- 密度 [g/cm3]: 1.35
- 缺口冲击强度: 6.0
- 拉伸强度 [MPa]: 97.0
- 断裂伸长率 [%]: 162
- 弯曲模量 [MPa]: 4.70
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.3 % | 3.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.70 GPa | 827 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 162 MPa | 23500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.70 GPa | 682 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 19.4 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 27.8 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 159 °C | 318 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |