- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 0.25
- 缺口冲击强度: 0.641
- 拉伸强度 [MPa]: 110.0
- 断裂伸长率 [%]: 160
- 弯曲模量 [MPa]: 7.79
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Water Absorption | 0.25 % @Time 86400 sec | 0.25 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.17 mm | 0.0050 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Yield Strength | 160 MPa | 23200 psi | ASTM D790 |
| Flexural Modulus | 7.79 GPa | 1130 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 3.17 mm | 1.20 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 34.2 µm/m-°C | 19.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |