TPU 92 P 4207 物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM D995 |
| Melt Flow | 15 - 30 g/10 min | 15 - 30 g/10 min | Melt Volume Rate (cm³/10 min) |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 92 | 92 | ASTM D2240 |
| Hardness, Shore D | 40 | 40 | ASTM D2240 |
| Tensile Strength at Break | 49.0 MPa | 7110 psi | DIN 53504 |
| Elongation at Break | 640 % | 640 % | ASTM D412 |
| 100% Modulus | 0.00950 GPa | 1.38 ksi | DIN 53504 |
| 300% Modulus | 0.0166 GPa | 2.41 ksi | DIN 53504 |
| Rebound | 34 % | 34 % | Bayshore; ASTM D2632 |
| Tear Strength | 119 kN/m | 680 pli | ASTM D624 |
| Abrasion | 25 | 25 | [mm3]; ISO 4649 |
| Compression Set | 28 % @Temperature 23.0 °C, Time 252000 sec |
28 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 44 % @Temperature 70.0 °C, Time 86400 sec |
44 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 165 - 188 °C | 329 - 370 °F | Huntsman/TMA |
高耐磨性:硬度范围广：通过改变/TPU各反应组分的配比，可以得到不同硬度的产品，而且随着硬度的增加,其产品仍保持良好的弹性/机械强度高：制品的承载能力、抗冲击性及减震性能突出、耐寒性突出：TPU的玻璃态转变温度比较低，在零下35度仍保持良好的弹性、柔顺性和其他物理性能、加工性能好、TPU可采用常见的热塑性材料的加工方法进行加工，
可采用常见的热塑性材料的加工方法进行加工,如注射、挤出、压延等等、同时，TPU与某些高分子材料共同加工能够得到性能互补的聚合物合金、耐油、耐水、耐霉菌、在生利用性好。
优良的抗微生物性，高低温适应性，特别适用于电缆护套及软管类产品。