 23.0 °C		277 psi
@Strain 0.0600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 1.97 MPa
@Strain 0.0700 %,
Temperature -20.0 °C		286 psi
@Strain 0.0700 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 2.05 MPa
@Strain 0.100 %,
Temperature -40.0 °C		297 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 2.31 MPa
@Strain 0.0900 %,
Temperature 0.000 °C		335 psi
@Strain 0.0900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 2.33 MPa
@Strain 0.160 %,
Temperature 23.0 °C		338 psi
@Strain 0.160 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 2.36 MPa
@Strain 0.0800 %,
Temperature -20.0 °C		342 psi
@Strain 0.0800 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 2.57 MPa
@Strain 0.130 %,
Temperature -40.0 °C		373 psi
@Strain 0.130 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 2.76 MPa
@Strain 0.130 %,
Temperature -40.0 °C		400 psi
@Strain 0.130 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 2.77 MPa
@Strain 0.100 %,
Temperature -20.0 °C		402 psi
@Strain 0.100 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 2.93 MPa
@Strain 0.110 %,
Temperature 0.000 °C		425 psi
@Strain 0.110 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 2.95 MPa
@Strain 0.180 %,
Temperature 40.0 °C		428 psi
@Strain 0.180 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 3.04 MPa
@Strain 1.20 %,
Temperature 150 °C		441 psi
@Strain 1.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.24 MPa
@Strain 0.110 %,
Temperature -20.0 °C		470 psi
@Strain 0.110 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 3.27 MPa
@Strain 0.230 %,
Temperature 23.0 °C		474 psi
@Strain 0.230 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 3.29 MPa
@Strain 0.130 %,
Temperature 0.000 °C		477 psi
@Strain 0.130 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 3.33 MPa
@Strain 0.130 %,
Temperature 23.0 °C		483 psi
@Strain 0.130 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 3.38 MPa
@Strain 0.160 %,
Temperature -40.0 °C		490 psi
@Strain 0.160 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 3.44 MPa
@Strain 0.160 %,
Temperature -40.0 °C		499 psi
@Strain 0.160 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 3.49 MPa
@Strain 0.140 %,
Temperature -20.0 °C		506 psi
@Strain 0.140 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 4.05 MPa
@Strain 0.150 %,
Temperature 0.000 °C		587 psi
@Strain 0.150 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 4.13 MPa
@Strain 0.190 %,
Temperature -40.0 °C		599 psi
@Strain 0.190 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 4.16 MPa
@Strain 0.180 %,
Temperature -40.0 °C		603 psi
@Strain 0.180 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 4.18 MPa
@Strain 0.150 %,
Temperature -20.0 °C		606 psi
@Strain 0.150 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 4.24 MPa
@Strain 0.170 %,
Temperature -20.0 °C		615 psi
@Strain 0.170 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 4.26 MPa
@Strain 0.170 %,
Temperature 0.000 °C		618 psi
@Strain 0.170 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 4.71 MPa
@Strain 0.200 %,
Temperature 23.0 °C		683 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 4.76 MPa
@Strain 0.210 %,
Temperature -40.0 °C		690 psi
@Strain 0.210 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 4.90 MPa
@Strain 0.200 %,
Temperature -20.0 °C		711 psi
@Strain 0.200 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 4.95 MPa
@Strain 0.210 %,
Temperature -40.0 °C		718 psi
@Strain 0.210 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 4.99 MPa
@Strain 0.180 %,
Temperature -20.0 °C		724 psi
@Strain 0.180 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 5.13 MPa
@Strain 1.15 %,
Temperature 90.0 °C		744 psi
@Strain 1.15 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 5.15 MPa
@Strain 0.210 %,
Temperature 0.000 °C		747 psi
@Strain 0.210 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 5.29 MPa
@Strain 0.210 %,
Temperature 0.000 °C		767 psi
@Strain 0.210 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 5.42 MPa
@Strain 0.240 %,
Temperature -40.0 °C		786 psi
@Strain 0.240 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 5.49 MPa
@Strain 0.310 %,
Temperature 40.0 °C		796 psi
@Strain 0.310 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 5.59 MPa
@Strain 0.230 %,
Temperature -20.0 °C		811 psi
@Strain 0.230 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 5.71 MPa
@Strain 0.240 %,
Temperature -40.0 °C		828 psi
@Strain 0.240 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 5.79 MPa
@Strain 0.210 %,
Temperature -20.0 °C		840 psi
@Strain 0.210 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 6.03 MPa
@Strain 0.240 %,
Temperature 0.000 °C		875 psi
@Strain 0.240 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 6.65 MPa
@Strain 0.250 %,
Temperature -20.0 °C		965 psi
@Strain 0.250 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 7.31 MPa
@Strain 1.29 %,
Temperature 60.0 °C		1060 psi
@Strain 1.29 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 7.57 MPa
@Strain 0.300 %,
Temperature 0.000 °C		1100 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 8.01 MPa
@Strain 2.81 %,
Temperature 120 °C		1160 psi
@Strain 2.81 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.15 MPa
@Strain 2.30 %,
Temperature 90.0 °C		1180 psi
@Strain 2.30 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 8.54 MPa
@Strain 4.56 %,
Temperature 150 °C		1240 psi
@Strain 4.56 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.79 MPa
@Strain 0.370 %,
Temperature -20.0 °C		1270 psi
@Strain 0.370 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 8.95 MPa
@Strain 2.95 %,
Temperature 120 °C		1300 psi
@Strain 2.95 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.14 MPa
@Strain 1.22 %,
Temperature 60.0 °C		1330 psi
@Strain 1.22 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 9.21 MPa
@Strain 4.55 %,
Temperature 150 °C		1340 psi
@Strain 4.55 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.57 MPa
@Strain 0.450 %,
Temperature -40.0 °C		1533 psi
@Strain 0.450 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 10.59 MPa
@Strain 0.460 %,
Temperature 23.0 °C		1536 psi
@Strain 0.460 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 11.16 MPa
@Strain 8.07 %,
Temperature 150 °C		1619 psi
@Strain 8.07 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.18 MPa
@Strain 1.45 %,
Temperature 40.0 °C		1767 psi
@Strain 1.45 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 12.5 MPa
@Strain 11.67 %,
Temperature 150 °C		1810 psi
@Strain 11.67 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.96 MPa
@Strain 6.16 %,
Temperature 120 °C		1880 psi
@Strain 6.16 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.31 MPa
@Strain 15.42 %,
Temperature 150 °C		1930 psi
@Strain 15.42 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.85 MPa
@Strain 19.27 %,
Temperature 150 °C		2009 psi
@Strain 19.27 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.23 MPa
@Strain 23.18 %,
Temperature 150 °C		2064 psi
@Strain 23.18 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.51 MPa
@Strain 27.21 %,
Temperature 150 °C		2105 psi
@Strain 27.21 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.61 MPa
@Strain 70.73 %,
Temperature 150 °C		2119 psi
@Strain 70.73 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.62 MPa
@Strain 5.55 %,
Temperature 90.0 °C		2120 psi
@Strain 5.55 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 14.71 MPa
@Strain 31.33 %,
Temperature 150 °C		2134 psi
@Strain 31.33 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.71 MPa
@Strain 64.63 %,
Temperature 150 °C		2134 psi
@Strain 64.63 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.75 MPa
@Strain 76.61 %,
Temperature 150 °C		2139 psi
@Strain 76.61 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.86 MPa
@Strain 82.44 %,
Temperature 150 °C		2155 psi
@Strain 82.44 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.86 MPa
@Strain 35.5 %,
Temperature 150 °C		2155 psi
@Strain 35.5 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.93 MPa
@Strain 58.92 %,
Temperature 150 °C		2165 psi
@Strain 58.92 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.93 MPa
@Strain 88.32 %,
Temperature 150 °C		2165 psi
@Strain 88.32 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.96 MPa
@Strain 94.16 %,
Temperature 150 °C		2170 psi
@Strain 94.16 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.96 MPa
@Strain 39.81 %,
Temperature 150 °C		2170 psi
@Strain 39.81 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.98 MPa
@Strain 100.03 %,
Temperature 150 °C		2173 psi
@Strain 100.03 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.02 MPa
@Strain 44.23 %,
Temperature 150 °C		2178 psi
@Strain 44.23 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.02 MPa
@Strain 53.69 %,
Temperature 150 °C		2178 psi
@Strain 53.69 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.03 MPa
@Strain 48.85 %,
Temperature 150 °C		2180 psi
@Strain 48.85 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.19 MPa
@Strain 19.25 %,
Temperature 150 °C		2203 psi
@Strain 19.25 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.43 MPa
@Strain 9.69 %,
Temperature 120 °C		2238 psi
@Strain 9.69 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.39 MPa
@Strain 35.37 %,
Temperature 150 °C		2377 psi
@Strain 35.37 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.71 MPa
@Strain 94.29 %,
Temperature 150 °C		2424 psi
@Strain 94.29 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.72 MPa
@Strain 72.53 %,
Temperature 150 °C		2425 psi
@Strain 72.53 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.73 MPa
@Strain 52.94 %,
Temperature 150 °C		2426 psi
@Strain 52.94 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.85 MPa
@Strain 13.5 %,
Temperature 120 °C		2444 psi
@Strain 13.5 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.04 MPa
@Strain 115.46 %,
Temperature 150 °C		2471 psi
@Strain 115.46 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.2 MPa
@Strain 133.98 %,
Temperature 150 °C		2490 psi
@Strain 133.98 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.24 MPa
@Strain 4.42 %,
Temperature 60.0 °C		2500 psi
@Strain 4.42 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.4 MPa
@Strain 149.46 %,
Temperature 150 °C		2520 psi
@Strain 149.46 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.65 MPa
@Strain 162.3 %,
Temperature 150 °C		2560 psi
@Strain 162.3 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.73 MPa
@Strain 17.45 %,
Temperature 120 °C		2572 psi
@Strain 17.45 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.83 MPa
@Strain 170.98 %,
Temperature 150 °C		2586 psi
@Strain 170.98 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.17 MPa
@Strain 9.13 %,
Temperature 90.0 °C		2635 psi
@Strain 9.13 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 18.18 MPa
@Strain 176.07 %,
Temperature 150 °C		2637 psi
@Strain 176.07 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.31 MPa
@Strain 21.46 %,
Temperature 120 °C		2656 psi
@Strain 21.46 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.71 MPa
@Strain 179.33 %,
Temperature 150 °C		2714 psi
@Strain 179.33 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.72 MPa
@Strain 25.67 %,
Temperature 120 °C		2715 psi
@Strain 25.67 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.0 MPa
@Strain 29.94 %,
Temperature 120 °C		2760 psi
@Strain 29.94 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.2 MPa
@Strain 34.3 %,
Temperature 120 °C		2780 psi
@Strain 34.3 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.24 MPa
@Strain 17.77 %,
Temperature 120 °C		2791 psi
@Strain 17.77 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.3 MPa
@Strain 81.44 %,
Temperature 120 °C		2800 psi
@Strain 81.44 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.3 MPa
@Strain 87.7 %,
Temperature 120 °C		2800 psi
@Strain 87.7 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.34 MPa
@Strain 38.8 %,
Temperature 120 °C		2805 psi
@Strain 38.8 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.34 MPa
@Strain 75.29 %,
Temperature 120 °C		2805 psi
@Strain 75.29 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.4 MPa
@Strain 69.4 %,
Temperature 120 °C		2810 psi
@Strain 69.4 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.4 MPa
@Strain 93.89 %,
Temperature 120 °C		2810 psi
@Strain 93.89 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.42 MPa
@Strain 43.44 %,
Temperature 120 °C		2817 psi
@Strain 43.44 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.46 MPa
@Strain 63.74 %,
Temperature 120 °C		2822 psi
@Strain 63.74 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.48 MPa
@Strain 48.19 %,
Temperature 120 °C		2825 psi
@Strain 48.19 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.5 MPa
@Strain 53.19 %,
Temperature 120 °C		2830 psi
@Strain 53.19 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.5 MPa
@Strain 58.33 %,
Temperature 120 °C		2830 psi
@Strain 58.33 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.54 MPa
@Strain 100.05 %,
Temperature 120 °C		2834 psi
@Strain 100.05 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.94 MPa
@Strain 184.6 %,
Temperature 150 °C		2892 psi
@Strain 184.6 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.19 MPa
@Strain 12.96 %,
Temperature 90.0 °C		2928 psi
@Strain 12.96 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 20.75 MPa
@Strain 34.7 %,
Temperature 120 °C		3010 psi
@Strain 34.7 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.08 MPa
@Strain 53.27 %,
Temperature 120 °C		3057 psi
@Strain 53.27 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.09 MPa
@Strain 73.93 %,
Temperature 120 °C		3059 psi
@Strain 73.93 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.14 MPa
@Strain 96.6 %,
Temperature 120 °C		3066 psi
@Strain 96.6 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.31 MPa
@Strain 194.13 %,
Temperature 150 °C		3091 psi
@Strain 194.13 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.44 MPa
@Strain 17.0 %,
Temperature 90.0 °C		3110 psi
@Strain 17.0 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 21.48 MPa
@Strain 119.15 %,
Temperature 120 °C		3115 psi
@Strain 119.15 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.8 MPa
@Strain 139.57 %,
Temperature 120 °C		3160 psi
@Strain 139.57 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.91 MPa
@Strain 4.49 %,
Temperature 60.0 °C		3178 psi
@Strain 4.49 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 21.99 MPa
@Strain 209.11 %,
Temperature 150 °C		3189 psi
@Strain 209.11 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.99 MPa
@Strain 0.890 %,
Temperature -40.0 °C		3189 psi
@Strain 0.890 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 22.1 MPa
@Strain 156.05 %,
Temperature 120 °C		3210 psi
@Strain 156.05 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.2 MPa
@Strain 7.78 %,
Temperature 60.0 °C		3220 psi
@Strain 7.78 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.24 MPa
@Strain 21.15 %,
Temperature 90.0 °C		3226 psi
@Strain 21.15 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 22.35 MPa
@Strain 168.26 %,
Temperature 120 °C		3242 psi
@Strain 168.26 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.6 MPa
@Strain 176.09 %,
Temperature 120 °C		3280 psi
@Strain 176.09 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.77 MPa
@Strain 25.45 %,
Temperature 90.0 °C		3303 psi
@Strain 25.45 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 22.82 MPa
@Strain 226.05 %,
Temperature 150 °C		3310 psi
@Strain 226.05 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.06 MPa
@Strain 180.93 %,
Temperature 120 °C		3345 psi
@Strain 180.93 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.11 MPa
@Strain 29.9 %,
Temperature 90.0 °C		3352 psi
@Strain 29.9 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.27 MPa
@Strain 15.13 %,
Temperature 90.0 °C		3375 psi
@Strain 15.13 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 23.32 MPa
@Strain 34.44 %,
Temperature 90.0 °C		3382 psi
@Strain 34.44 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.37 MPa
@Strain 76.27 %,
Temperature 90.0 °C		3390 psi
@Strain 76.27 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.37 MPa
@Strain 82.23 %,
Temperature 90.0 °C		3390 psi
@Strain 82.23 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.42 MPa
@Strain 70.47 %,
Temperature 90.0 °C		3397 psi
@Strain 70.47 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.43 MPa
@Strain 88.21 %,
Temperature 90.0 °C		3398 psi
@Strain 88.21 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.45 MPa
@Strain 39.13 %,
Temperature 90.0 °C		3401 psi
@Strain 39.13 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.47 MPa
@Strain 64.81 %,
Temperature 90.0 °C		3404 psi
@Strain 64.81 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.49 MPa
@Strain 59.34 %,
Temperature 90.0 °C		3407 psi
@Strain 59.34 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.52 MPa
@Strain 43.95 %,
Temperature 90.0 °C		3411 psi
@Strain 43.95 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.52 MPa
@Strain 54.03 %,
Temperature 90.0 °C		3411 psi
@Strain 54.03 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.53 MPa
@Strain 94.15 %,
Temperature 90.0 °C		3413 psi
@Strain 94.15 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.54 MPa
@Strain 48.9 %,
Temperature 90.0 °C		3414 psi
@Strain 48.9 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.63 MPa
@Strain 100.03 %,
Temperature 90.0 °C		3427 psi
@Strain 100.03 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.87 MPa
@Strain 241.87 %,
Temperature 150 °C		3462 psi
@Strain 241.87 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.97 MPa
@Strain 1.70 %,
Temperature 23.0 °C		3477 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 24.26 MPa
@Strain 185.28 %,
Temperature 120 °C		3519 psi
@Strain 185.28 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.32 MPa
@Strain 4.39 %,
Temperature 40.0 °C		3527 psi
@Strain 4.39 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 24.7 MPa
@Strain 254.5 %,
Temperature 150 °C		3580 psi
@Strain 254.5 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.03 MPa
@Strain 11.39 %,
Temperature 60.0 °C		3630 psi
@Strain 11.39 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.78 MPa
@Strain 31.95 %,
Temperature 90.0 °C		3739 psi
@Strain 31.95 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 25.78 MPa
@Strain 264.64 %,
Temperature 150 °C		3739 psi
@Strain 264.64 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.84 MPa
@Strain 192.22 %,
Temperature 120 °C		3748 psi
@Strain 192.22 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.36 MPa
@Strain 50.43 %,
Temperature 90.0 °C		3823 psi
@Strain 50.43 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 26.55 MPa
@Strain 70.47 %,
Temperature 90.0 °C		3851 psi
@Strain 70.47 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 26.73 MPa
@Strain 15.2 %,
Temperature 60.0 °C		3877 psi
@Strain 15.2 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 26.75 MPa
@Strain 91.61 %,
Temperature 90.0 °C		3880 psi
@Strain 91.61 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 26.9 MPa
@Strain 274.34 %,
Temperature 150 °C		3900 psi
@Strain 274.34 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.93 MPa
@Strain 204.81 %,
Temperature 120 °C		3906 psi
@Strain 204.81 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.13 MPa
@Strain 112.83 %,
Temperature 90.0 °C		3935 psi
@Strain 112.83 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 27.38 MPa
@Strain 8.07 %,
Temperature 60.0 °C		3971 psi
@Strain 8.07 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 27.53 MPa
@Strain 1.18 %,
Temperature 0.000 °C		3993 psi
@Strain 1.18 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 27.64 MPa
@Strain 132.53 %,
Temperature 90.0 °C		4009 psi
@Strain 132.53 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 27.68 MPa
@Strain 222.33 %,
Temperature 120 °C		4015 psi
@Strain 222.33 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.75 MPa
@Strain 19.13 %,
Temperature 60.0 °C		4025 psi
@Strain 19.13 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.96 MPa
@Strain 284.09 %,
Temperature 150 °C		4055 psi
@Strain 284.09 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.13 MPa
@Strain 148.88 %,
Temperature 90.0 °C		4080 psi
@Strain 148.88 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 28.38 MPa
@Strain 23.24 %,
Temperature 60.0 °C		4116 psi
@Strain 23.24 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.52 MPa
@Strain 161.32 %,
Temperature 90.0 °C		4136 psi
@Strain 161.32 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 28.77 MPa
@Strain 27.52 %,
Temperature 60.0 °C		4173 psi
@Strain 27.52 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.84 MPa
@Strain 240.47 %,
Temperature 120 °C		4183 psi
@Strain 240.47 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.98 MPa
@Strain 31.91 %,
Temperature 60.0 °C		4203 psi
@Strain 31.91 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.99 MPa
@Strain 77.43 %,
Temperature 60.0 °C		4205 psi
@Strain 77.43 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.0 MPa
@Strain 83.06 %,
Temperature 60.0 °C		4210 psi
@Strain 83.06 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.01 MPa
@Strain 71.93 %,
Temperature 60.0 °C		4208 psi
@Strain 71.93 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.01 MPa
@Strain 170.27 %,
Temperature 90.0 °C		4208 psi
@Strain 170.27 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 29.03 MPa
@Strain 66.53 %,
Temperature 60.0 °C		4210 psi
@Strain 66.53 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.03 MPa
@Strain 293.65 %,
Temperature 150 °C		4210 psi
@Strain 293.65 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.05 MPa
@Strain 88.72 %,
Temperature 60.0 °C		4213 psi
@Strain 88.72 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.06 MPa
@Strain 61.15 %,
Temperature 60.0 °C		4215 psi
@Strain 61.15 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.1 MPa
@Strain 55.95 %,
Temperature 60.0 °C		4220 psi
@Strain 55.95 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.1 MPa
@Strain 36.43 %,
Temperature 60.0 °C		4220 psi
@Strain 36.43 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.1 MPa
@Strain 94.37 %,
Temperature 60.0 °C		4220 psi
@Strain 94.37 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.14 MPa
@Strain 50.88 %,
Temperature 60.0 °C		4226 psi
@Strain 50.88 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.14 MPa
@Strain 41.11 %,
Temperature 60.0 °C		4226 psi
@Strain 41.11 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.15 MPa
@Strain 45.92 %,
Temperature 60.0 °C		4228 psi
@Strain 45.92 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.18 MPa
@Strain 100.03 %,
Temperature 60.0 °C		4232 psi
@Strain 100.03 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.39 MPa
@Strain 304.36 %,
Temperature 120 °C		4263 psi
@Strain 304.36 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.55 MPa
@Strain 302.72 %,
Temperature 150 °C		4286 psi
@Strain 302.72 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.72 MPa
@Strain 176.98 %,
Temperature 90.0 °C		4311 psi
@Strain 176.98 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 29.88 MPa
@Strain 7.69 %,
Temperature 40.0 °C		4334 psi
@Strain 7.69 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 30.08 MPa
@Strain 256.31 %,
Temperature 120 °C		4363 psi
@Strain 256.31 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.62 MPa
@Strain 11.8 %,
Temperature 60.0 °C		4441 psi
@Strain 11.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.84 MPa
@Strain 183.06 %,
Temperature 90.0 °C		4473 psi
@Strain 183.06 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 31.17 MPa
@Strain 267.95 %,
Temperature 120 °C		4521 psi
@Strain 267.95 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.33 MPa
@Strain 304.35 %,
Temperature 120 °C		4689 psi
@Strain 304.35 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.59 MPa
@Strain 15.71 %,
Temperature 60.0 °C		4727 psi
@Strain 15.71 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.64 MPa
@Strain 191.83 %,
Temperature 90.0 °C		4734 psi
@Strain 191.83 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 32.64 MPa
@Strain 277.69 %,
Temperature 120 °C		4734 psi
@Strain 277.69 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 33.19 MPa
@Strain 11.16 %,
Temperature 40.0 °C		4814 psi
@Strain 11.16 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 33.63 MPa
@Strain 206.12 %,
Temperature 90.0 °C		4878 psi
@Strain 206.12 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 33.74 MPa
@Strain 1.50 %,
Temperature -40.0 °C		4894 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 33.8 MPa
@Strain 19.71 %,
Temperature 60.0 °C		4900 psi
@Strain 19.71 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.99 MPa
@Strain 1.54 %,
Temperature -20.0 °C		4930 psi
@Strain 1.54 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 34.05 MPa
@Strain 1.39 %,
Temperature -20.0 °C		4939 psi
@Strain 1.39 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 34.08 MPa
@Strain 287.5 %,
Temperature 120 °C		4943 psi
@Strain 287.5 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.55 MPa
@Strain 23.9 %,
Temperature 60.0 °C		5011 psi
@Strain 23.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.62 MPa
@Strain 224.73 %,
Temperature 90.0 °C		5021 psi
@Strain 224.73 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 34.9 MPa
@Strain 87.9 %,
Temperature 40.0 °C		5060 psi
@Strain 87.9 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 34.96 MPa
@Strain 94.0 %,
Temperature 40.0 °C		5071 psi
@Strain 94.0 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.03 MPa
@Strain 28.23 %,
Temperature 60.0 °C		5081 psi
@Strain 28.23 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.07 MPa
@Strain 81.85 %,
Temperature 40.0 °C		5086 psi
@Strain 81.85 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.15 MPa
@Strain 14.74 %,
Temperature 40.0 °C		5098 psi
@Strain 14.74 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.23 MPa
@Strain 100.03 %,
Temperature 40.0 °C		5110 psi
@Strain 100.03 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.26 MPa
@Strain 75.95 %,
Temperature 40.0 °C		5114 psi
@Strain 75.95 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.35 MPa
@Strain 32.62 %,
Temperature 60.0 °C		5127 psi
@Strain 32.62 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.36 MPa
@Strain 302.51 %,
Temperature 90.0 °C		5129 psi
@Strain 302.51 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 35.48 MPa
@Strain 70.19 %,
Temperature 40.0 °C		5146 psi
@Strain 70.19 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.5 MPa
@Strain 297.4 %,
Temperature 120 °C		5150 psi
@Strain 297.4 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.57 MPa
@Strain 37.13 %,
Temperature 60.0 °C		5159 psi
@Strain 37.13 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.71 MPa
@Strain 100.03 %,
Temperature 60.0 °C		5179 psi
@Strain 100.03 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.73 MPa
@Strain 41.72 %,
Temperature 60.0 °C		5182 psi
@Strain 41.72 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.75 MPa
@Strain 94.03 %,
Temperature 60.0 °C		5185 psi
@Strain 94.03 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.75 MPa
@Strain 64.65 %,
Temperature 40.0 °C		5185 psi
@Strain 64.65 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.8 MPa
@Strain 88.13 %,
Temperature 60.0 °C		5190 psi
@Strain 88.13 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.83 MPa
@Strain 46.35 %,
Temperature 60.0 °C		5197 psi
@Strain 46.35 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.88 MPa
@Strain 82.41 %,
Temperature 60.0 °C		5204 psi
@Strain 82.41 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.9 MPa
@Strain 51.18 %,
Temperature 60.0 °C		5210 psi
@Strain 51.18 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.92 MPa
@Strain 76.83 %,
Temperature 60.0 °C		5210 psi
@Strain 76.83 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.94 MPa
@Strain 71.41 %,
Temperature 60.0 °C		5213 psi
@Strain 71.41 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.95 MPa
@Strain 66.18 %,
Temperature 60.0 °C		5214 psi
@Strain 66.18 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.95 MPa
@Strain 56.03 %,
Temperature 60.0 °C		5214 psi
@Strain 56.03 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.97 MPa
@Strain 61.03 %,
Temperature 60.0 °C		5217 psi
@Strain 61.03 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.98 MPa
@Strain 59.29 %,
Temperature 40.0 °C		5218 psi
@Strain 59.29 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.15 MPa
@Strain 243.63 %,
Temperature 90.0 °C		5243 psi
@Strain 243.63 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 36.18 MPa
@Strain 54.11 %,
Temperature 40.0 °C		5247 psi
@Strain 54.11 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.23 MPa
@Strain 18.52 %,
Temperature 40.0 °C		5255 psi
@Strain 18.52 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.39 MPa
@Strain 49.14 %,
Temperature 40.0 °C		5278 psi
@Strain 49.14 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.59 MPa
@Strain 44.32 %,
Temperature 40.0 °C		5307 psi
@Strain 44.32 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.76 MPa
@Strain 39.66 %,
Temperature 40.0 °C		5332 psi
@Strain 39.66 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.77 MPa
@Strain 22.45 %,
Temperature 40.0 °C		5333 psi
@Strain 22.45 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.92 MPa
@Strain 35.17 %,
Temperature 40.0 °C		5355 psi
@Strain 35.17 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.98 MPa
@Strain 26.54 %,
Temperature 40.0 °C		5364 psi
@Strain 26.54 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 37.0 MPa
@Strain 30.78 %,
Temperature 40.0 °C		5370 psi
@Strain 30.78 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 37.45 MPa
@Strain 302.46 %,
Temperature 90.0 °C		5432 psi
@Strain 302.46 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 37.75 MPa
@Strain 259.88 %,
Temperature 90.0 °C		5475 psi
@Strain 259.88 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 38.26 MPa
@Strain 49.73 %,
Temperature 23.0 °C		5549 psi
@Strain 49.73 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.65 MPa
@Strain 62.09 %,
Temperature 23.0 °C		5606 psi
@Strain 62.09 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.68 MPa
@Strain 55.87 %,
Temperature 23.0 °C		5610 psi
@Strain 55.87 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.71 MPa
@Strain 68.34 %,
Temperature 23.0 °C		5614 psi
@Strain 68.34 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.74 MPa
@Strain 74.65 %,
Temperature 23.0 °C		5619 psi
@Strain 74.65 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.74 MPa
@Strain 80.97 %,
Temperature 23.0 °C		5619 psi
@Strain 80.97 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.79 MPa
@Strain 87.33 %,
Temperature 23.0 °C		5626 psi
@Strain 87.33 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.89 MPa
@Strain 93.72 %,
Temperature 23.0 °C		5641 psi
@Strain 93.72 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.01 MPa
@Strain 271.79 %,
Temperature 90.0 °C		5658 psi
@Strain 271.79 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 39.02 MPa
@Strain 2.46 %,
Temperature 40.0 °C		5659 psi
@Strain 2.46 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 39.06 MPa
@Strain 100.06 %,
Temperature 23.0 °C		5665 psi
@Strain 100.06 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.78 MPa
@Strain 4.62 %,
Temperature 23.0 °C		5770 psi
@Strain 4.62 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 40.23 MPa
@Strain 69.49 %,
Temperature 40.0 °C		5835 psi
@Strain 69.49 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 40.35 MPa
@Strain 63.34 %,
Temperature 40.0 °C		5852 psi
@Strain 63.34 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 40.59 MPa
@Strain 280.8 %,
Temperature 90.0 °C		5887 psi
@Strain 280.8 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 40.63 MPa
@Strain 75.55 %,
Temperature 40.0 °C		5893 psi
@Strain 75.55 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 40.72 MPa
@Strain 81.62 %,
Temperature 40.0 °C		5906 psi
@Strain 81.62 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 40.83 MPa
@Strain 87.74 %,
Temperature 40.0 °C		5922 psi
@Strain 87.74 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 40.88 MPa
@Strain 93.89 %,
Temperature 40.0 °C		5929 psi
@Strain 93.89 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 40.97 MPa
@Strain 100.03 %,
Temperature 40.0 °C		5942 psi
@Strain 100.03 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 42.36 MPa
@Strain 289.53 %,
Temperature 90.0 °C		6144 psi
@Strain 289.53 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 42.85 MPa
@Strain 43.46 %,
Temperature 23.0 °C		6215 psi
@Strain 43.46 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.14 MPa
@Strain 30.76 %,
Temperature 23.0 °C		6257 psi
@Strain 30.76 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 43.29 MPa
@Strain 8.09 %,
Temperature 23.0 °C		6279 psi
@Strain 8.09 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.37 MPa
@Strain 46.78 %,
Temperature 23.0 °C		6290 psi
@Strain 46.78 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 43.38 MPa
@Strain 52.13 %,
Temperature 23.0 °C		6292 psi
@Strain 52.13 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 43.43 MPa
@Strain 57.48 %,
Temperature 23.0 °C		6299 psi
@Strain 57.48 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 43.44 MPa
@Strain 41.46 %,
Temperature 23.0 °C		6300 psi
@Strain 41.46 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 43.48 MPa
@Strain 36.11 %,
Temperature 23.0 °C		6306 psi
@Strain 36.11 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 43.59 MPa
@Strain 57.02 %,
Temperature 40.0 °C		6322 psi
@Strain 57.02 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 43.64 MPa
@Strain 62.78 %,
Temperature 23.0 °C		6329 psi
@Strain 62.78 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 43.89 MPa
@Strain 68.08 %,
Temperature 23.0 °C		6366 psi
@Strain 68.08 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.0 MPa
@Strain 78.75 %,
Temperature 23.0 °C		6380 psi
@Strain 78.75 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.04 MPa
@Strain 73.43 %,
Temperature 23.0 °C		6387 psi
@Strain 73.43 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.05 MPa
@Strain 84.08 %,
Temperature 23.0 °C		6389 psi
@Strain 84.08 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.08 MPa
@Strain 298.85 %,
Temperature 90.0 °C		6393 psi
@Strain 298.85 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 44.27 MPa
@Strain 89.42 %,
Temperature 23.0 °C		6421 psi
@Strain 89.42 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.43 MPa
@Strain 100.04 %,
Temperature 23.0 °C		6444 psi
@Strain 100.04 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.44 MPa
@Strain 94.73 %,
Temperature 23.0 °C		6445 psi
@Strain 94.73 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.57 MPa
@Strain 2.07 %,
Temperature 0.000 °C		6464 psi
@Strain 2.07 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 44.92 MPa
@Strain 51.43 %,
Temperature 40.0 °C		6515 psi
@Strain 51.43 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 44.98 MPa
@Strain 2.20 %,
Temperature 23.0 °C		6524 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 45.02 MPa
@Strain 38.87 %,
Temperature 23.0 °C		6530 psi
@Strain 38.87 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 45.48 MPa
@Strain 9.63 %,
Temperature 40.0 °C		6596 psi
@Strain 9.63 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 45.59 MPa
@Strain 11.66 %,
Temperature 23.0 °C		6612 psi
@Strain 11.66 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 45.62 MPa
@Strain 46.32 %,
Temperature 40.0 °C		6617 psi
@Strain 46.32 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 45.63 MPa
@Strain 43.48 %,
Temperature 0.000 °C		6618 psi
@Strain 43.48 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 45.78 MPa
@Strain 5.85 %,
Temperature 40.0 °C		6640 psi
@Strain 5.85 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 46.11 MPa
@Strain 41.55 %,
Temperature 40.0 °C		6688 psi
@Strain 41.55 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 46.12 MPa
@Strain 13.35 %,
Temperature 40.0 °C		6689 psi
@Strain 13.35 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 46.27 MPa
@Strain 34.73 %,
Temperature 23.0 °C		6711 psi
@Strain 34.73 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.48 MPa
@Strain 37.02 %,
Temperature 40.0 °C		6741 psi
@Strain 37.02 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 46.66 MPa
@Strain 17.06 %,
Temperature 40.0 °C		6767 psi
@Strain 17.06 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 46.76 MPa
@Strain 32.72 %,
Temperature 40.0 °C		6782 psi
@Strain 32.72 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 46.94 MPa
@Strain 20.77 %,
Temperature 40.0 °C		6808 psi
@Strain 20.77 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 46.95 MPa
@Strain 28.61 %,
Temperature 40.0 °C		6810 psi
@Strain 28.61 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 47.03 MPa
@Strain 24.63 %,
Temperature 40.0 °C		6821 psi
@Strain 24.63 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 47.03 MPa
@Strain 15.26 %,
Temperature 23.0 °C		6821 psi
@Strain 15.26 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.1 MPa
@Strain 48.46 %,
Temperature 0.000 °C		6830 psi
@Strain 48.46 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 47.11 MPa
@Strain 30.68 %,
Temperature 23.0 °C		6833 psi
@Strain 30.68 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.12 MPa
@Strain 63.63 %,
Temperature 0.000 °C		6834 psi
@Strain 63.63 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 47.13 MPa
@Strain 79.14 %,
Temperature 0.000 °C		6836 psi
@Strain 79.14 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 47.16 MPa
@Strain 58.55 %,
Temperature 0.000 °C		6840 psi
@Strain 58.55 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 47.29 MPa
@Strain 53.5 %,
Temperature 0.000 °C		6859 psi
@Strain 53.5 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 47.45 MPa
@Strain 68.64 %,
Temperature 0.000 °C		6882 psi
@Strain 68.64 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 47.52 MPa
@Strain 2.06 %,
Temperature -40.0 °C		6892 psi
@Strain 2.06 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 47.58 MPa
@Strain 73.68 %,
Temperature 0.000 °C		6901 psi
@Strain 73.68 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 47.63 MPa
@Strain 26.68 %,
Temperature 23.0 °C		6908 psi
@Strain 26.68 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.72 MPa
@Strain 18.98 %,
Temperature 23.0 °C		6921 psi
@Strain 18.98 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.87 MPa
@Strain 22.78 %,
Temperature 23.0 °C		6943 psi
@Strain 22.78 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 49.7 MPa
@Strain 26.31 %,
Temperature 0.000 °C		7210 psi
@Strain 26.31 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 49.8 MPa
@Strain 10.0 %,
Temperature 23.0 °C		7220 psi
@Strain 10.0 %,
Temperature 73.4 °F		DAM; ISO 527
 50.13 MPa
@Strain 49.07 %,
Temperature -20.0 °C		7271 psi
@Strain 49.07 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 50.22 MPa
@Strain 40.87 %,
Temperature -20.0 °C		7284 psi
@Strain 40.87 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 50.28 MPa
@Strain 29.86 %,
Temperature 0.000 °C		7293 psi
@Strain 29.86 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 50.61 MPa
@Strain 40.33 %,
Temperature 0.000 °C		7340 psi
@Strain 40.33 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 50.61 MPa
@Strain 43.84 %,
Temperature 0.000 °C		7340 psi
@Strain 43.84 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 50.64 MPa
@Strain 33.34 %,
Temperature 0.000 °C		7345 psi
@Strain 33.34 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 50.73 MPa
@Strain 36.83 %,
Temperature 0.000 °C		7358 psi
@Strain 36.83 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 50.86 MPa
@Strain 47.32 %,
Temperature 0.000 °C		7377 psi
@Strain 47.32 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 50.91 MPa
@Strain 44.58 %,
Temperature -20.0 °C		7384 psi
@Strain 44.58 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 50.96 MPa
@Strain 54.64 %,
Temperature 0.000 °C		7391 psi
@Strain 54.64 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 51.08 MPa
@Strain 50.8 %,
Temperature 0.000 °C		7409 psi
@Strain 50.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 51.92 MPa
@Strain 2.46 %,
Temperature 0.000 °C		7530 psi
@Strain 2.46 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 52.11 MPa
@Strain 46.25 %,
Temperature -20.0 °C		7558 psi
@Strain 46.25 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 52.24 MPa
@Strain 29.04 %,
Temperature -20.0 °C		7577 psi
@Strain 29.04 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 52.48 MPa
@Strain 42.56 %,
Temperature -20.0 °C		7612 psi
@Strain 42.56 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 52.62 MPa
@Strain 32.42 %,
Temperature -20.0 °C		7632 psi
@Strain 32.42 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 52.65 MPa
@Strain 39.17 %,
Temperature -20.0 °C		7636 psi
@Strain 39.17 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 52.72 MPa
@Strain 35.79 %,
Temperature -20.0 °C		7646 psi
@Strain 35.79 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 52.87 MPa
@Strain 24.57 %,
Temperature 23.0 °C		7668 psi
@Strain 24.57 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 53.37 MPa
@Strain 2.52 %,
Temperature -40.0 °C		7741 psi
@Strain 2.52 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 55.6 MPa
@Strain 36.38 %,
Temperature -20.0 °C		8060 psi
@Strain 36.38 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 56.13 MPa
@Strain 19.2 %,
Temperature 23.0 °C		8141 psi
@Strain 19.2 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 56.9 MPa
@Strain 2.80 %,
Temperature -20.0 °C		8250 psi
@Strain 2.80 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 57.57 MPa
@Strain 14.18 %,
Temperature 23.0 °C		8350 psi
@Strain 14.18 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 58.6 MPa
@Strain 2.83 %,
Temperature -20.0 °C		8500 psi
@Strain 2.83 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 59.09 MPa
@Strain 9.35 %,
Temperature 23.0 °C		8570 psi
@Strain 9.35 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 59.78 MPa
@Strain 36.96 %,
Temperature 0.000 °C		8670 psi
@Strain 36.96 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.77 MPa
@Strain 4.39 %,
Temperature 0.000 °C		9104 psi
@Strain 4.39 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.47 MPa
@Strain 32.14 %,
Temperature 0.000 °C		9206 psi
@Strain 32.14 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.72 MPa
@Strain 4.75 %,
Temperature 23.0 °C		9242 psi
@Strain 4.75 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 64.46 MPa
@Strain 27.97 %,
Temperature 0.000 °C		9349 psi
@Strain 27.97 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.89 MPa
@Strain 24.39 %,
Temperature -20.0 °C		9412 psi
@Strain 24.39 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 64.92 MPa
@Strain 21.49 %,
Temperature 0.000 °C		9416 psi
@Strain 21.49 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 65.3 MPa
@Strain 24.08 %,
Temperature 0.000 °C		9470 psi
@Strain 24.08 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.39 MPa
@Strain 7.37 %,
Temperature 0.000 °C		9484 psi
@Strain 7.37 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.8 MPa
@Strain 10.52 %,
Temperature 0.000 °C		9540 psi
@Strain 10.52 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.9 MPa
@Strain 20.48 %,
Temperature 0.000 °C		9560 psi
@Strain 20.48 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.95 MPa
@Strain 13.76 %,
Temperature 0.000 °C		9565 psi
@Strain 13.76 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.99 MPa
@Strain 17.08 %,
Temperature 0.000 °C		9571 psi
@Strain 17.08 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.15 MPa
@Strain 3.24 %,
Temperature -40.0 °C		9594 psi
@Strain 3.24 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 68.11 MPa
@Strain 17.9 %,
Temperature 0.000 °C		9879 psi
@Strain 17.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 68.57 MPa
@Strain 3.50 %,
Temperature -40.0 °C		9945 psi
@Strain 3.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 69.76 MPa
@Strain 3.89 %,
Temperature 0.000 °C		10120 psi
@Strain 3.89 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 69.83 MPa
@Strain 14.6 %,
Temperature 0.000 °C		10130 psi
@Strain 14.6 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 71.42 MPa
@Strain 11.46 %,
Temperature 0.000 °C		10360 psi
@Strain 11.46 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 72.18 MPa
@Strain 31.43 %,
Temperature -20.0 °C		10470 psi
@Strain 31.43 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 72.3 MPa
@Strain 4.54 %,
Temperature -20.0 °C		10500 psi
@Strain 4.54 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 73.35 MPa
@Strain 8.49 %,
Temperature 0.000 °C		10640 psi
@Strain 8.49 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 74.18 MPa
@Strain 27.98 %,
Temperature -20.0 °C		10760 psi
@Strain 27.98 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 74.52 MPa
@Strain 20.24 %,
Temperature -20.0 °C		10810 psi
@Strain 20.24 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 75.34 MPa
@Strain 5.85 %,
Temperature 0.000 °C		10930 psi
@Strain 5.85 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.4 MPa
@Strain 24.82 %,
Temperature -20.0 °C		10900 psi
@Strain 24.82 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 76.29 MPa
@Strain 21.85 %,
Temperature -20.0 °C		11060 psi
@Strain 21.85 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 76.8 MPa
@Strain 6.60 %,
Temperature -20.0 °C		11100 psi
@Strain 6.60 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 76.92 MPa
@Strain 19.06 %,
Temperature -20.0 °C		11160 psi
@Strain 19.06 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 77.2 MPa
@Strain 16.37 %,
Temperature -20.0 °C		11200 psi
@Strain 16.37 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 77.24 MPa
@Strain 16.86 %,
Temperature -20.0 °C		11200 psi
@Strain 16.86 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 77.48 MPa
@Strain 13.8 %,
Temperature -20.0 °C		11240 psi
@Strain 13.8 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 77.7 MPa
@Strain 8.87 %,
Temperature -20.0 °C		11300 psi
@Strain 8.87 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 77.74 MPa
@Strain 11.28 %,
Temperature -20.0 °C		11280 psi
@Strain 11.28 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 78.53 MPa
@Strain 4.44 %,
Temperature -40.0 °C		11390 psi
@Strain 4.44 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 79.13 MPa
@Strain 13.7 %,
Temperature -20.0 °C		11480 psi
@Strain 13.7 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 80.51 MPa
@Strain 4.54 %,
Temperature -40.0 °C		11680 psi
@Strain 4.54 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 80.91 MPa
@Strain 10.78 %,
Temperature -20.0 °C		11740 psi
@Strain 10.78 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 82.2 MPa
@Strain 5.89 %,
Temperature -20.0 °C		11900 psi
@Strain 5.89 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 82.6 MPa
@Strain 8.14 %,
Temperature -20.0 °C		12000 psi
@Strain 8.14 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 84.13 MPa
@Strain 25.03 %,
Temperature -40.0 °C		12200 psi
@Strain 25.03 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 85.43 MPa
@Strain 29.61 %,
Temperature -40.0 °C		12390 psi
@Strain 29.61 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 86.37 MPa
@Strain 5.77 %,
Temperature -40.0 °C		12530 psi
@Strain 5.77 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 87.14 MPa
@Strain 21.35 %,
Temperature -40.0 °C		12640 psi
@Strain 21.35 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 87.31 MPa
@Strain 25.86 %,
Temperature -40.0 °C		12660 psi
@Strain 25.86 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 88.8 MPa
@Strain 5.71 %,
Temperature -40.0 °C		12900 psi
@Strain 5.71 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 89.44 MPa
@Strain 23.28 %,
Temperature -40.0 °C		12970 psi
@Strain 23.28 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 89.59 MPa
@Strain 18.83 %,
Temperature -40.0 °C		12990 psi
@Strain 18.83 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 90.38 MPa
@Strain 7.30 %,
Temperature -40.0 °C		13110 psi
@Strain 7.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 90.68 MPa
@Strain 20.93 %,
Temperature -40.0 °C		13150 psi
@Strain 20.93 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 91.05 MPa
@Strain 16.49 %,
Temperature -40.0 °C		13210 psi
@Strain 16.49 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.54 MPa
@Strain 18.71 %,
Temperature -40.0 °C		13280 psi
@Strain 18.71 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 91.95 MPa
@Strain 9.00 %,
Temperature -40.0 °C		13340 psi
@Strain 9.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 92.11 MPa
@Strain 16.62 %,
Temperature -40.0 °C		13360 psi
@Strain 16.62 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 92.32 MPa
@Strain 10.82 %,
Temperature -40.0 °C		13390 psi
@Strain 10.82 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 92.33 MPa
@Strain 14.36 %,
Temperature -40.0 °C		13390 psi
@Strain 14.36 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 92.4 MPa
@Strain 14.63 %,
Temperature -40.0 °C		13400 psi
@Strain 14.63 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 92.44 MPa
@Strain 12.65 %,
Temperature -40.0 °C		13410 psi
@Strain 12.65 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 93.2 MPa
@Strain 7.10 %,
Temperature -40.0 °C		13500 psi
@Strain 7.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.43 MPa
@Strain 12.34 %,
Temperature -40.0 °C		13550 psi
@Strain 12.34 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 94.33 MPa
@Strain 10.44 %,
Temperature -40.0 °C		13680 psi
@Strain 10.44 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 94.56 MPa
@Strain 8.71 %,
Temperature -40.0 °C		13710 psi
@Strain 8.71 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Tensile Strength, Yield 58.0 MPa
@Temperature 23.0 °C		8410 psi
@Temperature 73.4 °F		DAM; ISO 527
Elongation at Break 230 %
@Temperature 23.0 °C		230 %
@Temperature 73.4 °F		DAM; ISO 527
Elongation at Yield 5.0 %
@Temperature 23.0 °C		5.0 %
@Temperature 73.4 °F		DAM; ISO 527
Tensile Modulus  0.226 GPa
@Temperature 150 °C		32.8 ksi
@Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.255 GPa
@Temperature 150 °C		37.0 ksi
@Temperature 302 °F		DAM; ISO 11403-1/-2
 0.302 GPa
@Temperature 120 °C		43.8 ksi
@Temperature 248 °F		50%RH; ISO 11403-1/-2
 0.332 GPa
@Temperature 120 °C		48.2 ksi
@Temperature 248 °F		DAM; ISO 11403-1/-2
 0.381 GPa
@Temperature 90.0 °C		55.3 ksi
@Temperature 194 °F		50%RH; ISO 11403-1/-2
 0.420 GPa
@Temperature 90.0 °C		60.9 ksi
@Temperature 194 °F		DAM; ISO 11403-1/-2
 0.495 GPa
@Temperature 60.0 °C		71.8 ksi
@Temperature 140 °F		50%RH; ISO 11403-1/-2
 0.602 GPa
@Temperature 60.0 °C		87.3 ksi
@Temperature 140 °F		DAM; ISO 11403-1/-2
 0.762 GPa
@Temperature 40.0 °C		111 ksi
@Temperature 104 °F		50%RH; ISO 11403-1/-2
 1.341 GPa
@Temperature 23.0 °C		194.5 ksi
@Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 1.602 GPa
@Temperature 40.0 °C		232.4 ksi
@Temperature 104 °F		DAM; ISO 11403-1/-2
 2.00 GPa
@Temperature 23.0 °C		290 ksi
@Temperature 73.4 °F		DAM; ISO 527
 2.114 GPa
@Temperature 23.0 °C		306.6 ksi
@Temperature 73.4 °F		DAM; ISO 11403-1/-2
 2.308 GPa
@Temperature 0.000 °C		334.7 ksi
@Temperature 32.0 °F		DAM; ISO 11403-1/-2
 2.338 GPa
@Temperature 0.000 °C		339.1 ksi
@Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 2.369 GPa
@Temperature -20.0 °C		343.6 ksi
@Temperature -4.00 °F		DAM; ISO 11403-1/-2
 2.419 GPa
@Temperature -20.0 °C		350.8 ksi
@Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 2.569 GPa
@Temperature -40.0 °C		372.6 ksi
@Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 2.579 GPa
@Temperature -40.0 °C		374.1 ksi
@Temperature -40.0 °F		DAM; ISO 11403-1/-2
Charpy Impact, Notched  0.680 J/cm²
@Temperature 23.0 °C		3.24 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 0.870 J/cm²
@Temperature -40.0 °C		4.14 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 
Processing PropertiesMetricEnglishComments
Melt Temperature 223 °C433 °F10°C/min; DAM; ISO 11357-1/-3
 245 °C473 °FDAM; Optimum; Extrusion
 240 - 255 °C464 - 491 °FDAM; Extrusion
 250 °C482 °FDAM; Optimum; Injection Molding
 230 - 290 °C446 - 554 °FDAM; Injection Molding
Mold Temperature 70.0 °C158 °FDAM; optimum; Injection Molding
 50.0 - 90.0 °C122 - 194 °FDAM; Injection Molding
Drying Temperature 80.0 °C176 °FDAM; Extrusion
 80.0 °C176 °FDAM; Injection Molding
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM; Injection Molding
 3.00 - 4.00 hour3.00 - 4.00 hourDAM; Extrusion
Moisture Content <= 0.050 %<= 0.050 %DAM; Extrusion
 <= 0.10 %<= 0.10 %DAM; Injection Molding
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesChemical Resistance, GoodDAM
 Dimensional Stability, GoodDAM
 Flexibility, GoodDAM
 Moisture Absorption, LowDAM
 Renewable Resource ContentDAM
 Viscosity, LowDAM
 Viscosity, MediumDAM
FormsPelletsDAM
GenericPA610DAM
Material StatusPreliminary DataDAM
Part Marking Code>PA610<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA610DAM
Processing MethodExtrusionDAM
Product CategoryExtrusion ResinsDAM
 Renewably Sourced ResinsDAM
 Unreinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA610ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
UsesAutomotive ApplicationsDAM
 Cable JacketingDAM
 Consumer ApplicationsDAM
 FilamentsDAM
 HoseDAM
 Industrial ApplicationsDAM
 TubingDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47876.html

免责声明: 本文 DuPont Performance Polymers Zytel® RS LC3060 NC010 Nylon 610 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4