类别：热塑性聚合物；聚合物；ABS；聚碳酸酯/ ABS合金，无筋；聚碳酸酯（PC）
材料说明：概述：脉冲分机100工程树脂的设计是为了提供良好的加工性能，较高的耐热性，在室温和低温下冲击强度高。脉冲分机100工程树脂已用于汽车外饰件的应用。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
简介：
Physical Properties |
Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 | ||
| Melt Density | 1.02 g/cc | 0.0368 lb/in³ | |||
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 | ||
| Melt Flow | 1.3 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.3 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | Type I, 51 mm/min; ASTM D638 | ||
| Elongation at Break | 80 % | 80 % | Type I, 51 mm/min; ASTM D638 | ||
| Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 | ||
| Flexural Modulus | 2.24 GPa | 325 ksi | ASTM D790 | ||
| Izod Impact, Notched | 4.80 J/cm @Thickness 3.20 mm, Temperature -29.0 °C |
8.99 ft-lb/in @Thickness 0.126 in, Temperature -20.2 °F |
0.25 mm Notch Depth, Injection Molded; ASTM D256 | ||
| 6.40 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
12.0 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
0.25 mm Notch Depth, Injection Molded; ASTM D256 | |||
| Dart Drop, Total Energy | 54.2 J @Thickness 3.20 mm, Temperature 23.0 °C |
40.0 ft-lb @Thickness 0.126 in, Temperature 73.4 °F |
3.39 m/sec; ASTM D3763 | ||
| 59.9 J @Thickness 3.20 mm, Temperature -29.0 °C |
44.2 ft-lb @Thickness 0.126 in, Temperature -20.2 °F |
3.39 m/sec; ASTM D3763 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 | ||
| Specific Heat Capacity | 1.98 J/g-°C | 0.473 BTU/lb-°F | Melt; ASTM C351 | ||
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | Melt; ASTM C177 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | Unannealed; ASTM D648 | ||
| De |
|||||
| Ejection Temperature | 138°C | ||||
| No Flow Temperature | 160°C |
||||