- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 0.45
- 拉伸强度 [MPa]: 110.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | in normal climate 23°C/50%RH; ISO 62 |
| Water Absorption at Saturation | 0.45 % | 0.45 % | in water at 23°C; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 105 @Thickness 10.0 mm | 105 @Thickness 0.394 in | ISO 2039-2 |
| Ball Indentation Hardness | 230 MPa | 33400 psi | value at 30 sec.; ISO 2039-1 |
| Tensile Strength, Yield | 110 MPa | 16000 psi | v = 50 mm/min; ISO 527-2 |
| Elongation at Break | 20 % | 20 % | ISO 527-2 |
| Tensile Modulus | 4.40 GPa | 638 ksi | ISO 527-2 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 100 Hz | 3.2 @Frequency 100 Hz | IEC 60250 |
| 3.6 @Frequency 1e+6 Hz | 3.6 @Frequency 1e+6 Hz | IEC 60250 | |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | in transformer oil; IEC 60243-1 |
| Dissipation Factor | 0.0010 @Frequency 100 Hz | 0.0010 @Frequency 100 Hz | IEC 60250 |
| 0.0020 @Frequency 1e+6 Hz | 0.0020 @Frequency 1e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 µm/m-°C @Temperature 20.0 °C | 27.8 µin/in-°F @Temperature 68.0 °F | ISO 11359 |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | |
| Melting Point | 340 °C | 644 °F | 10K/min; ISO 3146 |
| Maximum Service Temperature, Air | 250 °C | 482 °F | Long Term |
| 310 °C | 590 °F | Short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ISO 75-2 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |
| V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | ||