- 吸水率 [%]: 0.5
- 缺口冲击强度: 7.0
- 拉伸强度 [MPa]: 89.6
- 弯曲模量 [MPa]: 4.10
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ISO 1183 | ||
| Water Absorption | 0.50 % | 0.50 % | ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 89.6 MPa | 13000 psi | ISO 527 | ||
| 114.0 MPa | 16530 psi | Extruded Rod; ISO 527 | |||
| Elongation at Break | 30 % | 30 % | ISO 527 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 | ||
| Tensile Modulus | 3.40 GPa | 493 ksi | ISO 527 | ||
| Flexural Strength | 170 MPa | 24700 psi | Extruded Rod; ISO 178 | ||
| Flexural Modulus | 4.10 GPa | 595 ksi | Extruded Rod; ISO 178 | ||
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180 Type 1B | ||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistivity per Square | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 60.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 33.3 µin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359 | ||
| Vicat Softening Point | 335 °C @Load 1.02 kg | 635 °F @Load 2.25 lb | Method A; ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 340 °C | 644 °F | DSC, Second Heating; ISO 11357 | ||
| Descriptive Properties | |||||
| Cytatoxicity | Pass | ISO-10993-5 | |||