- 缺口冲击强度: 0.82
- 弯曲模量 [MPa]: 33.82
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0030 cm/cm @Time 86400 sec | 0.0015 - 0.0030 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.014 cm/cm @Time 86400 sec | 0.0070 - 0.014 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 321 MPa | 46600 psi | 5 mm/min; ISO 527 |
| 330 MPa | 47900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 40.42 GPa | 5862 ksi | 1 mm/min; ISO 527 |
| 41.48 GPa | 6016 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 460 MPa | 66700 psi | ISO 178 |
| 492 MPa | 71400 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 33.82 GPa | 4905 ksi | 2 mm/min; ISO 178 |
| 35.2 GPa | 5110 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Compressive Strength | 215 MPa | 31200 psi | SABIC Method |
| Poissons Ratio | 0.47 | 0.47 | ASTM E 132 |
| Shear Modulus | 5.003 GPa | 725.6 ksi | ASTM C273 |
| Shear Strength | 126 MPa | 18300 psi | ASTM C273 |
| Izod Impact, Notched | 0.820 J/cm | 1.54 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.63 J/cm | 16.2 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C | 5.16 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 335 °C @Thickness 3.20 mm | 635 °F @Thickness 0.126 in | unannealed; ASTM D648 |