- 弯曲强度 [MPa]: 10.8
- 脆化温度 [℃]: -43.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | 23°C; ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 45 | 45 | .12 in; ASTM D2240 | ||
| 50 | 50 | 302°F, 168 hr; ASTM D573 | |||
| Tensile Strength at Break | 13.350 MPa | 1936.3 psi | 212°F, 70 hr, in IRM Oil; ASTM D471 | ||
| 16.538 MPa | 2398.7 psi | 302°F, 168 hr; ASTM D573 | |||
| 19.9 MPa | 2890 psi | Across Flow; ASTM D412 | |||
| Tensile Strength, Ultimate | 10.8 MPa | 1570 psi | Across Flow; ASTM D412 | ||
| Elongation at Break | 412 % | 412 % | 212°F, 70 hr, in IRM Oil; ASTM D471 | ||
| 525 % | 525 % | 302°F, 168 hr; ASTM D573 | |||
| 750 % | 750 % | Across Flow; ASTM D412 | |||
| Tear Strength | 88.0 kN/m | 502 pli | 73°F, Die C; ASTM D624 | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | -43.9 °C | -47.0 °F | ASTM 746 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 175 - 230 °C | 347 - 446 °F | |||
| Rear Barrel Temperature | 188 °C | 370 °F | |||
| Middle Barrel Temperature | 191 °C | 375 °F | |||
| Front Barrel Temperature | 199 °C | 390 °F | |||
| Nozzle Temperature | 199 °C | 390 °F | |||
| Die Temperature | 221 °C | 430 °F | Extrusion | ||
| Melt Temperature | 177 - 216 °C | 350 - 420 °F | Extrusion | ||
| 204 °C | 400 °F | ||||
| Mold Temperature | 10.0 - 51.7 °C | 50.0 - 125 °F | Processing | ||
| Drying Temperature | 82.2 °C | 180 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| Moisture Content | 0.080 % | 0.080 % | |||
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | Processing | ||
| 5.00 - 20.0 MPa | 725 - 2900 psi | Extrusion | |||
| Clamp Pressure | 41.4 - 68.9 MPa | 6000 - 10000 psi | |||
| Vent Depth | 0.00254 cm | 0.00100 in | |||
| Cushion | 0.317 - 0.635 cm | 0.125 - 0.250 in | |||
| Screw Speed | 100 - 200 rpm | 100 - 200 rpm | |||
| Descriptive Properties | |||||
| Color | Natural Color | ||||
| Form | Pellets | ||||
| Injection Rate | Fast | ||||
| Maximum Regrind % | 20 | ||||
| Screw Compression Ratio | 2:1 - 2.5:1 | ||||
| Screw L/D Ratio | 16:1 - 20:1 | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.