- 缺口冲击强度: 0.93
- 弯曲模量 [MPa]: 29.65
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ASTM D792 |
| Moisture Absorption | 0.410 % | 0.410 % | 50% RH, 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 280 MPa | 40600 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.3 % | 1.3 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 41.5 GPa | 6020 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 424 MPa | 61500 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 29.65 GPa | 4300 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.930 J/cm | 1.74 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.28 J/cm | 15.5 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 332 °C @Thickness 3.20 mm | 630 °F @Thickness 0.126 in | unannealed; ASTM D648 |