- 密度 [g/cm3]: 1.55
- 吸水率 [%]: 0.17
- 缺口冲击强度: 1.07
- 拉伸强度 [MPa]: 234.0
- 弯曲模量 [MPa]: 13.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ASTM D792 |
| Water Absorption | 0.17 % @Time 86400 sec | 0.17 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.17 mm | 0.0020 in/in @Thickness 0.125 in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm @Thickness 3.17 mm | 0.0030 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 234 MPa | 34000 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Flexural Strength | 338 MPa | 49000 psi | ASTM D790 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm | 2.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 8.00e+15 ohm-cm | 8.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 23.6 kV/mm | 600 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 34.2 µm/m-°C | 19.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 302 °C | 575 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |