- 缺口冲击强度: 0.267
- 弯曲模量 [MPa]: 9.38
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | Method A; ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 139 MPa | 20200 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Tensile Modulus | 9.72 GPa | 1410 ksi | ASTM D638 |
| Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 9.38 GPa | 1360 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.18 mm | 0.500 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 379 - 388 °C | 714 - 730 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.10 % | 0.10 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |