- 密度 [g/cm3]: 0.94
- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ISO 2781 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 92.0 | 92.0 | ISO 868 |
| Hardness, Shore D | 40.0 | 40.0 | ISO 868 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 37 |
| Tensile Stress | 8.00 MPa @Strain 100 % | 1160 psi @Strain 100 % | ISO 37 |
| 10.8 MPa @Strain 300 % | 1570 psi @Strain 300 % | ISO 37 | |
| Elongation at Break | 500 % | 500 % | ISO 37 |
| Tear Strength | 87.7 kN/m | 500 pli | ISO 34-1 |
| Compression Set | 38.0 % @Temperature 70.0 °C, Time 79200 sec | 38.0 % @Temperature 158 °F, Time 22.0 hour | ASTM D3995B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -60.0 °C | -76.0 °F | ASTM D746 |
| Flammability, UL94 | HB @Thickness 1.00 mm | HB @Thickness 0.0394 in | |
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||