- 密度 [g/cm3]: 1.05
- 弯曲模量 [MPa]: 0.720
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183/A | ||
| Viscosity | 700 cP @Shear Rate 1000 1/s, Temperature 230 °C | 700 cP @Shear Rate 1000 1/s, Temperature 446 °F | |||
| 1000 cP @Shear Rate 100 1/s, Temperature 230 °C | 1000 cP @Shear Rate 100 1/s, Temperature 446 °F | ||||
| 5000 cP @Shear Rate 10.0 1/s, Temperature 230 °C | 5000 cP @Shear Rate 10.0 1/s, Temperature 446 °F | ||||
| Linear Mold Shrinkage | 0.0104 cm/cm | 0.0104 in/in | Isotropy | ||
| Linear Mold Shrinkage, Flow | 0.0242 cm/cm | 0.0242 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0233 cm/cm | 0.0233 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 Type 1A | ||
| Tensile Stress | 12.0 MPa @Strain 100 %, Temperature 150 °C | 1740 psi @Strain 100 %, Temperature 302 °F | |||
| 12.0 MPa @Strain 20.0 %, Temperature 150 °C | 1740 psi @Strain 20.0 %, Temperature 302 °F | ||||
| 15.0 MPa @Strain 160 %, Temperature 150 °C | 2180 psi @Strain 160 %, Temperature 302 °F | ||||
| 15.0 MPa @Strain 20.0 %, Temperature 135 °C | 2180 psi @Strain 20.0 %, Temperature 275 °F | ||||
| 16.0 MPa @Strain 100 %, Temperature 135 °C | 2320 psi @Strain 100 %, Temperature 275 °F | ||||
| 20.0 MPa @Strain 160 %, Temperature 135 °C | 2900 psi @Strain 160 %, Temperature 275 °F | ||||
| 23.0 MPa @Strain 20.0 %, Temperature 80.0 °C | 3340 psi @Strain 20.0 %, Temperature 176 °F | ||||
| 27.0 MPa @Strain 100 %, Temperature 80.0 °C | 3920 psi @Strain 100 %, Temperature 176 °F | ||||
| 30.0 MPa @Strain 160 %, Temperature 80.0 °C | 4350 psi @Strain 160 %, Temperature 176 °F | ||||
| 40.0 MPa @Strain 20.0 %, Temperature 23.0 °C | 5800 psi @Strain 20.0 %, Temperature 73.4 °F | ||||
| 41.0 MPa @Strain 100 %, Temperature 23.0 °C | 5950 psi @Strain 100 %, Temperature 73.4 °F | ||||
| 43.0 MPa @Strain 160 %, Temperature 23.0 °C | 6240 psi @Strain 160 %, Temperature 73.4 °F | ||||
| Elongation at Break | 215 % | 215 % | ISO 527 Type 1A | ||
| Tensile Modulus | 0.890 GPa | 129 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 33.0 MPa | 4790 psi | ISO 178 | ||
| Flexural Modulus | 0.720 GPa | 104 ksi | ISO 178 | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 2.50 J/cm² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Flammability, UL94 | HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ISO 1210 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ISO 1210 | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ISO 1210 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 200 - 220 °C | 392 - 428 °F | |||
| Melt Temperature | 215 °C | 419 °F | ISO 11357 | ||
| Drying Temperature | 80.0 °C @Time 28800 sec | 176 °F @Time 8.00 hour | dew point -35°C | ||
| Moisture Content | <= 0.10 % | <= 0.10 % | |||
| Descriptive Properties | |||||
| Compression Zone | 210-230°C | ||||