| Styron PULSE™ 2100 LG PC/ABS Engineering Resin |
|---|
材料说明：
概述：脉冲2100lg工程树脂是专为在恶劣的应用提供最高的性能，从单件物品复杂的成分。理想的能源管理解决方案，它可以承受高温和低温、快速，重复的温度波动。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
| ysical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792; ISO 1183/B | ||
| Water Absorption | 0.15 % @Temperature 23.0 °C, Time 86400 sec |
0.15 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 | ||
| 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 | |||
| Melt Flow | 4.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 | ||
| 4.5 g/10 min @Load 3.80 kg, Temperature 260 °C |
4.5 g/10 min @Load 8.38 lb, Temperature 500 °F |
ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 53.8 MPa @Thickness 3.20 mm |
7800 psi @Thickness 0.126 in |
Injection Molded; ASTM D638 | ||
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ISO 527-2 | ||
| 53.1 MPa @Thickness 3.20 mm |
7700 psi @Thickness 0.126 in |
Injection Molded; ASTM D638 | |||
| Elongation at Break | 120 % | 120 % | ISO 527-2 | ||
| 130 % @Thickness 3.20 mm |
130 % @Thickness 0.126 in |
Injection Molded; ASTM D638 | |||
| Elongation at Yield | 4.5 % | 4.5 % | ISO 527-2 | ||
| 5.0 % @Thickness 3.20 mm |
5.0 % @Thickness 0.126 in |
Injection Molded; ASTM D638 | |||
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527-2 | ||
| 2.34 GPa @Thickness 3.20 mm |
339 ksi @Thickness 0.126 in |
Injection Molded; ASTM D638 | |||
| Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 | ||
| 80.7 MPa @Thickness 3.20 mm |
11700 psi @Thickness 0.126 in |
Injection Molded; ASTM D790 | |||
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 | ||
| 2.34 GPa @Thickness 3.20 mm |
339 ksi @Thickness 0.126 in |
Injection Molded; ASTM D790 | |||
| Izod Impact, Notched | 5.30 J/cm @Thickness 3.20 mm, Temperature -29.0 °C |
9.93 ft-lb/in @Thickness 0.126 in, Temperature -20.2 °F |
Injection Molded; ASTM D256 | ||
| 6.40 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
12.0 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
Injection Molded; ASTM D256 | |||
| Izod Impact, Notched (ISO) | 24.0 kJ/m² @Temperature -40.0 °C |
11.4 ft-lb/in² @Temperature -40.0 °F |
ISO 180 | ||
| 32.0 kJ/m² @Temperature -30.0 °C |
15.2 ft-lb/in² @Temperature -22.0 °F |
ISO 180 | |||
| 52.0 kJ/m² @Temperature 23.0 °C |
24.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |||
| Dart Drop, Total Energy | 56.5 J @Thickness 3.20 mm, Temperature 23.0 °C |
41.7 ft-lb @Thickness 0.126 in, Temperature 73.4 °F |
6.6 m/sec; ASTM D3763 | ||
| 62.1 J @Thickness 3.20 mm, Temperature -29.0 °C |
45.8 ft-lb @Thickness 0.126 in, Temperature -20.2 °F |
6.6 m/sec; ASTM D3763 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 74.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
41.1 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
Unannealed; ISO 75-2/B | ||
| 129 °C @Thickness 3.20 mm |
264 °F @Thickness 0.126 in |
Unannealed; ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
Unannealed; ISO 75-2/A | ||
| 107 °C @Thickness 3.20 mm |
225 °F @Thickness 0.126 in |
Unannealed; ASTM D648 | |||
| Vicat Softening Point | 128 °C | 262 °F | ISO 306/B50 | ||
| 142 °C | 288 °F | ISO 306/A120 | |||
| 143 °C @Load 5.10 kg |
289 °F @Load 11.2 lb |
Rate A (50°C/h); ASTM D1525 | |||
| Optical Properties | Metric | English | Comments | ||
| Gloss | 25 % | 25 % | Gardner, 60°, Smooth; ASTM D542 | ||
| De |
|||||
| GMCP88 - Light Stipple | 0.065 | ASTM D524 | |||
| Monticello | 0.033 | ASTM D524 | |||