- 密度 [g/cm3]: 1.16
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | DIN 53479 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 90 | 90 | DIN EN ISO 1183-1:2004 | ||
| Tensile Strength at Break | 6.00 MPa | 870 psi | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504/ ISO 37 | ||
| Elongation at Break | 500 % | 500 % | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504/ ISO 37 | ||
| Tear Strength | 22.0 kN/m | 126 pli | ISO 34-1 method B (b) | ||
| Compression Set | 35 % @Temperature 23.0 °C, Time 259000 sec | 35 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 85 % @Temperature 70.0 °C, Time 79200 sec | 85 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 90 % @Temperature 100 °C, Time 79200 sec | 90 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| 90 % @Temperature -25.0 °C, Time 79200 sec | 90 % @Temperature -13.0 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | |||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 160 - 180 °C | 320 - 356 °F | for 30-55 Shore A | ||
| 160 - 180 °C | 320 - 356 °F | for 60-90 Shore A | |||
| Descriptive Properties | |||||
| Color | Black | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.