颗粒： 
物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.296 g/cc | 0.04682 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 125 MPa | 18100 psi | 5mm/min; ISO 527-2/1A | ||
| Tensile Strength | 103 MPa @Temperature 80.0 °C |
14900 psi @Temperature 176 °F |
ISO 527-1, -2 | ||
| Elongation at Break | 1.6 % | 1.6 % | 5mm/min; ISO 527-2/1A | ||
| 2.6 % @Temperature 80.0 °C |
2.6 % @Temperature 176 °F |
ISO 527-1, -2 | |||
| Tensile Modulus | 8.30 GPa | 1200 ksi | 1mm/min; ISO 527-2/1A | ||
| 4.97 GPa @Temperature 80.0 °C |
721 ksi @Temperature 176 °F |
ISO 527-1, -2 | |||
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 | ||
| 175 MPa @Temperature 80.0 °C |
25400 psi @Temperature 176 °F |
ISO 178 | |||
| Flexural Modulus | 7.10 GPa | 1030 ksi | ISO 178 | ||
| 4.40 GPa @Temperature 80.0 °C |
638 ksi @Temperature 176 °F |
ISO 178 | |||
| Izod Impact, Notched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | ISO 180/1A | ||
| 21.0 kJ/m² @Temperature -30.0 °C |
9.99 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A | |||
| Charpy Impact Unnotched | 4.10 J/cm² | 19.5 ft-lb/in² | ISO 179/1eU | ||
| 5.20 J/cm² @Temperature -30.0 °C |
24.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 2.40 J/cm² | 11.4 ft-lb/in² | ISO 179/1eA | ||
| 2.70 J/cm² @Temperature -30.0 °C |
12.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 238 °C | 460 °F | ISO 75-1, -2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| 80.0 - 100 °C | 176 - 212 °F | Cavity temperature | |||
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 285 - 295 °C | 545 - 563 °F | |||
| Zone 2 | 290 - 300 °C | 554 - 572 °F | |||
| Zone 3 | 300 - 310 °C | 572 - 590 °F | |||
| Zone 4 | 300 - 315 °C | 572 - 599 °F | |||
| Die Temperature | 300 - 315 °C | 572 - 599 °F | |||
| Melt Temperature | 300 - 315 °C | 572 - 599 °F | |||
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | 0.15 % | 0.15 % | Necessary low maximum residual | ||
| Injection Pressure | 120 - 150 MPa | 17400 - 21800 psi | |||
| Hold Pressure | 50.0 - 80.0 MPa | 7250 - 11600 psi | |||
| Back Pressure | 3.00 MPa | 435 psi | |||
| Screw Speed | 25 rpm @Diameter 75.0 mm |
25 rpm @Diameter 2.95 in |
|||
| 35 rpm @Diameter 55.0 mm |
35 rpm @Diameter 2.17 in |
||||
| 50 rpm @Diameter 40.0 mm |
50 rpm @Diameter 1.57 in |
||||
| De |
|||||
| Heat stabilized/stable to heat | Yes | ||||
| Injection speed | medium | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。