物性表:
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.136 g/cc | 0.04104 lb/in³ | Melt; ISO 1183 | ||
1.39 g/cc | 0.0502 lb/in³ | ISO 1183 | |||
Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test | ||
6.4 % | 6.4 % | ISO 62 | |||
Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 23°C/50% R.H.; ISO 62 | ||
Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
Viscosity Measurement | 50 | 50 | Formic Acid | ||
Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
Tensile Strength at Break | 195 MPa | 28300 psi | 0.2 in/min; ASTM Test | ||
83.0 MPa @Temperature 120 °C |
12000 psi @Temperature 248 °F |
ASTM Test | |||
83.0 MPa @Temperature 120 °C |
12000 psi @Temperature 248 °F |
ISO Data | |||
110 MPa @Temperature 80.0 °C |
16000 psi @Temperature 176 °F |
ISO Data | |||
110 MPa @Temperature 80.0 °C |
16000 psi @Temperature 176 °F |
ASTM Test | |||
283 MPa @Temperature -40.0 °C |
41000 psi @Temperature -40.0 °F |
ASTM Test | |||
283 MPa @Temperature -40.0 °C |
41000 psi @Temperature -40.0 °F |
ISO Data | |||
Tensile Strength, Ultimate | 185 MPa | 26800 psi | 5mm/min; ISO 527 | ||
Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527 | ||
3.5 % | 3.5 % | 0.2 in/min; ASTM Test | |||
3.6 % @Temperature -40.0 °C |
3.6 % @Temperature -40.0 °F |
ASTM Test | |||
3.6 % @Temperature -40.0 °C |
3.6 % @Temperature -40.0 °F |
ISO Data | |||
7.0 % @Temperature 120 °C |
7.0 % @Temperature 248 °F |
ISO Data | |||
7.0 % @Temperature 80.0 °C |
7.0 % @Temperature 176 °F |
ISO Data | |||
7.0 % @Temperature 120 °C |
7.0 % @Temperature 248 °F |
ASTM Test | |||
7.0 % @Temperature 80.0 °C |
7.0 % @Temperature 176 °F |
ASTM Test | |||
Tensile Modulus | 10.1 GPa | 1460 ksi | 1mm/min; ISO 527 | ||
3.55 GPa @Temperature 120 °C |
515 ksi @Temperature 248 °F |
ISO Data | |||
4.43 GPa @Temperature 80.0 °C |
643 ksi @Temperature 176 °F |
ISO Data | |||
10.5 GPa @Temperature -40.0 °C |
1520 ksi @Temperature -40.0 °F |
ISO Data | |||
Flexural Strength | 260 MPa | 37700 psi | ISO Data | ||
297 MPa | 43100 psi | ASTM Test | |||
112 MPa @Temperature 120 °C |
16200 psi @Temperature 248 °F |
ASTM Test | |||
140 MPa @Temperature 93.0 °C |
20300 psi @Temperature 199 °F |
ASTM Test | |||
160 MPa @Temperature 65.0 °C |
23200 psi @Temperature 149 °F |
ASTM Test | |||
380 MPa @Temperature -40.0 °C |
55100 psi @Temperature -40.0 °F |
ASTM Test | |||
Flexural Modulus | 8.20 GPa | 1190 ksi | ISO Data | ||
9.04 GPa | 1310 ksi | ASTM Test | |||
3.32 GPa @Temperature 120 °C |
482 ksi @Temperature 248 °F |
ASTM Test | |||
3.75 GPa @Temperature 93.0 °C |
544 ksi @Temperature 199 °F |
ASTM Test | |||
4.02 GPa @Temperature 65.0 °C |
583 ksi @Temperature 149 °F |
ASTM Test | |||
Izod Impact, Notched | 1.07 J/cm @Temperature -40.0 °C |
2.00 ft-lb/in @Temperature -40.0 °F |
ASTM Test | ||
1.48 J/cm @Thickness 3.17 mm |
2.77 ft-lb/in @Thickness 0.125 in |
ASTM Test | |||
Izod Impact, Unnotched | 13.7 J/cm | 25.7 ft-lb/in | ASTM Test | ||
Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO Test | ||
8.50 kJ/m² @Temperature -40.0 °C |
4.04 ft-lb/in² @Temperature -40.0 °F |
ISO Test | |||
Charpy Impact Unnotched | 8.80 J/cm² | 41.9 ft-lb/in² | ISO 179 | ||
Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179 | ||
1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
ASTM Data | |||
3.8 @Frequency 1e+9 Hz |
3.8 @Frequency 1e+9 Hz |
ASTM Data | |||
4.2 @Frequency 100 Hz |
4.2 @Frequency 100 Hz |
IEC 60250 | |||
Dielectric Strength | 44.0 kV/mm | 1120 kV/in | IEC 60243-1 | ||
Dissipation Factor | 0.010 @Frequency 1e+9 Hz |
0.010 @Frequency 1e+9 Hz |
ASTM Data | ||
0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
ASTM Data | |||
0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
0.020 @Frequency 100 Hz |
0.020 @Frequency 100 Hz |
IEC 60250 | |||
Thermal Properties | Metric | English | Comments | ||
CTE, linear | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM Test | ||
CTE, linear, Parallel to Flow | 21.0 µm/m-°C | 11.7 µin/in-°F | ISO 11359 | ||
CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359 | ||
Specific Heat Capacity | 2.434 J/g-°C | 0.5817 BTU/lb-°F | Melt | ||
Thermal Conductivity | 0.275 W/m-K | 1.91 BTU-in/hr-ft²-°F | Melt | ||
Melting Point | 220 °C | 428 °F | 10 K/min | ||
220 °C | 428 °F | ASTM Test | |||
Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 | ||
218 °C | 424 °F | ASTM Test | |||
Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75 | ||
210 °C | 410 °F | ASTM Test | |||
Flammability, UL94 | HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
|||
HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||||
De |
|||||
Color | Natural | ||||
Commercial Status | Active America | ||||
Form | Pellets | ||||
Impact Modified | No | ||||
Primary Processing Technique | Injection Molding | ||||
Processing | Injection Molding | ||||
Special characteristic | Heat stabilized or stable to heat | ||||
UL.UL-C | Yes |