- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.14
- 缺口冲击强度: 0.427
- 拉伸强度 [MPa]: 103.0
- 断裂伸长率 [%]: 200
- 弯曲模量 [MPa]: 6.89
- 硬度: 126.0
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Water Absorption | 0.14 % @Time 86400 sec | 0.14 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 3.17 mm | 0.0080 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 126 | 126 | ASTM D785 |
| Tensile Strength, Yield | 103 MPa | 15000 psi | ASTM D638 |
| Elongation at Yield | 1.5 % | 1.5 % | ASTM D638 |
| Flexural Yield Strength | 200 MPa | 29000 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm | 0.800 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 43.2 µm/m-°C | 24.0 µin/in-°F | ASTM D696 |
| Maximum Service Temperature, Air | 141 °C | 285 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 159 °C | 318 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |