LG GN5001SF PC/ABS，无卤阻燃剂_产品资讯

LG GN5001SF PC/ABS，无卤阻燃剂侵蚀而导致制品开裂等缺陷。特别是当PC/ABS 制品喷涂某些车身外饰漆时，由于其溶剂的强腐蚀性，易导致制品出现应力痕，龟裂，甚至开裂。

PC/ABS，聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物，是由聚碳酸酯（Polycarbonate）和聚丙烯腈（ABS）合金而成的热可塑性塑胶，结合了两种材料的优异特性，ABS材料的成型性和PC的机械性、冲击强度和耐温、抗紫外线（UV）等性质，可广泛使用在汽车内部零件、事务机器、通信器材、家电用品及照明设备上。

典型应用范围:
汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件　2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器　3.电信，移动电话外壳，附件以及智能卡（SIM卡）：　4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道　5.家用电器，如洗衣机，吹风机，微波炉内外部件等。

Physical Properties	Metric	English	Comments
物性表：
Specific Gravity	1.18 g/cc	1.18 g/cc	ASTM D792
Maximum Moisture Content	0.020	0.020	Injection Molding
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Thickness 3.20 mm	0.0040 - 0.0060 in/in @Thickness 0.126 in	ASTM D955
Melt Flow	23 g/10 min @Load 2.16 kg, Temperature 250 °C	23 g/10 min @Load 4.76 lb, Temperature 482 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	58.8 MPa @Thickness 3.20 mm	8530 psi @Thickness 0.126 in	50mm/min; ASTM D638
Elongation at Break	>= 50 % @Thickness 3.20 mm	>= 50 % @Thickness 0.126 in	50mm/min; ASTM D638
Flexural Yield Strength	87.3 MPa @Thickness 3.20 mm	12700 psi @Thickness 0.126 in	10mm/min; ASTM D790
Flexural Modulus	2.45 GPa @Thickness 3.20 mm	356 ksi @Thickness 0.126 in	10mm/min; ASTM D790
Izod Impact, Notched	2.94 J/cm @Thickness 3.20 mm, Temperature 23.0 °C	5.51 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	90.0 °C @Thickness 6.40 mm	194 °F @Thickness 0.252 in	Unannealed; ASTM D648
UL RTI, Electrical	60.0 °C @Thickness >=1.50 mm	140 °F @Thickness >=0.0591 in
	60.0 °C @Thickness >=2.10 mm	140 °F @Thickness >=0.0827 in
UL RTI, Mechanical with Impact	60.0 °C @Thickness >=1.50 mm	140 °F @Thickness >=0.0591 in
	60.0 °C @Thickness >=2.10 mm	140 °F @Thickness >=0.0827 in
UL RTI, Mechanical without Impact	60.0 °C @Thickness >=1.50 mm	140 °F @Thickness >=0.0591 in
	60.0 °C @Thickness >=2.10 mm	140 °F @Thickness >=0.0827 in
Flammability, UL94	V-0 @Thickness >=1.50 mm	V-0 @Thickness >=0.0591 in
	V-0 @Thickness >=2.10 mm	V-0 @Thickness >=0.0827 in
	5VA @Thickness >=2.10 mm	5VA @Thickness >=0.0827 in

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	210 - 240 °C	410 - 464 °F	Injection Molding
Middle Barrel Temperature	215 - 250 °C	419 - 482 °F	Injection Molding
Front Barrel Temperature	225 - 260 °C	437 - 500 °F	Injection Molding
Nozzle Temperature	220 - 250 °C	428 - 482 °F	Injection Molding
Melt Temperature	230 - 260 °C	446 - 500 °F	Injection Molding
Mold Temperature	50.0 - 70.0 °C	122 - 158 °F	Injection Molding
Drying Temperature	60.0 - 80.0 °C	140 - 176 °F	Injection Molding
Dry Time	4.00 - 6.00 hour	4.00 - 6.00 hour	Injection Molding
Screw Speed	40 - 70 rpm	40 - 70 rpm	Injection Molding

GN5001SF PC/ABS 物性表