- 密度 [g/cm3]: 1.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 50 | 50 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 3.30 MPa | 479 psi | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Elongation at Break | 430 % | 430 % | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Peel Strength | 5.00 - 10.0 kN/m | 28.5 - 57.1 pli | to ABS, depending on the hardness; Renault test D41 1916 | ||
| 6.00 - 18.0 kN/m | 34.2 - 103 pli | to PC/ABS, depending on the hardness; Renault test D41 1916 | |||
| 7.00 - 18.0 kN/m | 39.9 - 103 pli | to PC, depending on the hardness; Renault test D41 1916 | |||
| Graves Tear Strength | 11.0 kN/m | 62.8 pli | DIN ISO 34-1 Method B (b) | ||
| Compression Set | 13 % @Temperature 23.0 °C, Time 259000 sec | 13 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 44 % @Temperature 70.0 °C, Time 79200 sec | 44 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 79 % @Temperature 120 °C, Time 79200 sec | 79 % @Temperature 248 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Flammability, UL94 | HB | HB | |||
| Processing Properties | Metric | English | Comments | ||
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |||
| Drying Temperature | 60.0 - 80.0 °C @Time 7200 - 14400 sec | 140 - 176 °F @Time 2.00 - 4.00 hour | Pre drying | ||
| Descriptive Properties | |||||
| Color | Black | ||||