- 密度 [g/cm3]: 1.41
- 缺口冲击强度: 1.38
- 弯曲模量 [MPa]: 10.78
- 热变形温度 [℃]: 219.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 171 MPa | 24800 psi | ASTM D638 |
| 183 MPa | 26500 psi | ISO 527 | |
| Elongation at Break | 3.3 % | 3.3 % | ASTM D638 |
| Tensile Modulus | 12.42 GPa | 1801 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
| Flexural Modulus | 10.78 GPa | 1564 ksi | ISO 178 |
| 10.79 GPa | 1565 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.38 J/cm | 2.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.21 J/cm | 21.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C @Thickness 3.20 mm | 426 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 207 °C @Thickness 3.20 mm | 405 °F @Thickness 0.126 in | unannealed; ASTM D648 | |