| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 | ||
| Water Absorption | 0.20 % | 0.20 % | 24 hr. Immersion; ASTM D570 | ||
| Linear Mold Shrinkage | 0.0015 - 0.0020 cm/cm | 0.0015 - 0.0020 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 75.8 MPa | 11000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Tensile Modulus | 6.89 GPa | 1000 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 | ||
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.961 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.80 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 232 - 271 °C | 450 - 520 °F | Molding | ||
| Mold Temperature | >= 93.3 °C | >= 200 °F | |||
| Drying Temperature | 93.3 °C | 200 °F | |||
| Dry Time | 2 hour | 2 hour | |||
| De |
|||||
| Product Form | Pellets | ||||