Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Uses
|
|
|||
|
Forms
|
|
|||
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.57
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage
|
0.30 to 0.50
|
%
|
ISO 294-4 |
|
Water Absorption (Equilibrium, 23°C, 50% RH)
|
1.2
|
%
|
ISO 62 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
19500
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break)
|
260
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break)
|
2.0
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
16100
|
MPa
|
ISO 178 |
|
Flexural Strength
|
415
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (23°C)
|
16
|
kJ/m²
|
ISO 179 |
|
Charpy Unnotched Impact Strength (23°C)
|
59
|
kJ/m²
|
ISO 179 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
258
|
°C
|
ISO 75-2/A |
|
Melting Temperature (DSC)
|
256
|
°C
|
ISO 3146 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+13
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
1.0E+14
|
ohm·cm
|
IEC 60093 |
|
Comparative Tracking Index (Solution A)
|
600
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating (1.60 mm)
|
HB
|
|
UL 94 |
|
Glow Wire Flammability Index (1.60 mm)
|
650
|
°C
|
IEC 60695-2-12 |
|
Oxygen Index
|
23
|
%
|
ISO 4589-2 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
90.0
|
°C
|
|
|
Drying Time
|
4.0
|
hr
|
|
|
Rear Temperature
|
290 to 305
|
°C
|
|
|
Middle Temperature
|
285 to 300
|
°C
|
|
|
Front Temperature
|
280 to 295
|
°C
|
|
|
Processing (Melt) Temp
|
275 to 280
|
°C
|
|
|
Mold Temperature
|
90.0 to 120
|
°C
|
|
|
Injection Pressure
|
95.0 to 120
|
MPa
|
|
|
Injection Rate
|
Fast
|
|
|
|
Holding Pressure
|
60.0 to 80.0
|
MPa
|
|
|
Screw L/D Ratio
|
15.0:1.0 to 20.0:1.0
|
|