- 密度 [g/cm3]: 0.97
- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | ISO 2781 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50.0 | 50.0 | ISO 868 |
| Tensile Strength at Break | 5.40 MPa | 783 psi | ISO 37 |
| Tensile Stress | 1.60 MPa @Strain 100 % | 232 psi @Strain 100 % | ISO 37 |
| 2.70 MPa @Strain 300 % | 392 psi @Strain 300 % | ISO 37 | |
| Elongation at Break | 550 % | 550 % | ISO 37 |
| Tear Strength | 28.0 kN/m | 160 pli | ISO 34-1 |
| Compression Set | 34.0 % @Temperature 70.0 °C, Time 79200 sec | 34.0 % @Temperature 158 °F, Time 22.0 hour | ASTM D3995B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -60.0 °C | -76.0 °F | ASTM D746 |
| Flammability, UL94 | HB @Thickness 1.00 mm | HB @Thickness 0.0394 in | |
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||