- 缺口冲击强度: 10.0
- 拉伸强度 [MPa]: 350.0
- 弯曲模量 [MPa]: 36.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc @Temperature 23.0 °C | 1.44 g/cc @Temperature 73.4 °F | ISO 1183 |
| Viscosity | 330000 cP @Temperature 400 °C | 330000 cP @Temperature 752 °F | 0.5mm die; Victrex test method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 350 MPa @Temperature 23.0 °C | 50800 psi @Temperature 73.4 °F | ISO 527 |
| Elongation at Yield | 1.3 % @Temperature 23.0 °C | 1.3 % @Temperature 73.4 °F | ISO 527 |
| Tensile Modulus | 45.0 GPa @Temperature 23.0 °C | 6530 ksi @Temperature 73.4 °F | ISO 527 |
| Flexural Strength | 500 MPa @Temperature 23.0 °C | 72500 psi @Temperature 73.4 °F | ISO 178 |
| Flexural Modulus | 36.0 GPa @Temperature 23.0 °C | 5220 ksi @Temperature 73.4 °F | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | ISO 180 |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 349 °C | 660 °F | ISO 75A-f |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | >= 400 °C | >= 752 °F | |
| Middle Barrel Temperature | >= 400 °C | >= 752 °F | |
| Front Barrel Temperature | >= 400 °C | >= 752 °F | |
| Mold Temperature | 175 - 205 °C | 347 - 401 °F | |
| Drying Temperature | >= 150 °C @Time 10800 sec | >= 302 °F @Time 3.00 hour | |
| >= 160 °C @Time 7200 sec | >= 320 °F @Time 2.00 hour | ||