- 密度 [g/cm3]: 1.43
- 缺口冲击强度: 0.641
- 拉伸强度 [MPa]: 179.0
- 弯曲模量 [MPa]: 13.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | Method A; ASTM D792 |
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 179 MPa | 26000 psi | ASTM D638 |
| Tensile Strength, Yield | 179 MPa | 26000 psi | ASTM D638 |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 |
| Elongation at Yield | 1.7 % | 1.7 % | ASTM D638 |
| Tensile Modulus | 16.6 GPa | 2410 ksi | ASTM D638 |
| Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 3.18 mm | 1.20 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 4.91 J/cm @Thickness 3.18 mm | 9.20 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 6.60 kJ/m² | 3.14 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 34.6 kJ/m² | 16.5 ft-lb/in² | ISO 180 |
| Falling Dart Impact | 8.80 J | 6.49 ft-lb | ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.35 | 0.35 | vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894 |
| Coefficient of Friction, Static | 0.28 | 0.28 | vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894 |
| K (wear) Factor | 26.2 x 10-8 mm³/N-M | 13.0 x 10-10 in³-min/ft-lb-hr | 40psi, 50ft/min; tested in accordance with LNP WI-0687 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 299 °C | 570 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 379 - 388 °C | 714 - 730 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.10 % | 0.10 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |