- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 1.33
- 弯曲模量 [MPa]: 14.06
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 195 MPa | 28300 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 17.16 GPa | 2489 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 289 MPa | 41900 psi | ASTM D790 |
| Flexural Modulus | 14.06 GPa | 2039 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.14 J/cm | 19.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C @Thickness 3.20 mm | 414 °F @Thickness 0.126 in | unannealed; ASTM D648 |