- 缺口冲击强度: 0.75
- 弯曲模量 [MPa]: 27.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0030 cm/cm @Time 86400 sec | 0.0015 - 0.0030 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.014 cm/cm @Time 86400 sec | 0.0070 - 0.014 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 314 MPa | 45500 psi | Type I, 5 mm/min; ASTM D638 |
| 319 MPa | 46300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 31.7 GPa | 4600 ksi | 5 mm/min; ASTM D638 |
| 35.32 GPa | 5123 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 457 MPa | 66300 psi | ISO 178 |
| 477 MPa | 69200 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 27.1 GPa | 3930 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 27.23 GPa | 3949 ksi | 2 mm/min; ISO 178 | |
| Poissons Ratio | 0.44 | 0.44 | ASTM E 132 |
| Shear Modulus | 4.756 GPa | 689.8 ksi | ASTM C273 |
| Shear Strength | 119 MPa | 17300 psi | ASTM C273 |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.36 J/cm | 17.5 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C | 4.43 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1000 - 10000 ohm | 1000 - 10000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 5.00 µm/m-°C @Temperature -40.0 - 150 °C | 2.78 µin/in-°F @Temperature -40.0 - 302 °F | ASTM E 831 |
| CTE, linear, Transverse to Flow | 30.0 µm/m-°C @Temperature -40.0 - 150 °C | 16.7 µin/in-°F @Temperature -40.0 - 302 °F | ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 332 °C @Thickness 3.20 mm | 630 °F @Thickness 0.126 in | unannealed; ASTM D648 |