- 密度 [g/cm3]: 1.37
- 缺口冲击强度: 0.58
- 拉伸强度 [MPa]: 120.0
- 断裂伸长率 [%]: 203
- 弯曲模量 [MPa]: 5.66
- 热变形温度 [℃]: 285.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0700 % | 0.0700 % | 50% RH, 24 hrs; ASTM D570 |
| 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec | 0.0030 - 0.0060 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Time 86400 sec | 0.0050 - 0.0080 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
| 122 MPa | 17700 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 120 MPa | 17400 psi | Type I, 5 mm/min; ASTM D638 |
| 125 MPa | 18100 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| 4.2 % | 4.2 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 3.3 % | 3.3 % | Type I, 5 mm/min; ASTM D638 |
| 3.4 % | 3.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.08 GPa | 882 ksi | 5 mm/min; ASTM D638 |
| 6.49 GPa | 941 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 203 MPa | 29400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.66 GPa | 821 ksi | 2 mm/min; ISO 178 |
| 6.01 GPa | 872 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.60 J/cm | 16.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 49.0 kJ/m² | 23.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C | 5.90 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 35.2 µm/m-°C @Temperature -30.0 - 30.0 °C | 19.6 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 43.5 µm/m-°C @Temperature -30.0 - 30.0 °C | 24.2 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 285 °C | 545 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 326 °C @Thickness 3.20 mm | 619 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 171 °C | 340 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 169 °C @Thickness 3.20 mm | 336 °F @Thickness 0.126 in | unannealed; ASTM D648 | |