- 密度 [g/cm3]: 1.05
- 吸水率 [%]: 1.9
- 弯曲模量 [MPa]: 0.570
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183/A |
| Water Absorption | 1.9 % | 1.9 % | at saturation; ISO 62 |
| 0.65 % @Temperature 23.0 °C, Time 86400 sec | 0.65 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527 Type 1A |
| Elongation at Break | 215 % | 215 % | ISO 527 Type 1A |
| Tensile Modulus | 0.830 GPa | 120 ksi | ISO 527 Type 1A |
| Flexural Strength | 25.0 MPa | 3630 psi | ISO 178 |
| Flexural Modulus | 0.570 GPa | 82.7 ksi | ISO 178 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.350 J/cm² @Temperature -30.0 °C | 1.67 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 5.50 J/cm² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Processing Properties | Metric | English | Comments |
| Front Barrel Temperature | 215 - 235 °C | 419 - 455 °F | |
| Die Temperature | 210 - 230 °C | 410 - 446 °F | |
| Melt Temperature | 215 °C | 419 °F | ISO 11357 |
| Moisture Content | <= 0.10 % | <= 0.10 % | |