- 密度 [g/cm3]: 1.15
- 脆化温度 [℃]: -33.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50.0 | 50.0 | ASTM D2240 |
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D412 |
| Tensile Stress | 14.0 MPa @Strain 100 % | 2030 psi @Strain 100 % | ASTM D412 |
| 27.0 MPa @Strain 300 % | 3920 psi @Strain 300 % | ASTM D412 | |
| Elongation at Break | 450 % | 450 % | ASTM D412 |
| Tear Strength | 170 kN/m | 971 pli | Die C; ASTM D412 |
| Taber Abrasion, mg/1000 Cycles | 50.0 | 50.0 | ASTM D1044 |
| Abrasion | 23.0 | 23.0 | mm3; DIN 53516 |
| Compression Set | 33.0 % @Temperature 22.8 °C, Time 79200 sec | 33.0 % @Temperature 73.0 °F, Time 22.0 hour | ASTM D3995B |
| 46.0 % @Temperature 70.0 °C, Time 259000 sec | 46.0 % @Temperature 158 °F, Time 72.0 hour | ASTM D3995B | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 130 °C | 266 °F | ASTM D1525 |
| Brittleness Temperature | -33.0 °C | -27.4 °F | ASTM D746 |
| Flammability, UL94 | HB @Thickness 1.00 mm | HB @Thickness 0.0394 in | |
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 210 °C | 410 °F | Gate Temperature; Extrusion |
| 210 - 220 °C | 410 - 428 °F | Injection | |
| Rear Barrel Temperature | 195 °C | 383 °F | Injection |
| Middle Barrel Temperature | 205 °C | 401 °F | Injection |
| Front Barrel Temperature | 215 °C | 419 °F | Injection |
| Nozzle Temperature | 210 - 220 °C | 410 - 428 °F | Injection |
| Zone 1 | 195 °C | 383 °F | Extrusion |
| Zone 2 | 205 °C | 401 °F | Extrusion |
| Zone 3 | 215 °C | 419 °F | Extrusion |
| Die Temperature | 220 °C | 428 °F | Extrusion |
| Mold Temperature | 25.0 - 60.0 °C | 77.0 - 140 °F | Injection |
| Injection Velocity | >= 10.0 mm/sec | >= 0.394 in/sec | Injection |
| Drying Temperature | 90.0 °C | 194 °F | Injection |
| 90.0 °C | 194 °F | Extrusion | |
| Dry Time | 4.00 hour | 4.00 hour | Injection |
| 4.00 hour | 4.00 hour | Extrusion | |
| Back Pressure | 0.300 - 1.30 MPa | 43.5 - 189 psi | Injection |
| Clamp Pressure | 40.0 - 70.3 MPa | 5800 - 10200 psi | Injection |
| Screw Speed | 60.0 - 200 rpm | 60.0 - 200 rpm | Injection |