- 密度 [g/cm3]: 1.17
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | DIN 53479 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 49 | 49 | DIN 53505 | ||
| Tensile Strength at Break | 5.10 MPa | 740 psi | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504/ ISO 37 | ||
| Elongation at Break | 727 % | 727 % | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504/ ISO 37 | ||
| Tear Strength | 20.0 kN/m | 114 pli | ISO 34-1 method B (b) | ||
| Compression Set | 15 % @Temperature 23.0 °C, Time 259000 sec | 15 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 60 % @Temperature 70.0 °C, Time 79200 sec | 60 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 72 % @Temperature -25.0 °C, Time 79200 sec | 72 % @Temperature -13.0 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | |||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 140 - 160 °C | 284 - 320 °F | for 30-55 Shore A | ||
| 160 - 180 °C | 320 - 356 °F | for 60-90 Shore A | |||
| Descriptive Properties | |||||
| Color | Natural | ||||