Availability
|
|
|
Features
|
|
|
Appearance
|
|
|
Forms
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.39
|
g/cm³
|
ASTM D792 |
|
Molding Shrinkage - Flow
|
0.70 to 1.0
|
%
|
ASTM D955 |
|
Water Absorption (24 hr)
|
1.0
|
%
|
ASTM D570 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength (Yield)
|
65.5
|
MPa
|
ASTM D638 |
|
Tensile Elongation (Break)
|
3.0
|
%
|
ASTM D638 |
|
Flexural Modulus
|
4140
|
MPa
|
ASTM D790 |
|
Flexural Strength (Yield)
|
103
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (23°C, 3.18 mm)
|
27
|
J/m
|
ASTM D256 |
|
Tensile Impact Strength
|
84.1
|
kJ/m²
|
ASTM D1822 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
ASTM D648 | ||
|
0.45 MPa, Unannealed
|
218
|
°C
|
|
|
1.8 MPa, Unannealed
|
127
|
°C
|
|
|
Melting Temperature
|
249 to 260
|
°C
|
|
|
RTI Elec (0.710 mm)
|
130
|
°C
|
UL 746 |
|
RTI Imp
|
UL 746 | ||
|
0.710 mm
|
75.0
|
°C
|
|
|
1.47 mm
|
85.0
|
°C
|
|
|
RTI Str
|
UL 746 | ||
|
0.710 mm
|
120
|
°C
|
|
|
1.47 mm
|
130
|
°C
|
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Arc Resistance (3.05 mm)
|
60.0
|
sec
|
ASTM D495 |
|
Comparative Tracking Index (CTI) (3.05 mm)
|
212
|
V
|
UL 746 |
|
High Amp Arc Ignition (HAI)
|
UL 746 | ||
|
0.710 mm
|
51.0
|
|
|
|
3.05 mm
|
90.0
|
|
|
|
High Voltage Arc Tracking Rate (HVTR)
|
UL 746 | ||
|
0.710 mm
|
115
|
mm/min
|
|
|
1.47 mm
|
52.0
|
mm/min
|
|
|
Hot-wire Ignition (HWI) (0.710 mm)
|
45
|
sec
|
UL 746 |