- 密度 [g/cm3]: 1.44
- 缺口冲击强度: 13.0
- 断裂伸长率 [%]: 180
- 弯曲模量 [MPa]: 6.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 123 MPa | 17800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.6 % | 3.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.40 GPa | 1220 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 180 MPa | 26100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m² | 30.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.70 | 0.70 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 30.2 x 10-8 mm³/N-M | 15.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 15.0 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 107 µm/m-°C @Temperature 23.0 - 60.0 °C | 59.4 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |