- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 1.8
- 缺口冲击强度: 1.23
- 拉伸强度 [MPa]: 100.0
- 弯曲模量 [MPa]: 2.65
- 硬度: 115.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Water Absorption | 1.8 % @Time 86400 sec | 1.8 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Thickness 3.17 mm | 0.010 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 2.65 GPa | 385 ksi | ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm @Thickness 3.17 mm | 2.30 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.2 µm/m-°C | 39.0 µin/in-°F | ASTM D696 |
| Melting Point | 110 °C | 230 °F | |
| Maximum Service Temperature, Inert | 133 °C | 272 °F | ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Unannealed; ASTM D648 |