santoprene NOK 8281 - 35med物理性权威测试数据：
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 38 | 38 | 2 mm, 15 sec; ISO 868 | ||
| Tensile Strength at Break | 2.60 MPa | 377 psi | Across Flow; ASTM D412 | ||
| Tensile Stress | 0.903 MPa @Strain 100 % |
131 psi @Strain 100 % |
Across Flow; ASTM D412 | ||
| Elongation at Break | 360 % | 360 % | Across Flow; ASTM D412 | ||
| Tear Strength | 4.00 kN/m | 22.8 pli | 212°F, Die C; ASTM D624 | ||
| 9.01 kN/m | 51.4 pli | 73°C, Die C; ASTM D624 | |||
| Compression Set | 13 % | 13 % | 73°F, 168 hr; ASTM D395 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 175 - 230 °C | 347 - 446 °F | |||
| Rear Barrel Temperature | 177 - 191 °C | 351 - 376 °F | |||
| Middle Barrel Temperature | 179 - 193 °C | 354 - 379 °F | |||
| Front Barrel Temperature | 185 - 199 °C | 365 - 390 °F | |||
| Nozzle Temperature | 185 - 210 °C | 365 - 410 °F | |||
| Melt Temperature | 143 - 216 °C | 289 - 421 °F | Processing | ||
| Mold Temperature | 23.9 - 51.7 °C | 75.0 - 125 °F | |||
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |||
| Clamp Pressure | 41.0 - 69.0 MPa | 5950 - 10000 psi | |||
| Vent Depth | 0.00254 cm | 0.00100 in | |||
| Screw Speed | 100 - 200 rpm | 100 - 200 rpm | |||
| De |
|||||
| Color | Natural Color | ||||
| Form | Pellets | ||||
| Injection Rate | Fast | ||||
| Screw Compression Ratio | 2:1 - 2.5:1 | ||||
| Screw L/D Ratio | 16:1 - 20:1 | ||||
| Suggested Max Regrind | 20% |
||||
产品加工及加工成品优势：
1、 优异的抗老化性能和良好的耐候、耐热性能；
2、 优异的抗永久变形性能；
3、 优异的抗张强度、高韧性和高回弹性；
4、 优异的环保性能和可重复使用；
5、 优异的电绝缘性能；
6、 硬度范围广泛；
7、 使用温度范围广泛；
8、 颜色多样化，有全透明、半透明、浅色系列，着色容易，容易加工成型；
广泛用于运动器材、玩具、医用器材、潜水器材、箱包配件、各种手把、手柄等产品；工程料及工程改性料主要用于机械零件配件、电子组件配件等产品
上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询