- 密度 [g/cm3]: 1.39
- 缺口冲击强度: 0.53
- 拉伸强度 [MPa]: 125.0
- 弯曲模量 [MPa]: 7.00
- 热变形温度 [℃]: 325.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D 792 |
| 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0079 cm/cm @Time 86400 sec | 0.0079 in/in @Time 24.0 hour | ISO 294 |
| 0.0080 cm/cm @Time 86400 sec | 0.0080 in/in @Time 24.0 hour | ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Time 86400 sec | 0.010 in/in @Time 24.0 hour | ASTM D 955 |
| 0.010 cm/cm @Time 86400 sec | 0.010 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527 |
| 136 MPa | 19700 psi | ASTM D 638 | |
| Tensile Strength, Yield | 125 MPa | 18100 psi | ISO 527 |
| 136 MPa | 19700 psi | ASTM D 638 | |
| Elongation at Break | 2.4 % | 2.4 % | ISO 527 |
| 3.1 % | 3.1 % | ASTM D 638 | |
| Elongation at Yield | 2.4 % | 2.4 % | ISO 527 |
| 3.0 % | 3.0 % | ASTM D 638 | |
| Tensile Modulus | 6.93 GPa | 1010 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 199 MPa | 28900 psi | ASTM D 790 |
| 209 MPa | 30300 psi | ISO 178 | |
| Flexural Modulus | 7.00 GPa | 1020 ksi | ISO 178 |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C | 0.993 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 8.54 J/cm @Temperature 23.0 °C | 16.0 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 54.0 kJ/m² @Temperature 23.0 °C | 25.7 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| 15.0 J @Temperature 23.0 °C | 11.1 ft-lb @Temperature 73.4 °F | Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 48.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 26.7 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 48.6 µm/m-°C @Temperature -40.0 - 40.0 °C | 27.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C | 17.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 31.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 17.2 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 325 °C | 617 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 328 °C @Thickness 3.20 mm | 622 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 244 °C | 471 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 258 °C @Thickness 3.20 mm | 496 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |