- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 3.57
- 弯曲模量 [MPa]: 7.03
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec | 0.0010 - 0.0030 in/in @Time 24.0 hour | ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec | 0.0010 - 0.0030 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.011 cm/cm @Time 86400 sec | 0.0090 - 0.011 in/in @Time 24.0 hour | ASTM D955 |
| 0.0090 - 0.011 cm/cm @Time 86400 sec | 0.0090 - 0.011 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 134 MPa | 19400 psi | ISO 527 |
| 139 MPa | 20200 psi | ASTM D638 | |
| Elongation at Break | 3.4 % | 3.4 % | ASTM D638 |
| 3.6 % | 3.6 % | ISO 527 | |
| Tensile Modulus | 7.88 GPa | 1140 ksi | 1 mm/min; ISO 527 |
| 8.48 GPa | 1230 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| 208 MPa | 30200 psi | ISO 178 | |
| Flexural Modulus | 7.03 GPa | 1020 ksi | ASTM D790 |
| 7.25 GPa | 1050 ksi | ISO 178 | |
| Izod Impact, Notched | 3.57 J/cm | 6.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.58 J/cm | 21.69 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 73.0 kJ/m² | 34.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J | 6.64 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C | 17.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 32.2 µm/m-°C @Temperature -40.0 - 40.0 °C | 17.9 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 88.2 µm/m-°C @Temperature -40.0 - 40.0 °C | 49.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 88.2 µm/m-°C @Temperature -40.0 - 40.0 °C | 49.0 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 208 °C @Thickness 3.20 mm | 406 °F @Thickness 0.126 in | unannealed; ASTM D648 | |