Victrex® PEEK 450G903 Black Polyetheretherketone, Unreinforced

Victrex® PEEK 450G903 Black Polyetheretherketone, Unreinforced 物性表: Victrex® PEEK 450G903 Black Polyetheretherketone, Unreinforced物性表及特性介绍,Victrex® PEEK 450G903 Black Polyetheretherketone, Unreinforced注塑参数详情,如需Victrex® PEEK 450G903 Black Polyetheretherketone, Unreinforced下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.26
  • 吸水率 [%]: 0.07
  • 缺口冲击强度: 6.5
  • 拉伸强度 [MPa]: 100.0
  • 弯曲模量 [MPa]: 4.10
 
Physical PropertiesMetricEnglishComments
Density 1.26 g/cc0.0455 lb/in³Amorphous; ISO 1183
 1.30 g/cc0.0470 lb/in³Crystalline; ISO 1183
Water Absorption 0.070 %
@Temperature 23.0 °C,
Time 86400 sec
0.070 %
@Temperature 73.4 °F,
Time 24.0 hour
3.2mm thick tensile bar; ISO 62-1
Water Absorption at Saturation 0.40 %
@Temperature 23.0 °C
0.40 %
@Temperature 73.4 °F
Equilibrium; by immersion; ISO 62-1
Viscosity 350000 cP
@Temperature 400 °C
350000 cP
@Temperature 752 °F
melt; ISO 11443
Linear Mold Shrinkage, Flow 0.010 cm/cm0.010 in/in360°C nozzle, 160°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.013 cm/cm0.013 in/in375°C nozzle, 180°C tool; ISO 294-4
Spiral Flow 110 cm
@Thickness 1.00 mm
43.3 in
@Thickness 0.0394 in
375°C nozzle, 180°C tool
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore D 87
@Temperature 23.0 °C
87
@Temperature 73.4 °F
ISO 868
Tensile Strength, Yield 100 MPa
@Temperature 23.0 °C
14500 psi
@Temperature 73.4 °F
ISO 527
Elongation at Break 30 %
@Temperature 23.0 °C
30 %
@Temperature 73.4 °F
ISO 527
Tensile Modulus 3.70 GPa
@Temperature 23.0 °C
537 ksi
@Temperature 73.4 °F
ISO 527
Flexural Strength  12.0 MPa
@Temperature 275 °C
1740 psi
@Temperature 527 °F
ISO 178
 17.0 MPa
@Temperature 185 °C
2470 psi
@Temperature 365 °F
ISO 178
 19.0 MPa
@Temperature 165 °C
2760 psi
@Temperature 329 °F
ISO 178
 37.0 MPa
@Temperature 150 °C
5370 psi
@Temperature 302 °F
ISO 178
 60.0 MPa
@Temperature 140 °C
8700 psi
@Temperature 284 °F
ISO 178
 85.0 MPa
@Temperature 125 °C
12300 psi
@Temperature 257 °F
ISO 178
 160 MPa
@Temperature 23.0 °C
23200 psi
@Temperature 73.4 °F
ISO 178
Flexural Modulus 4.10 GPa
@Temperature 23.0 °C
595 ksi
@Temperature 73.4 °F
ISO 178
Compressive Strength  70.0 MPa
@Temperature 120 °C
10200 psi
@Temperature 248 °F
ISO 604
 120 MPa
@Temperature 23.0 °C
17400 psi
@Temperature 73.4 °F
ISO 604
Izod Impact, Notched (ISO) 6.50 kJ/m²
@Temperature 23.0 °C
3.09 ft-lb/in²
@Temperature 73.4 °F
ISO 180/A
Izod Impact, Unnotched (ISO) NB
@Temperature 23.0 °C
NB
@Temperature 73.4 °F
ISO 180/U
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+9 ohm-cm
@Temperature 275 °C
1.00e+9 ohm-cm
@Temperature 527 °F
IEC 60093
 1.00e+15 ohm-cm
@Temperature 125 °C
1.00e+15 ohm-cm
@Temperature 257 °F
IEC 60093
 1.00e+16 ohm-cm
@Temperature 23.0 °C
1.00e+16 ohm-cm
@Temperature 73.4 °F
IEC 60093
Dielectric Strength 17.0 kV/mm
@Thickness 2.50 mm
432 kV/in
@Thickness 0.0984 in
IEC 60243-1
Comparative Tracking Index 150 V150 VIEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear  45.0 µm/m-°C
@Temperature <=143 °C
25.0 µin/in-°F
@Temperature <=289 °F
Along flow below Tg; ISO 11359
 55.0 µm/m-°C
@Temperature <=143 °C
30.6 µin/in-°F
@Temperature <=289 °F
Average below Tg; ISO 11359
 120 µm/m-°C
@Temperature >=143 °C
66.7 µin/in-°F
@Temperature >=289 °F
Along flow above Tg; ISO 11359
 140 µm/m-°C
@Temperature >=143 °C
77.8 µin/in-°F
@Temperature >=289 °F
Average above Tg; ISO 11359
Specific Heat Capacity 2.20 J/g-°C
@Temperature 23.0 °C
0.526 BTU/lb-°F
@Temperature 73.4 °F
DSC
Thermal Conductivity 0.290 W/m-K
@Temperature 23.0 °C
2.01 BTU-in/hr-ft²-°F
@Temperature 73.4 °F
ISO/CD 22007-4
Melting Point 343 °C649 °FISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 152 °C306 °FISO 75-f
Glass Transition Temp, Tg 143 °C289 °FOnset; ISO 11357
Flammability, UL94 V-0
@Thickness 1.50 mm
V-0
@Thickness 0.0591 in
Oxygen Index  24 %
@Thickness 0.400 mm
24 %
@Thickness 0.0157 in
ISO 4239
 35 %
@Thickness 3.20 mm
35 %
@Thickness 0.126 in
ISO 4239
Glow Wire Test 960 °C
@Thickness 2.00 mm
1760 °F
@Thickness 0.0787 in
IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Mold Temperature 170 - 200 °C338 - 392 °F
Drying Temperature  120 °C
@Time 18000 sec
248 °F
@Time 5.00 hour
 150 °C
@Time 10800 sec
302 °F
@Time 3.00 hour
 
Descriptive Properties
Toxicity Index0.074NES 713; CO content
 0.15NES 713; CO2 content
 0.22NES 713; Total gases

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-50372.html

免责声明: 本文 Victrex® PEEK 450G903 Black Polyetheretherketone, Unreinforced 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4